4-methyl-1-pentene polymer particle and method for producing 4-methyl-1-pentene resin
A 4-methyl-1-pentene polymer particle (X) which satisfies the following requirements (X-a), (X-b) and (X-c): (X-a) being composed of a 4-methyl-1-pentene polymer which has a content of a constitutional unit derived from 4-methyl-1-pentene being 30.0 to 99.7% by mol, and a content of a constitutional unit derived from at least one olefin selected from ethylene and an α-olefin having 3 to 20 carbon atoms (except for 4-methyl-1-pentene) being 0.3 to 70.0% by mol; (X-b) having, when measured in a cross fractionation chromatograph apparatus (CFC) using an infrared spectrophotometer as a detector part, at least one peak A of an amount of a component eluted present in the range of 100 to 140° C., and at least one peak B of an amount of a component eluted present at lower than 100° C.; and (X-c) having a meso diad fraction (m) measured by 13 C-NMR falling within the range of 95.0 to 100%.
1. A 4-methyl-1-pentene polymer particle (X) which satisfies the following requirements (X-a), (X-b) and (X-c):
(X-a) being composed of a 4-methyl-1-pentene polymer which has a content of a constitutional unit derived from 4-methyl-1-pentene being 30.0 to 99.7% by mol and which has a content of a constitutional unit derived from at least one olefin selected from ethylene and an α-olefin having 3 to 20 carbon atoms (except for 4-methyl-1-pentene) being 0.3 to 70.0% by mol;
(X-b) having, when measured in a cross fractionation chromatograph apparatus (CFC) using an infrared spectrophotometer as a detector part, at least one peak A of an amount of a component eluted present in the range of 100 to 140° C., and at least one peak B of an amount of a component eluted present at lower than 100° C.; and
(X-c) having a meso diad fraction (m) measured by 13C-NMR falling within the range of 95.0 to 100%.
2. The 4-methyl-1-pentene polymer particle (X) according to claim 1 , containing 10.0 to 95.0 parts by mass of a 4-methyl-1-pentene polymer (x1) which satisfies the following requirement (x1-a), and 5.0 to 90.0 parts by mass of a 4-methyl-1-pentene copolymer (x2) which satisfies the following requirement (x2-a) (provided that a total amount of the polymer (x1) and the copolymer (x2) is 100 parts by mass):
(x1-a) having a content of a constitutional unit derived from 4-methyl-1-pentene being 80.0 to 100% by mol, and a content of a constitutional unit derived from at least one olefin selected from ethylene and an α-olefin having 3 to 20 carbon atoms (except for 4-methyl-1-pentene) being 0 to 20.0% by mol; and
(x2-a) having a content of a constitutional unit derived from 4-methyl-1-pentene being 20.0 to 98.0% by mol, and a content of a constitutional unit derived from at least one olefin selected from ethylene and an α-olefin having 3 to 20 carbon atoms (except for 4-methyl-1-pentene) being 2.0 to 80.0% by mol and being larger than the content of the constitutional unit derived from at least one olefin selected from ethylene and an α-olefin having 3 to 20 carbon atoms (except for 4-methyl-1-pentene) in the polymer (x1).
3. The 4-methyl-1-pentene polymer particle (X) according to claim 2 , wherein
the polymer (x1) has an intrinsic viscosity [η] of in the range of 0.5 to 20 dl/g measured in decalin of 135° C., and a melting point (Tm) of in the range of 210 to 260° C. measured by DSC, and
the copolymer (x2) has an intrinsic viscosity [η] of in the range of 0.5 to 20 dl/g measured in decalin of 135° C., and a melting point (Tm) of in the range of lower than 210° C. measured by DSC, or NO detected peak indicating a melting point in DSC measurement.
4. The 4-methyl-1-pentene polymer particle (X) according to claim 1 , having an intrinsic viscosity [η] measured in decalin of 135° C. falling within the range of 0.5 to 10.0 dl/g.
5. The 4-methyl-1-pentene polymer particle (X) according to claim 1 , wherein in the requirement (X-c), the meso diad fraction (m) falls within the range of 98.0 to 100%.
6. A resin composed of a 4-methyl-1-pentene polymer particle (X) according to claim 1 .
7. A resin composition comprising a resin according to claim 6 .
8. A molded article obtained by molding from a 4-methyl-1-pentene polymer particle (X) according to claim 1 .
9. A method for producing a 4-methyl-1-pentene resin (X), comprising the steps of:
(1) producing a 4-methyl-1-pentene polymer (x1) which satisfies the following requirement (x1-a) by slurry polymerization using a metallocene catalyst; and
(2) producing a 4-methyl-1-pentene copolymer (x2) which satisfies the following requirement (x2-a) by slurry polymerization using a metallocene catalyst in the presence of the polymer (x1) obtained in the step (1) such that an amount of the copolymer (x2) falls within the range of 5.0 to 90.0 parts by mass with respect to 100 parts by mass in total of the polymer (x1) and the copolymer (x2):
(x1-a) having a content of a constitutional unit derived from 4-methyl-1-pentene being 80.0 to 100% by mol, and a content of a constitutional unit derived from at least one olefin selected from ethylene and an α-olefin having 3 to 20 carbon atoms (except for 4-methyl-1-pentene) being 0 to 20.0% by mol; and
(x2-a) having a content of a constitutional unit derived from 4-methyl-1-pentene being 20.0 to 98.0% by mol, and a content of a constitutional unit derived from at least one olefin selected from ethylene and an α-olefin having 3 to 20 carbon atoms (except for 4-methyl-1-pentene) being 2.0 to 80.0% by mol and being larger than the content of the constitutional unit derived from at least one olefin selected from ethylene and an α-olefin having 3 to 20 carbon atoms, other than 4-methyl-1-pentene, in the polymer (x1).
10. The method for producing a 4-methyl-1-pentene resin (X) according to claim 9 , wherein
the polymer (x1) has an intrinsic viscosity [η] of in the range of 0.5 to 20 dl/g measured in decalin of 135° C., and a melting point (Tm) of in the range of 210 to 260° C. measured by DSC, and
the copolymer (x2) has an intrinsic viscosity [η] of in the range of 0.5 to 20 dl/g measured in decalin of 135° C., and a melting point (Tm) of in the range of lower than 210° C. measured by DSC, or NO detected peak indicating a melting point in DSC measurement.
11. The method for producing a 4-methyl-1-pentene resin (X) according to claim 9 , wherein a temperature at which the polymerization in the step (1) is performed and a temperature at which the polymerization in the step (2) each independently fall within the range of 0 to 100° C.
12. The method for producing a 4-methyl-1-pentene resin (X) according to claim 9 , wherein the metallocene catalyst comprises a metallocene compound (A) and is a catalyst in the form of particles having D50 of volume statistics of in the range of 1 to 500 μm.
13. The method for producing a 4-methyl-1-pentene resin (X) according to claim 9 , wherein the metallocene catalyst comprises a metallocene compound (A) and a support (B), and the support (B) is a support in the form of particles comprising 20% by mass or more of an aluminum atom and having D50 of volume statistics in the range of 1 to 500 μm.
14. A 4-methyl-1-pentene resin (X) obtained by the method for producing a 4-methyl-1-pentene resin (X) according to claim 9 .
15. A resin composition comprising the 4-methyl-1-pentene resin (X) according to claim 14 .
16. A molded article obtained by molding from the 4-methyl-1-pentene resin (X) according to claim 14 .
17. A molded article obtained by molding from a 4-methyl-1-pentene resin (X) according to claim 6 .
18. A molded article obtained by molding from a 4-methyl-1-pentene polymer a resin composition (X) according to claim 7 .
19. A molded article obtained by molding from the 4-methyl-1-pentene resin composition (X) according to claim 7 .