Plastic laminated film
A plastic laminated film comprising a first layer comprising a polyamideimide copolymer and a second layer provided on at least one surface of the first layer and comprising a polyimide copolymer. The plastic laminated film has both excellent mechanical properties and UV weathering resistance while being colorless and transparent, and can be suitably used as cover films for various flexible or foldable devices.
1. A plastic laminated film comprising:
a first layer comprising a polyamideimide copolymer,
wherein the polyamideimide copolymer is an imide of a polyamic acid resulting from copolymerizing an aromatic diamine monomer, a dianhydride monomer, and an aromatic dicarbonyl monomer, and
a second layer provided on at least one surface of the first layer and comprising a polyimide copolymer,
wherein the polyimide copolymer is an imide of a polyamic acid resulting from copolymerizing an aromatic diamine monomer and a dianhydride monomer,
wherein each dianhydride monomer is an aromatic dianhydride monomer, cyclobutane tetracarboxylic dianhydride, or cyclopentane tetracarboxylic dianhydride, and
wherein the plastic laminate film has ΔYI represented by the following Mathematical Formula 1 of 2.0 or less:
[Mathematical Formula 1]
Δ YI=YI 1 −YI 0
wherein, in Mathematical Formula 1, YI 0 and YI 1 are yellowness indexes of the film measured according to ASTM D1925,
where YI 0 is an initial yellowness index of the film, and
YI 1 is a yellowness index of the film exposed to ultraviolet light and moisture for 96 hours according to ASTM G53, and
wherein the plastic laminated film has a transmittance of 88% or more with respect to visible light having a wavelength of 550 nm at a thickness of 50±5 μm, and a transmittance of 13% or less with respect to ultraviolet light having a wavelength of 388 nm at a thickness of 50±5 μm.
2. The plastic laminated film of claim 1 ,
wherein the second layer further comprises a silane-based compound in the polyimide copolymer.
3. The plastic laminated film of claim 2 ,
wherein the silane-based compound comprises tetraethoxysilane.
4. The plastic laminated film of claim 1 ,
wherein YI 0 is 4.5 or less and YI 1 is 6.0 or less.
5. The plastic laminated film of claim 1 ,
wherein each aromatic diamine monomer is independently at least one compound selected from the group of 2,2′-bis(trifluoromethyl)-4,4′-biphenyldiamine, 4,4′-diaminodiphenyl sulfone, 4,4′-(9-fluorenylidene)dianiline, bis(4-(4-aminophenoxy)phenyl)sulfone, 2,2′,5,5′-tetrachlorobenzidine, 2,7-diaminofluorene, 4,4-diaminooctafluorobiphenyl, m-phenylenediamine, p-phenylenediamine, 4,4′-oxydianiline, 2,2′-dimethyl-4,4′-diaminobiphenyl, 2,2-bis(4-(4-aminophenoxy)phenyl)propane, 1,3-bis(4-aminophenoxy)benzene, and 4,4′-diaminobenzanilide;
each aromatic dianhydride monomer is independently at least one compound selected from the group of 3,3′,4,4′-biphenyltetracarboxylic acid dianhydride, 2,2-bis-(3,4-dicarboxyphenyl)hexafluoropropane dianhydride, benzophenone tetracarboxylic dianhydride, pyromellitic dianhydride, benzophenone tetracarboxylic dianhydride, oxydiphthalic anhydride, and bis(3,4-dicarboxyphenyl)sulfone dianhydride; and
the aromatic dicarbonyl monomer is at least one compound selected from the group of terephthaloyl chloride, isophthaloyl chloride, biphenyldicarbonyl chloride, terephthalic acid, pyridine-2,5-dicarbonyl chloride, pyridine-2,5-dicarboxylic acid, pyrimidine-2,5-dicarbonyl chloride, pyrimidine-2,5-dicarboxylic acid, 4,4′-biphenyldicarbonyl chloride, and 4,4′-biphenyldicarboxylic acid.
6. The plastic laminated film of claim 1 ,
wherein a thickness ratio of the first layer and the second layer is 1:0.01 to 1:0.2.
7. The plastic laminated film of claim 1 ,
wherein the film has a thickness of 10 to 100 μm.
8. A device comprising the plastic laminated film of claim 1 as a cover film,
wherein the device is a flexible or foldable device.
9. The plastic laminated film of claim 1 ,
wherein each aromatic diamine monomer is independently at least one compound selected from the group of 2,2′-bis(trifluoromethyl)-4,4′-biphenyldiamine, 4,4′-diaminodiphenyl sulfone, 4,4′-(9-fluorenylidene)dianiline, bis(4-(4-aminophenoxy)phenyl)sulfone, 2,2′,5,5′-tetrachlorobenzidine, 2,7-diaminofluorene, 4,4-diaminooctafluorobiphenyl, m-phenylenediamine, p-phenylenediamine, 4,4′-oxydianiline, 2,2′-dimethyl-4,4′-diaminobiphenyl, 2,2-bis(4-(4-aminophenoxy)phenyl)propane, 1,3-bis(4-aminophenoxy)benzene, and 4,4′-diaminobenzanilide.
10. The plastic laminated film of claim 1 ,
wherein each aromatic dianhydride monomer is independently at least one compound selected from the group of 3,3′,4,4′-biphenyltetracarboxylic acid dianhydride, 2,2-bis-(3,4-dicarboxyphenyl)hexafluoropropane dianhydride, benzophenone tetracarboxylic dianhydride, pyromellitic dianhydride, benzophenone tetracarboxylic dianhydride, oxydiphthalic anhydride, and bis(3,4-dicarboxyphenyl)sulfone dianhydride.
11. The plastic laminated film of claim 1 ,
wherein the aromatic dicarbonyl monomer is at least one compound selected from the group of terephthaloyl chloride, isophthaloyl chloride, biphenyldicarbonyl chloride, terephthalic acid, pyridine-2,5-dicarbonyl chloride, pyridine-2,5-dicarboxylic acid, pyrimidine-2,5-dicarbonyl chloride, pyrimidine-2,5-dicarboxylic acid, 4,4′-biphenyldicarbonyl chloride, and 4,4′-biphenyldicarboxylic acid.