Methods of producing cobalt nanoparticles and hollow gold nanospheres and kits for practicing same
Provided are methods of producing cobalt nanoparticles (Co NPs). The methods include combining a cobalt salt, a capping agent, and a reducing agent, under Co NP synthesis conditions including a temperature selected to produce cobalt nanoparticles of a pre-selected diameter, where the temperature and pre-selected diameter are inversely related. In certain aspects, the methods further include producing hollow gold nano spheres (HGNs) using the cobalt nanoparticles as scaffolds. Also provided are cobalt nanoparticles and hollow gold nano spheres (HGNs) produced according to the present methods. Kits that find use in practicing the methods of the present disclosure are also provided.
1. A method of producing cobalt nanoparticles (Co NPs) of a pre-selected diameter, comprising:
(a) pre-selecting a desired diameter of Co NPs prior to production of the Co NPs;
(b) selecting a temperature of from 10° C. to 80° C. for Co NP synthesis for achieving the pre-selected desired diameter of the Co NPs;
(c) selecting:
a cobalt salt;
a capping agent; and
a reducing agent,
capable of forming Co NPs under Co NP synthesis conditions, wherein said Co NP synthesis conditions include an inverse relationship between a temperature of synthesis and a resulting diameter of Co NPs produced over the entire range of from 10° C. to 80° C., and
d) combining the cobalt salt, capping agent and reducing agent at the selected temperature to produce Co NPs of the desired diameter.
2. The method according to claim 1 , wherein the Co NP synthesis conditions comprise a constant temperature.
3. The method according to claim 1 , wherein the pre-selected diameter is from about 150 nm to about 30 nm.
4. The method according to claim 1 , wherein the cobalt salt is CoCl 2 .
5. The method according to claim 1 , wherein the capping agent is trisodium citrate.
6. The method according to claim 1 , wherein the reducing agent is NaBH 4 .
7. The method according to claim 1 , further comprising producing cobalt nanoparticles of a different pre-selected diameter by:
(d) pre-selecting a different desired diameter of Co NPs prior to production of the Co NPs;
(e) selecting a different temperature of from 10° C. to 80° C. for the Co NP synthesis for achieving the different pre-selected desired diameter of the Co NPs; and
(f) combining the
cobalt salt
capping agent and
reducing agent
under Co NP synthesis conditions comprising the different temperature to produce Co NPs of the different pre-selected diameter.
8. The method according to claim 1 , further comprising, subsequent to producing the cobalt nanoparticles, producing hollow gold nanospheres (HGNs) using the cobalt nanoparticles as scaffolds.
9. The method according to claim 8 , wherein the HGNs are produced via a galvanic exchange reaction.
10. The method according to claim 8 , wherein the HGNs have a diameter of from about 10 to about 200 nm.
11. The method according to claim 8 , wherein the HGNs exhibit a surface plasmon resonance (SPR) absorption with a maximum peak position of from about 565 to about 850 nm.
12. The method according to claim 8 , further comprising, subsequent to producing the HGNs, attaching a targeting moiety to the surface thereof.