Grain-oriented electrical steel sheet with excellent magnetic characteristics
A grain-oriented electrical steel sheet having a metallographic structure after secondary-recrystallized annealing including matrix grains of Goss-oriented secondary recrystallized grains, wherein an existence frequency of Goss-oriented crystal grains having a major diameter of 5 mm or less in the matrix grains is 1.5 grains/cm 2 or more and 8 grains/cm 2 or less, and the magnetic flux density B8 is 1.88 T or more, and wherein deviation angles from a rolling direction of [001] direction of the Goss-oriented crystal grains having the major diameter of 5 mm or less are 7″ or less and 5° or less, in terms of a simple or arithmetic average of α angle and β angle, respectively, wherein the α angle represents an angle formed by a longitudinal direction and a projection of the [001] on a specimen surface, and the β angle represents a tilt of the [001] out of the specimen surface.
1. A grain-oriented electrical steel sheet composed of 2.5 to 3.5% by mass of Si, with a balance being Fe and inevitable elements, and having a sheet thickness of 0.18 to 0.35 mm,
wherein its metallographic structure after secondary-recrystallized annealing includes matrix grains of Goss-oriented secondary recrystallized grains, and wherein, in the metallographic structure, an existence frequency of Goss-oriented crystal grains having a major or long diameter of 5 mm or less present in the matrix grains is 1.5 grains/cm 2 or more and 8 grains/cm 2 or less, and the magnetic flux density B8 is 1.88 T or more, wherein deviation angles from a rolling direction of [001] direction of the Goss-oriented crystal grains having the major or long diameter of 5 mm or less are 7° or less and 5° or less, in terms of a simple or arithmetic average of α angle and β angle, respectively, wherein the α angle and the β angle are as follows:
α angle; an angle formed by a longitudinal direction and a projection of the [001] on specimen surface, and
β angle; a tilt of the [001] out of the specimen surface.
2. A grain-oriented electrical steel sheet comprising 2.5 to 3.5% by mass of Si, with a balance comprising Fe and inevitable elements, and having a sheet thickness of 0.18 to 0.35 mm,
wherein its metallographic structure after secondary-recrystallized annealing includes matrix grains of Goss-oriented secondary recrystallized grains, and wherein, in the metallographic structure, an existence frequency of Goss-oriented crystal grains having a major or long diameter of 5 mm or less present in the matrix grains is 1.5 grains/cm 2 or more and 8 grains/cm 2 or less, and the magnetic flux density B8 is 1.88 T or more, wherein deviation angles from a rolling direction of [001] direction of the Goss-oriented crystal grains having the major or long diameter of 5 mm or less are 7° or less and 5° or less, in terms of a simple or arithmetic average of α angle and β angle, respectively, wherein the α angle and the β angle are as follows:
α angle; an angle formed by a longitudinal direction and a projection of the [001] on specimen surface, and
β angle; a tilt of the [001] out of the specimen surface.