Sputtering target, oxide semiconductor thin film, and method for producing these
A sputtering target including an oxide that includes an indium (In) element, a tin (Sn) element, a zinc (Zn) element and an aluminum (Al) element, wherein the oxide includes a homologous structure compound represented by InAlO 3 (ZnO) m (m is 0.1 to 10) and a bixbyite structure compound represented by In 2 O 3 .
1. An oxide semiconductor thin film formed by a sputtering method with the use of a sputtering target comprising an oxide that comprises an indium (In) element, a tin (Sn) element, a zinc (Zn) element and an aluminum (Al) element
wherein the atomic ratio of In, Sn, Zn and Al satisfies the following formulas (1) to (4):
0.50≤In/(In+Sn+Zn+Al)≤0.75 (1)
0.01≤Sn/(In+Sn+Zn+Al)≤0.30 (2)
0.10≤Zn/(In+Sn+Zn+Al)≤0.70 (3)
0.01≤Al/(In+Sn+Zn+Al)≤0.40 (4)
and wherein in the formulas, In, Sn, Zn and Al independently indicate an atomic ratio of each element in the sputtering target.
2. A method for producing an oxide semiconductor thin film, wherein the film is formed by a sputtering method with the use of sputtering target in an atmosphere of a mixed gas that comprises: one or more selected from water vapor, an oxygen gas and a nitrous oxide gas and further comprises a rare gas;
wherein the sputtering target comprises an oxide that comprises an indium (In) element, a tin (Sn) element, a zinc (Zn) element and an aluminum (Al) element
wherein the atomic ratio of In, Sn, Zn and Al satisfies the following formulas (1) to (4):
0.50≤In/(In+Sn+Zn+Al)≤0.75 (1)
0.01≤Sn/(In+Sn+Zn+Al)≤0.30 (2)
0.10≤Zn/(In+Sn+Zn+Al)≤0.70 (3)
0.01≤Al/(In+Sn+Zn+Al)≤0.40 (4)
and wherein in the formulas, In, Sn, Zn and Al independently indicate an atomic ratio of each element in the sputtering target.
3. The method for producing an oxide semiconductor thin film according to claim 2 , wherein the formation of the oxide semiconductor thin film is conducted in an atmosphere of a mixed gas that comprises a rare gas and at least water vapor.
4. The method for producing an oxide semiconductor thin film according to claim 3 , wherein the ratio of the water vapor contained in the mixed gas is 0.1% to 25% in terms of a partial pressure ratio.
5. The method for producing the oxide semiconductor thin film according to claim 2 comprising:
transporting substrates in sequence to positions opposing to 3 or more of the sputtering targets of claim 2 arranged in parallel with a prescribed interval in a vacuum chamber;
applying a negative potential and a positive potential alternately from an AC power source to each of the targets; and
causing plasma to be generated on the target by applying at least one output from the AC power source while switching the target to which a potential is applied among two or more of the sputtering targets that are divergently connected to this AC power source, thereby forming a film on a substrate surface.
6. The method for producing an oxide semiconductor thin film according to claim 5 , wherein the AC power density of the AC power source is 3 W/cm 2 or more and 20 W/cm 2 or less.
7. The method for producing an oxide semiconductor thin film according to claim 5 , wherein the frequency of the AC power source is 10 kHz to 1 MHz.
8. A thin film transistor comprising, as a channel layer, the oxide semiconductor thin film formed by the method for producing an oxide semiconductor thin film according to claim 2 .
9. The thin film transistor according to claim 8 that has a field effect mobility of 10 cm 2 /Vs or more.