Biaxially oriented microporous membrane
A microporous membrane is made by a dry-stretch process and has substantially round shaped pores and a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 5.0. The method of making the foregoing microporous membrane includes the steps of: extruding a polymer into a nonporous precursor, and biaxially stretching the nonporous precursor, the biaxial stretching including a machine direction stretching and a transverse direction stretching, the transverse direction stretching including a simultaneous controlled machine direction relax.
1. A membrane comprising:
a microporous multi-layer polymer film having outer layers made of a semi-crystalline polymer and at least one inner layer made of a polyethylene, wherein the layers are formed by co-extrusion followed by a dry-stretch process, the film having substantially round shaped pores and a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 5.0; wherein said dry-stretched process excludes the use of oils for subsequent removal to form pores or pore-forming materials to facilitate pore formation and pore formation results from stretching, and wherein said semi-crystalline polymer is polypropylene polymer, a polypropylene polymer or polypropylene co-polymer blend, or a co-polymer of polypropylene, wherein the polymer film has a thickness of from about 7.5 to about 20 microns and an TD tensile strength of at least 500 kg/cm 2 .
2. The membrane according to claim 1 wherein said semi-crystalline polymer having a crystallinity in the range of 20-80%.
3. The membrane according to claim 1 wherein an average pore size of said microporous polymer film being in the range of 0.03 to 0.30 microns.
4. The membrane according to claim 1 wherein said microporous polymer film having a porosity in the range of 20-80%.
5. The membrane according to claim 1 wherein said substantially round shaped pores having an aspect ratio in the range of 0.75 to 1.25.
6. The membrane according to claim 1 further including a filler.
7. The membrane according to claim 1 further including an elastomer.
8. The membrane according to claim 1 further including an anti-static agent, an anti-blocking agent, an anti-oxidant, or a lubricant.
9. The membrane according to claim 1 wherein the dry stretch process includes the steps of extruding a nonporous precursor and then biaxially stretching the nonporous precursor, the biaxial stretching including a machine direction stretch and transverse direction stretch with a simultaneous controlled machine direction relax.
10. A battery separator comprising the membrane of claim 1 .
11. A device having a membrane, the membrane being the membrane according to claim 1 , wherein the device being: a mass transfer device, a pressure regulator, a filter, a medical device, or a fuel cell.