Aqueous gelcasting formulation for ceramic products
The present disclosure relates to the manufacture of ceramic products by aqueous gelcasting. Exemplary ceramic products include sanitary ware, such as toilets and sinks. The process includes a slurrying step, a mixing step, a molding step involving aqueous gelcasting, a drying step, a glazing step, and a firing step.
1. A formulation comprising:
at least one mineral oxide constituting about 10 wt. % to about 88 wt. % of the formulation;
at least one alkali aluminosilicate mineral separate from the at least one mineral oxide and configured to serve as a fluxing agent to reduce the melting point of the formulation;
colloidal silica; and
water, wherein the formulation is a slurry capable of flowing into a mold.
2. The formulation of claim 1 , wherein the at least one mineral oxide includes silica and alumina.
3. The formulation of claim 1 , wherein the at least one alkali aluminosilicate mineral includes Feldspar or Nepheline Syenite.
4. The formulation of claim 1 , wherein the at least one mineral oxide constitutes about 25 wt. % to about 45 wt. % of the slurry.
5. The formulation of claim 1 , wherein the at least one alkali aluminosilicate mineral constitutes about 10 wt. % to about 85 wt. % of the slurry.
6. The formulation of claim 5 , wherein the at least one alkali aluminosilicate mineral constitutes about 50 wt. % to about 70 wt. % of the slurry.
7. The formulation of claim 1 , wherein the at least one alkali aluminosilicate mineral constitutes a majority of the slurry.
8. The formulation of claim 1 , wherein the colloidal silica has a solid content of about 10 wt. % to about 50 wt. %.
9. The formulation of claim 1 , wherein the colloidal silica constitutes about 2 wt. % to about 40 wt. % of the slurry.
10. The formulation of claim 1 , further comprising at least one additive comprising clay or clay minerals constituting about 10 wt. % or less of the slurry.
11. The formulation of claim 1 , further comprising at least one additive comprising an organic gum constituting about 2 wt. % or less of the slurry.
12. The formulation of claim 1 , wherein a solid content of the slurry is from about 70 wt. % to about 90 wt. %.
13. The formulation of claim 1 , less water, comprising:
17.8 wt. % silica;
17.4 wt. % alumina;
56.0 wt. % of the at least one alkali aluminosilicate mineral; and
8.8 wt. % of the colloidal silica.
14. The formulation of claim 1 , wherein the colloidal silica comprises 30 wt. % silica and 70 wt. % water.
15. The formulation of claim 1 , less water, comprising:
10.9 wt. % silica;
15.4 wt. % alumina;
56.0 wt. % of the at least one alkali aluminosilicate mineral; and
13.7 wt. % of the colloidal silica.
16. The formulation of claim 1 , wherein the colloidal silica comprises 40 wt. % silica and 60 wt. % water.
17. A formulation comprising:
at least one mineral oxide constituting at least about 10 wt. % of the formulation;
at least one alkali aluminosilicate mineral, separate from the at least one mineral oxide and configured to serve as a fluxing agent to reduce the melting point of the formulation;
colloidal silica; and
water, wherein the formulation is a slurry and the at least one alkali aluminosilicate mineral constitutes a majority of the slurry.
18. A formulation comprising:
17.8 wt. % silica;
17.4 wt. % alumina;
56.0 wt % of at least one alkali aluminosilicate mineral, separate from silica and alumina; and
8.8 wt. % colloidal silica, wherein the formulation is a slurry.
19. A formulation comprising:
12.9 wt. % silica;
17.4 wt. % alumina;
56.0 wt % of at least one alkali aluminosilicate mineral separate from silica and alumina; and
13.7 wt. % colloidal silica, wherein the formulation is a slurry.