Composition for 3 dimensional printing
The present invention relates to a composition for 3D printing, a 3D printing method using the same, and a three-dimensional comprising the same, and provides a composition for 3D printing capable of realizing a three-dimensional shape having precision and excellent curing stability.
1. A composition for 3D printing comprising a thermosetting compound, 2 to 28 parts by weight of a thermoplastic resin, relative to 100 parts by weight of said thermosetting compound, and magnetic particles,
wherein the magnetic particles have at least two magnetic domains, wherein the magnetic domains are irregularly arranged when an external magnetic field is absent, and are magnetized by an external alternate-current magnetic field,
wherein the magnetic domains have an average size in a range of 10 to 50 nm, and
wherein the thermosetting compound comprises at least one thermosetting functional group,
wherein the composition for 3D printing has a surface energy before curing in a range of 20 mN/m to 50 mN/m,
wherein the composition for 3D printing has a surface energy after curing in a range of 20 mN/m to 55 mN/m.
2. The composition for 3D printing according to claim 1 , wherein the magnetic particles have a coercive force in a range of 1 to 200 kOe.
3. The composition for 3D printing according to claim 1 , wherein the magnetic particles have a saturation magnetization value at 25° C. in a range of 20 to 150 emu/g.
4. The composition for 3D printing according to claim 1 , wherein the magnetic particles have an average particle size in a range of 20 to 300 nm.
5. The composition for 3D printing according to claim 1 , wherein the magnetic particles comprise metal oxide, ferrite or alloy particles.
6. The composition for 3D printing according to claim 1 , wherein the magnetic particles are comprised in an amount of 0.01 to 25 parts by weight, relative to 100 parts by weight of the thermosetting compound.
7. The composition for 3D printing according to claim 1 , wherein the magnetic particles are vibrated by magnetization reversal.
8. The composition for 3D printing according to claim 1 , wherein the thermoplastic resin comprises an acrylic resin, a silicone resin, a fluororesin, a styrene resin, a polyolefin resin, a thermoplastic elastomer, a polyoxyalkylene resin, a polyester resin, a polyvinyl chloride resin, a polycarbonate resin, a polyphenylene sulfide resin, polyurethane, a cellulose resin, a polyacetal resin, a melamine resin, a polyurethane resin or a polyamide resin.
9. The composition for 3D printing according to claim 1 , wherein the thermoplastic resin has a glass transition temperature before curing in a range of 40° C. to 150° C.
10. The composition for 3D printing according to claim 1 , further comprising a thermosetting agent.
11. A 3D printing method comprising a step of applying the composition for 3D printing of claim 1 to form a three-dimensional shape.
12. The 3D printing method according to claim 11 , further comprising a step of applying a magnetic field to the applied composition.
13. The 3D printing method according to claim 12 , wherein the step of applying a magnetic field applies a magnetic field with a current of 50 A to 500 A at a frequency of 100 kHz to 1 GHz for 20 seconds to 60 minutes.
14. The 3D printing method according to claim 12 , wherein the step of applying a magnetic field comprises at least two steps of multi-profile methods.
15. A three-dimensional shape comprising a cured product of the composition for 3D printing of claim 1 .