Large-format battery anodes comprising silicon particles
Large-scale anodes containing high weight percentages of silicon suitable for use in lithium-ion energy storage devices and batteries, and methods of manufacturing the same, are described. The anode material described herein can include a film cast on a current collector substrate, with the film including a plurality of active material particles and a conductive polymer membrane coated over the active material particles. In some embodiments, the conductive polymer membrane comprises polyacrylonitrile (PAN). The method of manufacturing the anode material can include preparation of a slurry including the active material particles and the conductive polymer material, casting the slurry on a current collector substrate, and subjecting the composite material to drying and heat treatments.
1. An energy storage device comprising:
a cathode;
an electrolyte; and
an anode comprising a film disposed over a current collector substrate, wherein the film has a thickness of 10 to 80 micrometers, wherein the current collector substrate has a surface roughness R z of greater than 1.5 micrometers, and wherein a magnitude of the arithmetical mean height Sa of the current collector substrate is less than three times a developed interfacial ratio Sdr of the current collector substrate, the film comprising:
A) a plurality of active material particles, wherein the active material particles include at least one of silicon, hard-carbon, graphite, graphene, germanium, titanium oxide, tin, magnesium, antimony, and lead; and
B) a conductive polymer membrane coating over the active material particles, the conductive polymer membrane coating comprising a thermoplastic polymer treated to become a cyclized, non-plastic ladder compound.
2. The energy storage device of claim 1 , wherein the anode comprises 30-60 wt. % silicon particles and an areal gravimetric capacity of the anode is 1.3 to 1.6 times that of an areal gravimetric capacity of the cathode.
3. The energy storage device of claim 1 , wherein the anode comprises greater than or equal to 60 wt. % silicon particles and an areal gravimetric capacity of the anode is 1.6 to 2.0 times that of an areal gravimetric capacity of the cathode.
4. The energy storage device of claim 1 , wherein the thermoplastic polymer treated to become a cyclized, non-plastic ladder compound comprises polyacrylonitrile.
5. The energy storage device of claim 1 , wherein the electrolyte comprises an imide-based room temperature ionic liquid.
6. The energy storage device of claim 1 , wherein a porosity of the anode film is between 50-70%.
7. The energy storage device of claim 1 , wherein the surface roughness R z is defined as the average of the peak-to-valley numbers in a given scan area of the anode film.
8. The energy storage device of claim 1 , wherein the surface roughness Lis greater than 6 micrometers.
9. The energy storage device of claim 1 , wherein the cathode is a nickel manganese cobalt oxide cathode.
10. A method of making the energy storage device of claim 1 , comprising:
preparing an anode having a film with a thickness of 10 to 80 micrometers cast over a current collector substrate, the film comprising a plurality of active material particles and a thermoplastic polymer treated to become a cyclized, non-plastic ladder compound, the method of preparing the anode comprising:
A) preparing a slurry having a Brookfield viscosity of 2000-6000 cP at 20 to 100 RPM using a #64 spindle, at room temperature, by placing a mixture of active material, additive powder and polymer powder in a solvent capable of dissolving the polymer powder;
B) mixing the slurry for a time of 1 to 4 hours;
C) casting the slurry over a current collector substrate;
D) drying the casted film; and
E) applying heat to the casted film at temperatures of 200 to 400° C. for a time of 1 to 12 hours; and
combining the anode with a cathode and electrolyte to form the energy storage device.
11. The method of claim 10 , wherein the active material includes at least one of silicon, hard-carbon, graphite, germanium, titanium oxide, tin, magnesium, antimony, and lead.
12. The method of claim 10 , wherein the thermoplastic polymer treated to become a cyclized, non-plastic ladder compound comprises polyacrylonitrile.
13. The method of claim 10 , wherein the additive powder comprises lithium metal powder.
14. The method of claim 10 , wherein the additive powder comprises lithium nitride.
15. The method of claim 10 , wherein the additive powder comprises oxalic acid.
16. The method of claim 10 , wherein the application of 200 to 400° C. heat is completed under vacuum or inert gas flow.
17. The method of claim 10 , wherein an areal gravimetric capacity of the anode is 1.3 to 2.0 times that of an areal gravimetric capacity of the cathode.
18. An energy storage device comprising:
a cathode;
an electrolyte;
a current collector substrate having a surface roughness R, of greater than 1.5 micrometers, wherein a magnitude of the arithmetical mean height Sa of the current collector substrate is less than three times a developed interfacial ratio Sdr of the current collector substrate; and
an anode film disposed over the current collector substrate, wherein the anode film has a thickness of 10 to 80 micrometers, and wherein a porosity of the anode film is between 50-70%, the anode film comprising:
A) a plurality of silicon active material particles; and
B) a polyacrylonitrile membrane disposed over the active material particles.
19. The energy storage device of claim 18 , wherein the cathode comprises a nickel manganese cobalt oxide cathode.