Thermoplastic toughened matrix resins containing nanoparticles
Pre-impregnated composite material (prepreg) that can be cured/molded to form aerospace composite parts. The prepreg includes carbon reinforcing fibers and an uncured resin matrix. The resin matrix includes an epoxy resin component, polyethersulfone as a toughening agent, a thermoplastic particle component, a nanoparticle component and a curing agent.
1. A prepreg comprising:
A) reinforcing fibers;
B) an uncured resin matrix comprising:
a) a resin component that comprises one or more epoxy resins;
b) a thermoplastic particle component that comprises thermoplastic particles, said thermoplastic particle component being present in an amount ranging from 10 to 20 weight percent, based on the total weight of said uncured resin matrix, wherein said thermoplastic particles comprise hybrid polyamide particles and wherein each of said hybrid polyamide particles comprises a mixture of a semi-crystalline polyamide and an amorphous polyamide, said amorphous polyamide being present in an amount of from 20 to 80 weight percent, based on the total weight of said hybrid polyamide particle, and said semi-crystalline polyamide being present in an amount of from 20 to 80 weight percent, based on the total weight of said hybrid polyamide particle, and wherein said semi-crystalline polyamide and amorphous polyamide are comprised of different stereo isomeric forms of the polyamide which is the polymeric condensation product of 1,10-decane dicarboxylic acid and an amine component having the formula
c) a thermoplastic toughening agent comprising polyethersulfone, said toughening agent being present in an amount ranging from 5 to 15 weight percent, based on the total weight of said uncured resin matrix;
d) a nanoparticles component comprising nanoparticles, said nanoparticle component being present in an amount ranging from 10 to 30 weight percent, based on the total weight of said uncured resin matrix; and
e) a curing agent.
2. The prepreg according to claim 1 wherein said nanoparticles comprise calcite nanoparticles.
3. The prepreg according to claim 1 wherein said thermoplastic particles additionally comprise non-cross-linked polyamide particles.
4. The prepreg according to claim 3 wherein said non-cross-linked particles comprise polyamide 11.
5. The prepreg according to claim 1 wherein said curing agent is an aromatic amine selected from the group consisting of 3,3′-diaminodiphenyl sulphone and 4,4′-diaminodiphenyl sulphone.
6. A composite part or structure that has been formed by curing a composite material comprising a prepreg according to claim 1 .
7. The composite part or structure according to claim 6 wherein said composite part or structure forms at least part of an aircraft primary structure.
8. A method for making a composite part or structure comprising the step of providing a composite material that comprises a prepreg according to claim 1 and curing said composite material to form said composite part or structure.
9. The method for making a composite part or structure according to claim 8 wherein said composite part or structure forms at least part of an aircraft primary structure.
10. A method for making a prepreg that is curable to form a composite part, said method comprising the steps of:
A) providing reinforcing fibers comprising carbon fibers; and
B) impregnating said reinforcing fibers with an uncured resin matrix wherein said uncured resin matrix comprises:
a) a resin component that comprises one or more epoxy resins;
b) a thermoplastic particle component that comprises thermoplastic particles, said thermoplastic particle component being present in an amount ranging from 10 to 20 weight percent, based on the total weight of said uncured resin matrix, wherein said thermoplastic particles comprise hybrid polyamide particles and wherein each of said hybrid polyamide particles comprises a mixture of a semi-crystalline polyamide and an amorphous polyamide, said amorphous polyamide being present in an amount of from 20 to 80 weight percent, based on the total weight of said hybrid polyamide particle, and said semi-crystalline polyamide being present in an amount of from 20 to 80 weight percent, based on the total weight of said hybrid polyamide particle, and wherein said semi-crystalline polyamide and amorphous polyamide are comprised of different stereo isomeric forms of the polyamide which is the polymeric condensation product of 1,10-decane dicarboxylic acid and an amine component having the formula
c) a thermoplastic toughening agent comprising polyethersulfone, said toughening agent being present in an amount ranging from 5 to 15 weight percent, based on the total weight of said uncured resin matrix;
d) a nanoparticles component comprising nanoparticles, said nanoparticle component being present in an amount ranging from 12 to 30 weight percent, based on the total weight of said uncured resin matrix; and
e) a curing agent.
11. The method for making a prepreg according to claim 10 wherein said nanoparticles comprise calcite nanoparticles.
12. The method for making a prepreg according to claim 10 wherein said thermoplastic particles additionally comprise non-cross-linked polyamide particles.
13. The method for making a prepreg according to 12 wherein said non-cross-linked particles comprise polyamide 11.
14. The method for making a prepreg according to claim 10 wherein said curing agent is an aromatic amine selected from the group consisting of 3,3′-diaminodiphenyl sulphone and 4,4′-diaminodiphenyl sulphone.