Alloy member, process for producing said alloy member, and product including said alloy member

1. An alloy member having a chemical composition comprising:

25 atomic % or more and 33 atomic % or less of Co;

15 atomic % or more and 23 atomic % or less of Cr;

15 atomic % or more and 23 atomic % or less of Fe;

17 atomic % or more and 28 atomic % or less of Ni;

5 atomic % or more and 10 atomic % or less of Ti; and

1.8 atomic % or more and 7 atomic % or less of Mo, and

wherein the alloy member further comprises ultrafine grains having an average grain diameter of 100 nm or less that are dispersed and precipitated in a parent phase crystal grain, and

wherein the average crystal grain diameter of the parent phase crystal grain is 100 μm or less.

2. The alloy member according to claim 1 , wherein the ultrafine grain is a crystalline grain in which the Ni component and the Ti component are more enriched than in the parent phase crystal.

3. The alloy member according to claim 1 , wherein the chemical composition comprises 25 atomic % or more and less than 30 atomic % of Co; 15 atomic % or more and less than 20 atomic % of Cr; 15 atomic % or more and less than 20 atomic % of Fe; 23 atomic % or more and 28 atomic % or less of Ni; 7 atomic % or more and 10 atomic % or less of Ti; and 1.8 atomic % or more and 7 atomic % or less of Mo.

4. The alloy member according to claim 1 , wherein the chemical composition comprises 30 atomic % or more and 33 atomic % or less of Co; 20 atomic % or more and 23 atomic % or less of Cr; 20 atomic % or more and 23 atomic % or less of Fe; 17 atomic % or more and less than 23 atomic % of Ni; 5 atomic % or more and less than 7 atomic % of Ti; and 1.8 atomic % or more and 3 atomic % or less of Mo.

5. The alloy member according to claim 1 , wherein the alloy member has a tensile strength of 1100 MPa or more and a breaking elongation of 10% or more.

6. The alloy member according to claim 1 , wherein the parent phase crystal has an equiaxed crystal shape and the crystal structure thereof comprises at least one of a simple cubic system and a face-centered cubic system.

7. A process for producing an alloy member, comprising:

a raw material mixing and melting step comprising mixing and melting raw materials of an alloy composition to form a molten metal so that the alloy composition comprises:

25 atomic % or more and 33 atomic % or less of Co;

15 atomic % or more and 23 atomic % or less of Cr;

15 atomic % or more and 23 atomic % or less of Fe;

17 atomic % or more and 28 atomic % or less of Ni;

5 atomic % or more and 10 atomic % or less of Ti; and

1.8 atomic % or more and 7 atomic % or less of Mo, and;

an atomizing step of forming an alloy powder from the molten metal; and

an additive manufacturing step of forming an alloy laminated molded body having a desired shape by a metal powder additive manufacturing process using the alloy powder, and

wherein the alloy member further comprises ultrafine grains having an average grain diameter of 100 nm or less that are dispersed and precipitated in a parent phase crystal grain, and

wherein the average crystal grain diameter of the parent phase crystal grain is 100 μm or less.

8. The process for producing an alloy member according to claim 7 ,

wherein the alloy member obtained through the additive manufacturing step has a parent phase crystal, and

wherein the parent phase crystal has a columnar crystal shape and the crystal structure thereof comprises at least one of a simple cubic system and a face-centered cubic system.

9. A process for producing an alloy member comprising:

a raw material mixing and melting step comprising mixing and melting raw materials of an alloy composition to form a molten metal so that the alloy composition comprises:

25 atomic % or more and 33 atomic % or less of Co;

15 atomic % or more and 23 atomic % or less of Cr;

15 atomic % or more and 23 atomic % or less of Fe;

17 atomic % or more and 28 atomic % or less of Ni;

5 atomic % or more and 10 atomic % or less of Ti; and

1.8 atomic % or more and 7 atomic % or less of Mo, and;

an atomizing step of forming an alloy powder from the molten metal;

an additive manufacturing step of forming an alloy laminated molded body having a desired shape by a metal powder additive manufacturing process using the alloy powder; and

a pseudo solution heat treatment step of performing a pseudo solution heat treatment on the alloy laminated molded body in a temperature range of 1080° C. or more and 1180° C. or less, and

wherein the alloy member further comprises ultrafine grains having an average grain diameter of 100 nm or less that are dispersed and precipitated in a parent phase crystal grain, and wherein the average crystal grain diameter of the parent phase crystal grain is 100 μm or less.

10. The process for producing an alloy member according to claim 9 , wherein the pseudo solution heat treatment step is a step of holding the alloy laminated molded body in the temperature range, thereby forming a resultant, and then cooling the resultant with water or air.

11. The process for producing an alloy member according to claim 9 , comprising an aging treatment step of performing an aging treatment in a temperature range of more than 500° C. and less than 900° C. after the pseudo solution heat treatment step.

12. The process for producing an alloy member according to claim 9 , wherein the alloy member obtained through the pseudo solution heat treatment step has a parent phase crystal, and

wherein the parent phase crystal has an equiaxed crystal shape and the crystal structure thereof comprises at least one of a simple cubic system and a face-centered cubic system.