Adaption of textile article for radio frequency (RF) absorption and attenuation
The present disclosure describes techniques for fabricating a textile article from a laminate formed by curing a reinforced fiber matrix and a resin substrate. The resin substrate may include iron oxide particles, such as iron oxide, Fe 3 O 4 , that are capable of absorbing and attenuating RF signals within a desired RF signal range, namely 0 GHz-3 GHz, 3 GHz, −8 GHz, and greater than or equal to 10 GHz. The iron oxide particles may include Fe 3 O 4 Fe, Fe 3 O 4 Ni, or Fe 3 O 4 , and/or so forth. Each iron oxide particle is selected based on the RF signal range that the textile article is intended to absorb. In other words, a change in iron oxide particle composition and proportion by volume may impact the RF signals absorbed and attenuated by the textile article.
1. A method of fabricating a textile article that is configured to absorb and attenuate radio frequency (RF) signals, the method comprising:
generating a resin substrate by incorporating a first portion of iron oxide particles and a second portion of an elastic polymer solution;
generating a wet laminate by saturating a reinforced fiber matrix within the resin substrate;
determining a cure time for the wet laminate, based at least in part on a volume ratio of the first portion of iron oxide particles by volume relative to the second portion of elastic polymer solution by volume;
curing the wet laminate at room temperature for the cure time,
identifying an RF signal range for absorption and attenuation of RF signals to be less than 3 GHz; and
determining the iron oxide particles to be Fe3O4Fe, based at least in part on the RF signal range, and
quantifying the first portion of iron oxide particles and the second portion of elastic polymer solution based at least in part of a predetermined ratio by volume of the first portion and the second portion that corresponds to 1:16.
2. The method of claim 1 , wherein the cure time is further based at least in part on an additional volume ratio of the resin substrate to the reinforced fiber matrix.
3. The method of claim 1 , further comprising:
determining an RF signal range to which the textile article is to absorb and attenuate RF signals; and
quantifying the first portion of iron oxide particles based at least in part on the RF signal range.
4. The method of claim 3 , further comprising:
determining a required viscosity to overlay the resin substrate onto the reinforced fiber matrix;
determining that a current viscosity of the resin substrate is greater than the required viscosity; and
adding a third portion of at least one of a thinning fluid or a cure retarder to reduce the current viscosity to be less than or equal to the required viscosity.
5. The method of claim 3 , further comprising:
determining that an additional volume ratio of the resin substrate to the reinforced fiber matrix is greater than a predetermined volume ratio, the predetermined volume ratio corresponding to a volume ratio associated with a desired adhesive property associated with the reinforced fiber matrix and the resin substrate; and
adding at least one of a third portion of thinning fluid or a cure retarder to reduce the volume ratio to be equal to or less than the predetermined volume ratio.
6. The method of claim 1 , wherein the iron oxide particles may correspond to one or more of Fe3O4Fe, Fe3O4Ni, and Fe3O4.
7. A method of fabricating a textile article that is configured to absorb and attenuate radio frequency (RF) signals, the method comprising:
generating a resin substrate by incorporating a first portion of iron oxide particles and a second portion of an elastic polymer solution;
generating a wet laminate by saturating a reinforced fiber matrix within the resin substrate;
determining a cure time for the wet laminate, based at least in part on a volume ratio of the first portion of iron oxide particles by volume relative to the second portion of elastic polymer solution by volume; and
curing the wet laminate at room temperature for the cure time;
identifying an RF signal range for absorption and attenuation of the RF signals to be greater than or equal to 3 GHz and less than 8 GHz; and
determining the iron oxide particles to be Fe3O4Ni, based at least in part on the RF signal range, and
quantifying the first portion of iron oxide particles and the second portion of elastic polymer solution based at least in part of a predetermined ratio by volume of the first portion relative to the second portion that corresponds to 1:16, based at least in part on the RF signal range.
8. A method of fabricating a textile article that is configured to absorb and attenuate radio frequency (RF) signals, the method comprising:
generating a resin substrate by incorporating a first portion of iron oxide particles and a second portion of an elastic polymer solution;
generating a wet laminate by saturating a reinforced fiber matrix within the resin substrate;
determining a cure time for the wet laminate, based at least in part on a volume ratio of the first portion of iron oxide particles by volume relative to the second portion of elastic polymer solution by volume;
curing the wet laminate at room temperature for the cure time;
identifying an RF signal range for absorption and attenuation of RF signals to be greater than 10 GHz; and
determining the iron oxide particles to be Fe3O4, based at least in part on the RF signal range, and
quantifying the first portion of iron oxide particles and the second portion of elastic polymer solution based at least in part of a predetermined ratio by volume of the first portion relative to the second portion that corresponds to 1:16, based at least in part on the RF signal range.
9. A method of fabricating a textile article that is configured to absorb and attenuate radio frequency (RF) signals, the method comprising:
generating a resin substrate by incorporating a first portion of iron oxide particles and a second portion of an elastic polymer solution;
generating a wet laminate by saturating a reinforced fiber matrix within the resin substrate;
determining a cure time for the wet laminate, based at least in part on a volume ratio of the first portion of iron oxide particles by volume relative to the second portion of elastic polymer solution by volume;
curing the wet laminate at room temperature for the cure time;
identifying an RF signal range for absorption and attenuation of RF signals that include RF signals that are less than 3 GHz through to RF signals greater than 10 GHz;
determining the iron oxide particles to be a combination of Fe3O4Fe, Fe3O4Ni, and Fe3O4, based at least in part on the RF signal range, wherein a relative portion by volume of Fe3O4Fe, Fe3O4Ni, and Fe3O4 corresponds to 1:1:1; and
quantifying the first portion of iron oxide particles and the second portion of elastic polymer solution based at least in part of a predetermined ratio by volume of the first portion relative to the second portion that corresponds to 1:3, based at least in part on the RF signal range.
10. The method of claim 1 , wherein the iron oxide particles retain a spherical or near-spherical shape to reduce reflection of the RF signals.
11. A fabrication process for a textile article that is configured to absorb and attenuate RF signals, the fabrication process comprising:
identifying an RF signal range for absorption and attenuation of the RF signals that include RF signals that are less than 3 GHz through to RF signals greater than 10 GHz;
determining a type of iron oxide particles to be at least one of the following particles: Fe3O4Fe, Fe3O4Ni, and Fe3O4, based at least in part on the RF signal range;
quantifying a first portion of the iron oxide particles and a second portion of elastic polymer solution based at least in part on the RF signal range;
generating a wet laminate by saturating a reinforced fiber matrix within the resin substrate;
determining a cure time for the wet laminate, based at least in part on a volume ration of the first portion of iron oxide particles by volume relative to the second portion of elastic polymer solution by volume; and
curing the wet laminate at room temperature for the cure time.
12. The fabrication process of claim 11 , further comprising:
determining an amount of viscosity that is required to overlay the resin substrate onto the reinforced fiber matrix, and
wherein the first portion of the iron oxide particles and the second portion of the elastic polymer solution is further based at least in part on the amount of viscosity.
13. The fabrication process of claim 11 , further comprising:
determining a required viscosity to overlay the resin substrate onto the reinforced fiber matrix;
determining that a current viscosity of the resin substrate is greater than the required viscosity; and
adding a third portion of at least one of a thinning fluid or a cure retarder to reduce the current viscosity to be less than or equal to the required viscosity.
14. The fabrication process of claim 11 , wherein the iron oxide particles may correspond to one or more of Fe3O4Fe, Fe3O4Ni, and Fe3O4.
15. The fabrication process of claim 11 , wherein the fiber matrix corresponds to one of a bamboo fiber matrix, a cotton fiber matrix, a polyester fiber matrix, a nylon fiber matrix, or a wool fiber matrix, and
wherein, the elastic polymer solution comprises a natural rubber, an acrylic, or a silicone-based elastic polymer solution.
16. The method of claim 7 , wherein the cure time is further based at least in part on an additional volume ratio of the resin substrate to the reinforced fiber matrix.
17. The method of claim 7 , further comprising:
determining a required viscosity to overlay the resin substrate onto the reinforced fiber matrix;
determining that a current viscosity of the resin substrate is greater than the required viscosity; and
adding a third portion of at least one of a thinning fluid or a cure retarder to reduce the current viscosity to be less than or equal to the required viscosity.
18. The method of claim 8 , wherein the cure time is further based at least in part on an additional volume ratio of the resin substrate to the reinforced fiber matrix.
19. The method of claim 8 , further comprising:
determining a required viscosity to overlay the resin substrate onto the reinforced fiber matrix;
determining that a current viscosity of the resin substrate is greater than the required viscosity; and
adding a third portion of at least one of a thinning fluid or a cure retarder to reduce the current viscosity to be less than or equal to the required viscosity.
20. The method of claim 9 , wherein the cure time is further based at least in part on an additional volume ratio of the resin substrate to the reinforced fiber matrix.