Decorative film and method for producing decorative molded body using same

1. A decorative film for sticking on a resin molded body by thermoforming, comprising:

a sealing layer (I) comprising a polypropylene-based resin (A); and

a layer (II) comprising a polypropylene-based resin (B),

wherein the polypropylene-based resin (A) satisfies (a1) to (a4) and the polypropylene-based resin (B) satisfies (b1) and (b2):

(a1) the melt flow rate of polypropylene-based resin (A) (MFR(A)) (at 230° C., a load of 2.16 kg) is more than 0.5 g/10 minutes,

(a2) the polypropylene-based resin (A) is a metallocene catalyst-based propylene-based polymer,

(a3) the melting peak temperature (Tm(A)) is lower than 150° C.,

(a4) the molecular weight distribution (Mw/Mn(A)) obtained by GPC measurement is 1.5 to 3.5,

(b1) the melt flow rate of polypropylene-based resin (B) (MFR(B)) (at 230° C., a load of 2.16 kg) and MFR(A) satisfy a relational expression (b-1);

MFR ( B )< MFR ( A )( b -1), and

(b2) the melting peak temperature (Tm(B)) and Tm(A) satisfy a relational expression (b-2);

Tm ( B )> Tm ( A )( b -2).

2. A decorative film for sticking on a resin molded body by thermoforming, comprising:

a sealing layer (I) comprising a polypropylene-based resin (A); and

a layer (II) comprising a polypropylene-based resin (B),

wherein the polypropylene-based resin (A) satisfies (a1) and (a5) and the polypropylene-based resin (B) satisfies (b1) and (b3):

(a1) the melt flow rate of polypropylene-based resin (A) (MFR(A)) (at 230° C., a load of 2.16 kg) is more than 0.5 g/10 minutes,

(a5) the crystallization temperature (Tc(A)) is lower than 100° C.,

(1) the melt flow rate of polypropylene-based resin (B) (MFR(B)) (at 230° C., a load of 2.16 kg) and MFR(A) satisfy a relational expression (b-1);

MFR ( B )< MFR ( A )( b -1), and

(b3) the crystallization temperature (Tc(A)) and (Tc(B)) satisfy a relational expression (b-3);

Tc ( B )> Tc ( A )( b -3).

3. A decorative film for sticking on a resin molded body by thermoforming, comprising:

a sealing layer (I) comprising a polypropylene-based resin (A); and

a layer (II) comprising a polypropylene-based resin (B),

wherein the polypropylene-based resin (A) satisfies (a1) and the polypropylene-based resin (B) satisfies (b1):

(a1) the melt flow rate of polypropylene-based resin (A) (MFR(A)) (at 230° C., a load of 2.16 kg) is more than 0.5 g/10 minutes, and

(b1) the melt flow rate of polypropylene-based resin (B) (MFR(B)) (at 230° C., a load of 2.16 kg) and MFR(A) satisfy a relational expression (b-1);

MFR ( B )< MFR ( A )( b -1),

wherein the sealing layer (I) comprises a resin composition (X3) in which the weight ratio of the propylene-based resin (A) to an ethylene-α-olefin random copolymer (C) is in a range of 97:3 to 5:95, and

the ethylene-α-olefin random copolymer (C) satisfies (c1) to (c3):

(c1) the ethylene content [E(C)] is 65% by weight or more,

(c2) the density is 0.850 to 0.950 g/cm 3 , and

(c3) the melt flow rate of ethylene-α-olefin random copolymer (C) (MFR(C)) (230° C., a load of 2.16 kg) is 0.1 to 100 g/10 minutes.

4. A decorative film for sticking on a resin molded body by thermoforming, comprising:

a sealing layer (I) comprising a polypropylene-based resin (A); and

a layer (II) comprising a polypropylene-based resin (B),

wherein the polypropylene-based resin (A) satisfies (a1) and the polypropylene-based resin (B) satisfies (b1):

(a1) the melt flow rate of polypropylene-based resin (A) (MFR(A)) (at 230° C., a load of 2.16 kg) is more than 0.5 g/10 minutes, and

(b1) the melt flow rate of polypropylene-based resin (B) (MFR(B)) (at 230° C., a load of 2.16 kg) and MFR(A) satisfy a relational expression (b-1);

MFR ( B )< MFR ( A )( b -1),

wherein the sealing layer (I) comprises a resin composition (X4) in which the weight ratio of the propylene-based resin (A) to a thermoplastic elastomer (D) is in a range of 97:3 to 5:95, and the thermoplastic elastomer (D) satisfies (d1) to (d3):

(d1) the thermoplastic elastomer (D) is a thermoplastic elastomer in which at least one selected from the group consisting of propylene and butene is a main component,

(d2) the density is 0.850 to 0.950 g/cm 3 , and

(d3) the melt flow rate of thermoplastic elastomer (D) (MFR(D)) (230° C., a load of 2.16 kg) is 0.1 to 100 g/10 minutes.

5. A decorative film for sticking on a resin molded body by thermoforming, comprising:

a sealing layer (I) comprising a polypropylene-based resin (A); and

a layer (II) comprising a polypropylene-based resin (B),

wherein the polypropylene-based resin (A) satisfies (a1) and the polypropylene-based resin (B) satisfies (b1):

(a1) the melt flow rate of polypropylene-based resin (A) (MFR(A)) (at 230° C., a load of 2.16 kg) is more than 0.5 g/10 minutes, and

(1) the melt flow rate of polypropylene-based resin (B) (MFR(B)) (at 230° C., a load of 2.16 kg) and MFR(A) satisfy a relational expression (b-1);

MFR ( B )< MFR ( A )( b -1),

wherein the sealing layer (I) comprises a resin composition (X5) in which the weight ratio of the propylene-based resin (A) and a thermoplastic resin (E) is in a range of 97:3 to 5:95 and the thermoplastic resin (E) satisfies (e1), and the resin composition (X5) satisfies (x1):

(e1) the thermoplastic resin (E) comprises at least one selected from the group consisting of an alicyclic hydrocarbon group and an aromatic hydrocarbon group, and

(x 1) the isothermal crystallization time (t(X)) (second) of the resin composition (X5) determined by a differential scanning calorimeter (DSC) satisfies expression (x-1);

t ( X )≥1.5× t ( A )( x -1)

wherein t(A) represents isothermal crystallization time (second) of the polypropylene-based resin (A) measured at a temperature 10° C. higher than the crystallization initiation temperature of the propylene-based resin (A) and t(X) is isothermal crystallization time (second) of the resin composition (X5) measured at a temperature that is 10° C. higher than the crystallization initiation temperature of the propylene-based resin (A).

6. A decorative film for sticking on a resin molded body by thermoforming, comprising:

a sealing layer (I) comprising a polypropylene-based resin (A); and

a layer (II) comprising a polypropylene-based resin (B),

wherein the polypropylene-based resin (A) satisfies (a1) and the polypropylene-based resin (B) satisfies (b1):

(a1) the melt flow rate of polypropylene-based resin (A) (MFR(A)) (at 230° C., a load of 2.16 kg) is more than 0.5 g/10 minutes, and

(b1) the melt flow rate of polypropylene-based resin (B) (MFR(B)) (at 230° C., a load of 2.16 kg) and MFR(A) satisfy a relational expression (b-1);

MFR ( B )< MFR ( A )( b -1),

wherein the sealing layer (I) comprises a propylene-ethylene block copolymer (F) that satisfies (f1) and (f2):

(f1) the melting peak temperature (Tm(F)) is 110 to 170° C., and

(f2) the propylene-ethylene block copolymer (F) comprises 5 to 97% by weight of a component (F1) comprising a propylene homopolymer or a propylene-ethylene random copolymer and 3 to 95% by weight of a component (F2) comprising a propylene-ethylene random copolymer having an ethylene content larger than that of the component (F1).

7. The decorative film according to claim 1 , wherein the polypropylene-based resin (A) is a propylene-α-olefin copolymer.

8. The decorative film according to claim 1 , wherein Tm(A) is 140° C. or lower.

9. The decorative film according to claim 3 , wherein the ethylene-α-olefin random copolymer (C) further satisfies at least one selected from the group consisting of (c4) and (c5):

(c4) the melting peak temperature (Tm(C)) is 30 to 130° C., and

(c5) the ethylene-α-olefin random copolymer (C) is a random copolymer of ethylene and an α-olefin having 3 to 20 carbon atoms.

10. The decorative film according to claim 4 , wherein the thermoplastic elastomer (D) is at least one copolymer selected from the group consisting of a propylene-ethylene copolymer having an ethylene content of less than 50 wt %, a butene-ethylene copolymer having an ethylene content of less than 50%, a propylene-ethylene-butene copolymer having an ethylene content of less than 50 wt %, a propylene-butene copolymer, and a butene homopolymer.

11. The decorative film according to claim 4 , wherein the thermoplastic elastomer (D) further satisfies (d4):

(d4) the melting peak temperature (Tm(D)) is 30 to 170° C.

12. The decorative film according to claim 5 , wherein the thermoplastic resin (E) is a styrene-based elastomer.

13. The decorative film according to claim 5 , wherein the thermoplastic resin (E) is an alicyclic hydrocarbon resin.

14. The decorative film according to claim 6 , wherein the propylene-ethylene block copolymer (F) further satisfies at least one selected from the group consisting of (f3) to (f5):

(f3) the ethylene content in the propylene-ethylene block copolymer (F) is 0.15 to 85% by weight,

(f4) the ethylene content of the component (F1) is in the range of 0 to 6% by weight, and

(f5) the ethylene content of the component (F2) is in the range of 5 to 90% by weight.

15. A method for producing a decorative molded body comprising:

preparing the decorative film according to claim 1 ,

preparing a resin molded body,

setting the resin molded body and the decorative film in a pressure-reducible chamber box,

reducing the pressure in the chamber box,

heating and softening the decorative film,

pushing the decorative film onto the resin molded body, and

returning the inside of the pressure-reduced chamber box to atmospheric pressure or pressurizing the inside.

16. The method for producing a decorative molded body according to claim 15 , wherein the resin molded body comprises a propylene-based resin composition.

17. The decorative film according to claim 2 , wherein the polypropylene-based resin (A) is a propylene-α-olefin copolymer.

18. The decorative film according to claim 10 , wherein the thermoplastic elastomer (D) further satisfies (d4):

(d4) the melting peak temperature (Tm(D)) is 30 to 170° C.

19. A method for producing a decorative molded body comprising:

preparing the decorative film according to claim 2 ,

preparing a resin molded body,

setting the resin molded body and the decorative film in a pressure-reducible chamber box,

reducing the pressure in the chamber box,

heating and softening the decorative film,

pushing the decorative film onto the resin molded body, and

returning the inside of the pressure-reduced chamber box to atmospheric pressure or pressurizing the inside.

20. A method for producing a decorative molded body comprising:

preparing the decorative film according to claim 3 ,

preparing a resin molded body,

setting the resin molded body and the decorative film in a pressure-reducible chamber box,

reducing the pressure in the chamber box,

heating and softening the decorative film,

pushing the decorative film onto the resin molded body, and

returning the inside of the pressure-reduced chamber box to atmospheric pressure or pressurizing the inside.

21. A method for producing a decorative molded body comprising:

preparing the decorative film according to claim 4 ,

preparing a resin molded body,

setting the resin molded body and the decorative film in a pressure-reducible chamber box,

reducing the pressure in the chamber box,

heating and softening the decorative film,

pushing the decorative film onto the resin molded body, and

returning the inside of the pressure-reduced chamber box to atmospheric pressure or pressurizing the inside.

22. A method for producing a decorative molded body comprising:

preparing the decorative film according to claim 5 ,

preparing a resin molded body,

setting the resin molded body and the decorative film in a pressure-reducible chamber box,

reducing the pressure in the chamber box,

heating and softening the decorative film,

pushing the decorative film onto the resin molded body, and

returning the inside of the pressure-reduced chamber box to atmospheric pressure or pressurizing the inside.

23. A method for producing a decorative molded body comprising:

preparing the decorative film according to claim 6 ,

preparing a resin molded body,

setting the resin molded body and the decorative film in a pressure-reducible chamber box,

reducing the pressure in the chamber box,

heating and softening the decorative film,

pushing the decorative film onto the resin molded body, and

returning the inside of the pressure-reduced chamber box to atmospheric pressure or pressurizing the inside.

24. A decorative film for sticking on a resin molded body by thermoforming, comprising:

a sealing layer (I) comprising a propylene-ethylene block copolymer (F); and

a layer (II) comprising a polypropylene-based resin (B),

wherein the propylene-ethylene block copolymer (F) satisfies (a1), (f1) and (f2) and the polypropylene-based resin (B) satisfies (b 1):

(a1) the melt flow rate of propylene-ethylene block copolymer (F) (MFR(F)) (at 230° C., a load of 2.16 kg) is more than 0.5 g/10 minutes,

(f1) the melting peak temperature (Tm(F)) is 110 to 170° C.,

(f2) the propylene-ethylene block copolymer (F) comprises 5 to 97% by weight of a component (F1) comprising a propylene homopolymer or a propylene-ethylene random copolymer and 3 to 95% by weight of a component (F2) comprising a propylene-ethylene random copolymer having an ethylene content larger than that of the component (F1), and

(b1) the melt flow rate of polypropylene-based resin (B) (MFR(B)) (at 230° C., a load of 2.16 kg) and MFR(F) satisfy a relational expression (b-1);

MFR ( B )< MFR ( A )( b -1).

25. A method for producing a decorative molded body comprising:

preparing the decorative film according to claim 24 ,

preparing a resin molded body,

setting the resin molded body and the decorative film in a pressure-reducible chamber box,

reducing the pressure in the chamber box,

heating and softening the decorative film,

pushing the decorative film onto the resin molded body, and

returning the inside of the pressure-reduced chamber box to atmospheric pressure or pressurizing the inside.