Pitch granules which are solid at room temperature
Pitch granules including a core made up of a first composition including at least one pitch, the composition having a penetrability at 25° C. of 0 to 45 1/10 mm, a ring-and-ball softening temperature (TBA) of 55° C. to 175° C., understanding the penetrability as measured according to standard EN 1426 and the TBA as measured according to standard EN 1427, and a layer encapsulating at least one portion of the surface of the core, the layer being made up of a coating composition including at least one anti-caking agent.
1. Pitch pellets comprising:
a core constituted of a first composition comprising at least one pitch, said composition having a penetrability at 25° C. ranging from 1 to 45 1/10 mm and a ring and ball softening point (RBSP) ranging from 55° C. to 175° C., wherein the penetrability is measured according to the standard EN 1426 and that the RBSP is measured according to the standard EN 1427, and
a layer coating at least part of the surface of the core, said layer being constituted of a coating composition comprising at least one anticaking agent chosen from pyrogenic silicas, and mixtures thereof, wherein the pyrogenic silicas have a specific surface area of between 120 and 280 m 2 /g.
2. The pitch pellets of claim 1 , wherein the anticaking agent is chosen from hydrophobic or hydrophilic pyrogenic silicas and mixtures thereof.
3. The pitch pellets of claim 1 , wherein the coating composition comprises at least 10% by mass of anticaking agent, relative to the total mass of the composition.
4. The pitch pellets of claim 3 , wherein the coating composition comprises from 10% to 90% by mass of anticaking agent, relative to the total mass of the composition.
5. The pitch pellets of claim 4 , wherein the coating composition comprises from 15% to 90% by mass of anticaking agent, relative to the total mass of the composition.
6. The pitch pellets of claim 1 , wherein the coating composition further comprises at least one viscosifying compound.
7. The pitch pellets of claim 6 , wherein the viscosifying compound is selected from the group consisting of:
gelling compounds;
polyethylene glycols (PEGs);
and mixtures thereof.
8. The pitch pellets of claim 6 , wherein the viscosifying compound is chosen from gelling compounds of plant or animal origin.
9. The pitch pellets as claimed 8 , wherein the gelling compound is selected from the group consisting of gelatin, agar-agar, alginates, cellulose derivatives, starches, modified starches and gellan gums.
10. The pitch pellets of claim 6 , wherein the viscosifying compound is chosen from polyethylene glycols (PEGs) having a molecular weight of between 800 g·mol −1 and 8000 g·mol −1 .
11. The pitch pellets of claim 10 , wherein the viscosifying compound is selected from the group consisting of: a PEG with a molecular weight of 800 g·mol −1 (PEG-800), a PEG with a molecular weight of 1000 g·mol −1 (PEG-1000), a PEG with a molecular weight of 1500 g·mol −1 (PEG-1500), a PEG with a molecular weight of 4000 g·mol −1 (PEG-4000) and a PEG with a molecular weight of 6000 g·mol −1 (PEG-6000).
12. The pitch pellets of claim 1 , wherein the coating composition represents between 0.2% and 10% by mass, relative to the total mass of the core of the pitch pellets.
13. The pitch pellets of claim 1 , wherein the coating composition represents between 0.5% and 8% by mass, relative to the total mass of the core of the pitch pellets.
14. The pitch pellets of claim 1 , wherein the coating composition represents between 0.5% and 5% by mass, relative to the total mass of the core of the pitch pellets.
15. The pitch pellets of claim 1 , wherein the size of the pellets is such that the longest mean dimension is less than or equal to 50 mm.
16. The pitch pellets of claim 15 , wherein the size of the pellets is such that the longest mean dimension is from 2 to 30 mm.
17. The pitch pellets of claim 1 , wherein the pellets solid at ambient temperature.
18. A process for manufacturing the pitch pellets of claim 1 , comprising:
i) forming the core of the pellets using a first composition comprising at least one pitch, and
ii) coating the core of the pellets over all or part of their surface with a coating composition comprising at least one anticaking compound.
19. A process comprising at least one of transporting, storing, and handling pitch at ambient temperature, wherein the pitch is in the form of the pitch pellets of claim 1 .