The present disclosure provides methods of compensation for capacity loss resulting from cycle-induced lithium consumption in an electrochemical cell including at least one electrode. Such methods may include adding a lithiation additive to the at least one electrode so as to create a lithium source. The lithium source compensates for cycle-induced lithiation loss such that the electrochemical cell having the lithiation additive experiences total capacity losses of less than or equal to about 5% of an initial capacity prior to cycling of lithium. The lithiation additive includes a lithium silicate represented by the formula Li u H r , where H r =Li y-u SiO z and where 0≤y≤3.75 and 0≤z≤2 and u is a useable portion of y, 0≤u≤y. The lithium source may include z 4 L i 4 Si O 4 and Li m Si, where 0≤m≤4.4.
1. A method of forming at least one electrode for an electrochemical cell to compensate for capacity loss resulting from cycle-induced lithium consumption, the method comprising:
combining a lithiation additive with an electroactive material to form the at least one electrode to create a lithium source capable of compensating for cycle-induced lithiation loss that occurs when lithium is cycled in the electrochemical cell such that the electrochemical cell experiences a total capacity loss of less than or equal to about 5% of an initial capacity prior to cycling of lithium in the electrochemical cell, wherein the lithiation additive comprises a lithium silicate represented by the formula Li u H r , wherein H r =Li y-u SiO z and wherein 0≤y≤3.75 and 0<z≤2 and u is a useable portion of y, 0≤u≤y.
2. The method of claim 1 , wherein the lithium source comprises
z
4
L
i
4
Si
O
4
and Li m Si, where 0≤m≤4.4.
3. The method of claim 1 , wherein the at least one electrode includes greater than or equal to about 1 wt. % to less than or equal to about 50 wt. % of the lithiation additive.
4. The method of claim 1 , wherein the method includes combining the lithiation additive with the electroactive material and a current collector in an environment comprising oxygen that is substantially free of water and has a dew point of greater than or equal to about −100° C. to less than or equal to about 0° C.
5. The method of claim 4 , wherein the combining includes mixing greater than or equal to about 1 wt. % to less than or equal to about 50 wt. % of the lithiation additive with greater than or equal to about 50 wt. % to less than or equal to about 95 wt. % of electroactive material and disposing the mixture on a first surface of the current collector.
6. The method of claim 4 , wherein the combining includes forming a lithiation layer comprising the lithiation additive adjacent to the current collector and forming an electroactive layer on one or more exposed surfaces of the lithiation layer.
7. The method of claim 6 , wherein the lithiation layer has a thickness greater than or equal to about 10 nm to less than or equal to about 10 μm; and the electroactive layer has a thickness greater than or equal to about 500 nm to less than or equal to about 200 μm.
8. The method of claim 4 , wherein the electroactive material is selected from the group consisting of: lithium, silicon, silicon oxide, graphite, graphene, carbon nanotubes, lithium titanium oxide (Li 4 Ti 5 O 12 ), tin (Sn), vanadium oxide (V 2 O 5 ), tin oxide (SnO), titanium dioxide (TiO 2 ), titanium niobium oxide (Ti x Nb y O z , where 0≤x≤2, 0≤y≤24, and 0≤z≤64), iron sulfide (FeS), and combinations thereof.
9. The method of claim 1 , wherein the method further includes cycling lithium in the electrochemical cell.
10. A method of forming at least one electrode for an electrochemical cell to compensate for capacity loss resulting from cycle-induced lithium consumption, the method comprising:
combining a lithiation additive with an electroactive material to form a mixture; and
casting the mixture on a current collector in an environment comprising oxygen that is substantially free of water and has a dew point of greater than or equal to about −100° C. to less than −50° C. to form the at least one electrode of the electrochemical cell; and
incorporating the at least one electrode into the electrochemical cell,
wherein the lithiation additive is a lithium source that compensates for cycle-induced lithiation loss that occurs when lithium is cycled in the electrochemical cell such that the electrochemical cell experiences a total capacity loss of less than or equal to about 5% of an initial capacity prior to cycling of lithium in the electrochemical cell, wherein the lithiation additive comprises a lithium silicate represented by the formula Li u H r , wherein H r =Li y-u SiO z and wherein 0≤y≤3.75 and 0≤z≤2 and u is a useable portion of y, 0≤u≤y.
11. The method of claim 10 , wherein the combining includes mixing greater than or equal to about 1 wt. % to less than or equal to about 50 wt. % of the lithiation additive with greater than or equal to about 50 wt. % to less than or equal to about 95 wt. % of electroactive material and disposing the mixture on a first surface of the current collector.
12. The method of claim 10 , wherein the lithiation layer has a thickness greater than or equal to about 10 nm to less than or equal to about 10 μm; and the electroactive layer has a thickness greater than or equal to about 500 nm to less than or equal to about 200 μm.
13. The method of claim 10 , wherein the electroactive material is selected from the group consisting of: lithium, silicon, silicon oxide, graphite, graphene, carbon nanotubes, lithium titanium oxide (Li 4 Ti 5 O 12 ), tin (Sn), vanadium oxide (V 2 O 5 ), tin oxide (SnO), titanium dioxide (TiO 2 ), titanium niobium oxide (Ti x Nb y O z , where 0≤x≤2, 0≤y≤24, and 0≤z≤64), iron sulfide (FeS), and combinations thereof.
14. The method of claim 10 , wherein the combining further includes combining an electrically conductive material and a binder with the lithiation additive and the electroactive material to form the mixture.