Filter element

1. A filter element ( 30 ) being porous to permit flow therethrough, comprising a filter body ( 20 ) which forms a porous sintered structure and is constructed with filter body particles ( 10 , 14 ) which are at least in part polysulfide particles ( 10 ), wherein:

the polysulfide particles ( 10 ) contain a tempered polysulfide; and

the tempering is carried out at a temperature of 255° C. to 275° C. over a period of time from 7 to 24 hours prior to sintering.

2. The filter element ( 30 ) of claim 1 , wherein the polysulfide particles ( 10 ) are polyphenylene sulfide particles.

3. The filter element ( 30 ) of claim 1 , wherein all filter body particles contain polysulfide.

4. The filter element ( 30 ) of claim 1 , wherein at least part of the filter body particles consists of polysulfide.

5. The filter element ( 30 ) of claim 4 , wherein all filter body particles consist of polysulfide.

6. The filter element of claim 1 , wherein the polysulfide particles ( 10 ) contain at least two polysulfides of different configuration.

7. The filter element ( 30 ) of claim 1 , wherein the filter body particles ( 10 ) have a melt flow index of at the most 500 g/10 min.

8. The filter element ( 30 ) of claim 1 , wherein the polysulfide particles ( 10 ) contain unfilled polysulfide.

9. The filter element ( 30 ) of claim 1 , wherein the polysulfide particles ( 10 ) contain at least one tempered polysulfide and at least one untempered polysulfide.

10. The filter element ( 30 ) of claim 1 , which has a porosity of at least 30%.

11. The filter element ( 30 ) of claim 1 , wherein the filter body ( 20 ) is formed such that the pressure loss across the filter element ( 30 ), measured with respect to an air flow without foreign matter load at a volumetric flow rate of 12.011 m 3 /(m 2 ×min) and with an air flow-through area of the filter body ( 20 ) of 256 mm×256 mm with a thickness of 4 mm, is at the most 2000 Pa.

12. The filter element ( 30 ) of claim 1 , wherein the polysulfide particles ( 10 ) have an average size of 50 to 500 μm.

13. The filter element ( 30 ) of claim 1 , wherein the filter body ( 20 ) comprises, in addition to the polysulfide particles ( 10 ), particles that are not polysulfide particles.

14. The filter element ( 30 ) of claim 1 , wherein the filter element ( 30 ), on an inflow side ( 22 ) thereof, is provided with a coating ( 24 ) constructed with additional particles ( 28 ), said coating ( 24 ) having a smaller pore size than the filter body ( 20 ).

15. The filter element ( 30 ) of claim 1 , wherein the filter body ( 20 ) in a tensile test reveals a tensile strength of at least 1 N/mm 2 .

16. The filter element ( 30 ) of claim 1 , wherein the filter body ( 20 ) in a tensile test has an elongation at break of at least 0.2 mm.

17. The filter element ( 30 ) of claim 1 , wherein the filter element is a lamellar filter element.

18. The filter element ( 30 ) of claim 17 , further comprising a filter head ( 36 ) and a filter foot ( 34 ), which are constructed with the same material as the filter body ( 10 ).

19. The filter element ( 30 ) of claim 1 , which is capable of withstanding a temperature in the range from 50 to 200° C.

20. A method of manufacturing a filter element ( 30 ) having inherent stability and being porous to permit flow therethrough, said method comprising steps of:

Providing filter body particles comprising polysulfide particles ( 10 ), at least part of said polysulfide particles tempered at a temperature of 255° C. to 275° C. over a period of time from 7 to 24 hours, and sintering the filter body particles to form a porous sintered filter body ( 20 ) of the filter element ( 30 ).

21. The method of claim 20 , wherein the polysulfide particles are polyphenylene sulfide particles.

22. The method of claim 20 , wherein the sintering takes place at ambient pressure.

23. The method of claim 20 , wherein the sintering takes place at a temperature of 290° C. to 350° C.

24. The method of claim 23 , wherein the sintering takes place over a period of time from 5 min to 180 min.

25. The method of claim 20 , wherein at least two polysulfides of different configuration are used for providing the filter body particles.

26. The method of claim 25 , wherein the provided filter body particles comprise tempered polysulfide and untempered polysulfide particles.

27. The filter element ( 30 ) of claim 16 , wherein the tensile test is performed according to DIN EN ISO 527-2 (2012-06) at a test speed of 80 mm/min.