Method of using water erodible marine antifouling coating
A method is described for inhibiting marine fouling on a surface. The surface is contacted with a composition comprising a waterborne polyurethane that is crosslinked with an acrylic acid functionalized polysaccharide, water, and a preservative. The composition is then dried to form a deposited film. The polysaccharide may be xanthan.
1. A method of inhibiting marine fouling of a surface, the method comprising:
contacting the surface with a composition to produce a coated surface, the composition comprising:
a waterborne polyurethane (WBPU) crosslinked with an acrylic acid functionalized polysaccharide;
water; and
a preservative dispersed in the crosslinked WBPU, and
drying the coated surface to produce a treated surface having a deposited film.
2. The method of claim 1 , wherein the acrylic acid functionalized polysaccharide is present in the deposited film at a weight percentage of 0.1-5.0 wt % relative to a total weight of the deposited film.
3. The method of claim 1 , wherein the polysaccharide is at least one selected from the group consisting of xanthan, beta-glucan, dextran, inulin, galactan, glycogen, hemicellulose, levan, lignin, mannan, pectin, amylopectin, and amylose.
4. The method of claim 1 , wherein the acrylic acid functionalized polysaccharide comprises 1-50 wt % acrylic acid functional groups relative to a total weight of the acrylic acid functionalized polysaccharide.
5. The method of claim 1 , wherein the polysaccharide is xanthan.
6. The method of claim 1 , wherein the composition comprises 50-90 wt % water relative to a total weight of the composition.
7. The method of claim 1 , wherein the preservative is present at a weight percentage of 0.01-2.0 wt % relative to a total weight of the composition.
8. The method of claim 1 , wherein the composition further comprises a pigment.
9. The method of claim 1 , wherein the composition consists of the crosslinked WBPU, the preservative, and water.
10. The method of claim 1 , wherein the contacting is done by electrocoating, spraying, electrostatic spraying, dipping, rolling, brushing, dropping, spin coating.
11. The method of claim 1 , wherein the preservative is zinc pyrithione.
12. The method of claim 1 , wherein the deposited film has a density in a range of 0.8-2.0 g/cm 3 .
13. The method of claim 1 , wherein the crosslinked WBPU has a number average molecular weight in a range of 26-32 kDa.
14. The method of claim 13 , wherein the number average molecular weight decreases to 22-24 kDa following at least 24 h of immersion in water, seawater, or brine.
15. The method of claim 1 , wherein the deposited film has a water contact angle in a range of 45°-67°.
16. The method of claim 1 , wherein the deposited film, when immersed in water, seawater, or brine for at least 24 hours, absorbs no more than 15 wt % water in relation to a weight of the deposited film.
17. The method of claim 1 , wherein the deposited film is in the form of a layer in direct contact with the surface, the deposited film having an average thickness in a range of 1-200 μm.
18. The method of claim 1 , wherein the deposited film, when placed in contact with water, seawater, or brine for 90 days, has a dry weight loss in a range of 1.5-8.0 wt % relative to an initial dry weight.