Ceramic material and method for preparing the same
A ceramic material including Co 0.5 Ti 0.5 TaO 4 . The ceramic material is prepared as follows: 1) weighting and mixing raw powders of Co 2 O 3 , TiO 2 and Ta 2 O 5 proportioned according to the chemical formula of Co 0.5 Ti 0.5 TaO 4 , to yield a mixture; 2) mixing the mixture obtained in 1), zirconia balls, and deionized water according to a mass ratio of 1:4-6:3-6, ball-milling for 6-8 h, drying at 80-120° C., sieving with a 60-200 mesh sieve, calcining in air atmosphere at 800-1100° C. for 3-5 h, to yield powders comprising a main crystalline phase of Co 0.5 Ti 0.5 TaO 4 ; and 3) mixing the powders obtained in 2), zirconia balls, and deionized water according to a mass ratio of 1:3-5:2-4, ball-milling for 4-6 h, and drying at 80-100° C.; adding a 2-5 wt. % of polyvinyl alcohol solution to a resulting product, granulating, sintering resulting granules at 1000-1100° C. in air atmosphere for 4-6 h.
1. A ceramic material, comprising Co 0.5 Ti 0.5 TaO 4 having a trirutile structure.
2. The ceramic material of claim 1 , wherein the ceramic material is prepared through a method comprising:
1) weighting and mixing raw powders of Co 2 O 3 , TiO 2 and Ta 2 O 5 proportioned according to the chemical formula of CO 0.5 Ti 0.5 TaO 4 , to yield a mixture;
2) mixing the mixture obtained in 1), zirconia balls, and deionized water according to a mass ratio of 1: 4-6: 3-6, ball-milling for 6-8 h, drying at 80-120° C., sieving with a 60-200 mesh sieve, calcining in air atmosphere at 800-1100° C. for 3-5 h, to yield powders comprising a main crystalline phase of Co 0.5 Ti 0.5 TaO 4 ; and
3) mixing the powders obtained in 2), zirconia balls, and deionized water according to a mass ratio of 1: 3-5: 2-4, ball-milling for 4-6 h, and drying at 80-100° C., adding a 2-5 wt. % of polyvinyl alcohol solution to a resulting product, granulating, sintering resulting granules at 1000-1100° C. in air atmosphere for 4-6 h, to yield the ceramic material.
3. The ceramic material of claim 2 , wherein a dielectric constant of the ceramic material is between 36 and 41.
4. The ceramic material of claim 2 , wherein a quality factor (Q×f) of the ceramic material is between 13135 and 17291 GHz.
5. The ceramic material of claim 2 , wherein a temperature coefficient of resonant frequency of the ceramic material is between 113 and 116 ppm/° C.