SiC composite and method for manufacturing the same
The present invention relates to a SiC composite and a method for manufacturing the same. More particularly, the present invention relates to a slurry composition for ceramic matrix composites which can not only reduce the number of precursor impregnation pyrolysis (PIP) cycles but also be useful in the PIP process to increase hardness, thermal stability, and relative density.
1. A slurry composition for ceramic matrix composites, comprising:
at least 58 vol % of a SiC filler;
a dispersion; and
a dispersant,
wherein the SiC filler consists of only fine particles having a D 50 diameter of more than 100 nm and less than 200 nm or consists of the fine particles and coarse particles having a D 50 diameter of 3 μm to 20 μm in a ratio of 2:1 to 4.5:1.
2. The slurry composition of claim 1 , wherein the SiC filler is oxidized.
3. The slurry composition of claim 1 , wherein the dispersion medium is water and the dispersant is included in an amount of 0.6 to 1.2 wt % based 100 wt % of SiC filler in the slurry composition for ceramic matrix composites.
4. A SiC particle-reinforced SiC composite densified through precursor impregnation pyrolysis (PIP) of a green body prepared by drying a slurry composition for ceramic matrix composites according to claim 1 ,
wherein the composite has a hardness of 10 GPa or more after 4 or less PIP cycles.
5. The SiC particle-reinforced SiC composite of claim 4 , wherein an amount of a precursor-derived ceramic phase in the SiC particle-reinforced SiC composite is 9.5 to 37 vol %.
6. The SiC particle-reinforced SiC composite of claim 4 , wherein a density of the SiC particle-reinforced SiC composite is 2.5 to 3 g/cm 3 .
7. A method for manufacturing a SiC composite, the method comprising:
preparing a slurry composition for ceramic matrix composites of claim 1 ;
impregnating the slurry into ceramic fiber bundles, carbon fiber bundles, or a fiber preform made thereof;
drying and stabilizing the fiber preform in which the slurry is impregnated;
impregnating a liquid ceramic precursor into the preform and curing the same to form a ceramic matrix composite preform; and
pyrolyzing the ceramic precursor in the ceramic matrix composite preform.
8. The method of claim 7 , further comprising heat treating the slurry-impregnated fiber preform at a temperature of 1500° C. or higher to promote crystallization of an amorphous SiC filler and to remove oxides from the surface of the SiC filler at the step of drying and stabilizing the fiber preform.
9. The method of claim 7 , wherein the step of impregnating a liquid ceramic precursor into the preform and curing the same comprises thermally curing a liquid ceramic precursor to 150 to 350° C.
10. The method of claim 7 , wherein the ceramic precursor comprises at least one of polysilane and polycarbosilane.