Vanadium oxide supported catalyst for alkane dehydrogenation
A catalyst for non-oxidative dehydrogenation of alkanes and a method for making and using the same is disclosed. The catalyst can include vanadium oxide derived from vanadyl oxalate. More particularly the catalyst is prepared by a method comprising the steps of: (a) contacting a transition alumina support with an aqueous solution comprising a vanadium carboxylate material solubilized therein; (b) heating the contacted alumina support to remove the water and produce a catalyst precursor material in solid form; and (c) heating the solid catalyst precursor material in the presence of an oxidizing source at a temperature of 500 to 800° C. to produce an alumina supported catalytic material comprising vanadium oxide. The catalyst can be further modified with an alkali metal oxide like potassium oxide, the precursor thereof being introduced with the impregnation solution.
1. A method of preparing an alkane dehydrogenation catalyst, the method comprising:
(a) contacting a transition alumina support with an aqueous solution comprising a vanadium carboxylate material and an alkali metal oxide precursor comprising an alkali metal solubilized therein;
(b) heating the contacted alumina support to remove the water and produce a catalyst precursor material in solid form; and
(c) heating the solid catalyst precursor material in the presence of an oxidizing source at a temperature of 500 to 800° C. to produce an alumina supported catalytic material comprising vanadium oxide;
wherein the catalyst has a surface area of 60 to 160 m 2 /g.
2. The method of claim 1 , wherein the vanadium carboxylate material is vanadium monocarboxylate, vanadium dicarboxylate, vanadium tricarboxylate, or any combination thereof.
3. The method of claim 2 , wherein the vanadium carboxylate is vanadium dicarboxylate.
4. The method of claim 1 , wherein step (b) heating comprises a temperature of 70 to 90° C.
5. The method of claim 1 , wherein the vanadium carboxylate is vanadyl oxalate.
6. The method of claim 1 , wherein the catalytic material comprises 2 to 20 wt. % of vanadium oxide.
7. The method of claim 1 , wherein the step (c) heating is sufficient to convert the alkali metal oxide precursor to an alkali metal oxide.
8. The method of claim 7 , wherein the catalytic material consists of 2 to 13 wt. % of vanadium oxide and 0.1 to 1 wt. % K 2 O with balance being transition alumina.
9. The method of claim 1 , wherein the catalytic material comprises 0.1 to 2 wt. % of the alkali metal oxide.
10. The method of claim 1 , wherein the alkali metal is potassium.
11. The method of claim 1 , further comprising the step of drying a moisture-containing transition alumina support to produce the transition alumina support.
12. A catalyst for non-oxidative dehydrogenation of alkanes, the catalyst comprising vanadium oxide derived from vanadyl oxalate and an alkali metal dopant, wherein the catalyst has a surface area of 60 to 160 m 2 /g.
13. The catalyst of claim 12 , wherein the dopant is potassium oxide.
14. The catalyst of claim 12 , wherein the catalyst consists of vanadium oxide, potassium oxide, and transition alumina.
15. The catalyst of claim 14 , wherein the catalyst consists of 2 to 20 wt. % vanadium oxide, 0.1 to 2 wt. % K 2 O, and 78 to 97.9 wt. % transition alumina.
16. The catalyst of claim 12 , wherein the catalyst further comprises a support.
17. A process for production of alkanes, the process comprising contacting the catalyst of claim 12 with a feed source comprising an alkane at a temperature of 400° C. to 800° C. to produce a product stream comprising an alkene, wherein the alkane is isobutane and the alkene is isobutene.
18. The process of claim 17 , wherein the contacting is done in the absence of oxygen and/or halogenated alkanes.
19. The process of claim 17 , further comprising:
(i) heating the catalyst at 400 to 800° C. in the presence of an oxidizing source prior to contacting;
(ii) removing the oxidizing source; and
(iii) heating the catalyst at 400 to 800° C. in the presence of a reducing source.