Process for producing a composite material
A process for producing a composite material comprising at least one particulate material and at least one polymeric binder, wherein the at least one particulate material and the at least one polymeric binder are mixed with one another and mechanically processed in the presence of at least one process auxiliary which reduces the mechanical and/or chemical interaction between the surfaces of the at least one particulate material and of the at least one polymeric binder, essentially dispensing with the use of solvents, characterized in that the weight ratio of process auxiliary to polymeric binder is within a range from 3:10 to 0.1:20.
1. A process for producing a composite material for an electrode of an electrochemical energy storage means, the process comprising:
mixing at least one particulate material and at least one polymeric binder, and
mechanically processing the at least one particulate material and the at least one polymeric binder in the presence of at least one process auxiliary to provide a composite material, wherein the particulate material comprises at least one electrode active material for an electrochemical energy storage means,
wherein the process is essentially solvent-free,
wherein the at least one process auxiliary reduces the mechanical and/or chemical interaction between the surfaces of the at least one particulate material and of the at least one polymeric binder,
wherein the mechanically processing is selected from the group consisting of kneading, extruding, calender rolling, and a combination thereof,
wherein a weight ratio of the at least one process auxiliary to the at least one polymeric binder is within a range from 3:10 to 0.1:20,
wherein the at least one process auxiliary is in a form of particles, and a ratio of an average particle diameter of the at least one particulate material to an average particle diameter of the at least one process auxiliary is within a range from 2000:1 to 0.4:1,
wherein the composite material is essentially free of pores, and
wherein the at least one process auxiliary is a separating agent.
2. The process according to claim 1 , further comprising mixing the at least one particulate material, the at least one polymeric binder, and the at least one process auxiliary prior to the mechanically processing.
3. The process according to claim 1 , wherein the weight ratio of the at least one process auxiliary to the at least one polymeric binder is within a range from 2:10 to 0.1:10.
4. The process according to claim 1 , wherein the at least one particulate material comprises at least one electrode active material for an electrochemical energy storage and the at least one polymeric binder comprises at least one polymer electrolyte.
5. The process according to claim 1 , wherein the at least one particulate material is in an amount of at least 85%, based on a total weight of the composite material.
6. The process according to claim 1 , wherein the composite material is in a form of a homogeneous film having a thickness of less than 300 μm.
7. A composite material comprising at least one particulate material, at least one polymeric binder, and at least one process auxiliary, characterized in that a weight ratio of the at least one process auxiliary to the at least one polymeric binder is within a range from 3:10 to 0.1:20, wherein the composite material is essentially free of pores.
8. The composite material according to claim 7 , wherein the at least one particulate material comprises at least one electrode active material and the at least one polymeric binder comprises at least one polymer electrolyte.
9. The composite material according to claim 7 , comprising:
(i) 85.0% to 98.9% by weight of the at least one particulate material;
(ii) 1.0% to 14.9% by weight of the at least one polymeric binder; and
(iii) 0.1% to 3.0% by weight of the at least one process auxiliary.
10. An electrochemical energy storage device or an electrochemical energy converter device having an electrode comprising the composite material according to claim 7 .
11. An electrochemical energy storage device or electrochemical energy converter device comprising the composite material according to claim 7 .
12. A process for producing a composite material, the process comprising:
mixing at least one particulate material and at least one polymeric binder, and
mechanically processing the at least one particulate material and the at least one polymeric binder in the presence of at least one process auxiliary to provide a composite material,
wherein the process is essentially solvent-free,
wherein the at least one process auxiliary reduces the mechanical and/or chemical interaction between the surfaces of the at least one particulate material and of the at least one polymeric binder,
wherein the mechanically processing is selected from the group consisting of kneading, extruding, calender rolling, and a combination thereof,
wherein a weight ratio of the at least one process auxiliary to the at least one polymeric binder is within a range from 3:10 to 0.1:20, and
wherein the at least one process auxiliary is a separating agent.
13. The process according to claim 1 , wherein the separating agent is selected from the group consisting of organic oxides including SiO 2 , Al 2 O 3 , ZrO, B 2 O 3 , or PbO, carbides including SiC, and nitrides including BN.