Heat-sealable packaging material
The present invention is directed to a packaging material free from aluminium in the form of a continuous foil or film, comprising a layer of microfibrillated cellulose (MFC), wherein the layer comprising MFC has been laminated or coated on at least one side with a heat-sealable material. The MFC layer contains at least 60% by weight of microfibrillated cellulose. The present invention is also directed to a method for induction sealing, wherein a packaging material to be heat-sealed by induction is placed against an induction heating surface.
1. A heat-sealable packaging material, free from aluminum in the form of a continuous foil or film, the heat-sealable packaging material comprising:
a layer that comprises at least 60% by weight of microfibrillated cellulose,
wherein the layer comprising at least 60% by weight of microfibrillated cellulose is laminated or coated with a heat-sealable material,
wherein a thickness of the heat-sealable packaging material is less than 70 μm, and
wherein at least one side of the heat-sealable packaging material is provided with a coating that prevents the at least one side form adhering to a heated metal surface selected from a group consisting of starch, a wax, a mineral coating, or pigment coating.
2. The heat-sealable packaging material according to claim 1 , wherein the heat-sealable material is selected from the group consisting of: polyethylene, polypropylene, polylactic acid, styrene acrylic latex, styrene butadiene latex, and mixtures thereof.
3. The heat-sealable packaging material according to claim 1 , wherein said heat-sealable material comprises a thermoplastic polymer.
4. The heat-sealable packaging material according to claim 3 , wherein said thermoplastic polymer is polyethylene.
5. The heat-sealable packaging material according to claim 1 , wherein the microfibrillated cellulose is native microfibrillated cellulose, modified microfibrillated cellulose, or a mixture thereof, and wherein the modified microfibrillated cellulose is phosphorylated microfibrillated cellulose or PCC coated microfibrillated cellulose.
6. A method of manufacturing the heat-sealable packaging material according to claim 1 , the method comprising the steps of
a) preparing the layer of at least 60% by weight of microfibrillated cellulose;
b) laminating or coating the layer of step a) with the heat-sealable material on at least one side of the microfibrillated cellulose layer.
7. A method for induction sealing, wherein the material to be sealed by induction is free from aluminum in the form of a continuous foil or film, the method comprising:
bringing the heat-sealable packaging material according to claim 1 into close proximity or contact with a surface;
heating the surface by induction, thereby heating and sealing, under applied pressure, the heat-sealable packaging material to provide a heat-sealed package.
8. The method according to claim 7 , wherein the sealing is achieved by softening or melting of the heat-sealable material and by applying a pressure to the softened or melted heat-sealable material.
9. The heat-sealable packaging material according to claim 3 , wherein said thermoplastic polymer has been extrusion coated or dispersion coated on the layer comprising at least 60% by weight of microfibrillated cellulose.