Polyester resins with particular carbon black as a reheat additive in the production of stretch blow molded bottles and containers
Provided is a polyester or co-polyester resin used in the manufacture of preforms suitable for making bottles and containers containing a carbon black, particularly lamp black carbon black, with a primary particle size in a range of from 100 to 160 nanometers.
1. A method of improving the reheat and color value L* of a preform and forming a clear bottle, the method comprising:
mixing a lamp black carbon black with a first co-polyester resin in molten form to form a lamp black carbon black composition,
mixing the lamp black carbon black composition and a second co-polyester resin to form a molding composition, wherein the second co-polyester resin does not contain a reheat additive, a colorant or a pigment other than the lamp black carbon black,
injection molding the molding composition into a mold to form the preform, wherein the preform has a CIE L* of at least 70 and a haze of no more than 7%,
heating the preform with infra-red heat, then
stretch-blow molding the infra-red heated preform to form the clear bottle,
wherein the lamp black carbon black has an average primary particle size of from 106 to 130 nm,
wherein the lamp black carbon black is present in the clear bottle at a concentration of from 3 ppm to 11 ppm by weight of the first and second resin compositions,
wherein the temperature of the heated preform during the injection molding is at least 8° C. higher than the temperature of an equivalently heated preform in the absence of the lamp black carbon black, and
wherein the first and second co-polyester resins comprise 70-95 mol % of reacted units of terephthalic acid and 5-30 mol % of reacted units of isophthalic acid, wherein mol % is based on the total number of mols of dicarboxylic acid units in the second co-polyester resin, and reacted units of polyethylene glycol.
2. The method of claim 1 , wherein the temperature of the heated preform is at least 110° C. during the stretch-blow molding.
3. The method of claim 1 , wherein the first copolyester resin and the second co-polyester resin do not comprise residues of an antimony catalyst.
4. The method of claim 1 , wherein the injection molding forms a preform having a haze of no more than 6.75%.
5. The method of claim 1 , wherein the injection molding forms a preform having an L* value of from 70 to 80.
6. The method of claim 1 , wherein the injection molding forms a preform having an L* value of greater than 75.
7. The method of claim 1 , wherein the average primary particle size of the lamp black carbon black is about 110 nm.
8. The method of claim 7 , wherein the lamp black carbon black is present in the clear bottle at a concentration of from 4 ppm to 6 ppm.