Low-dispersion single-mode optical fiber
A low-dispersion single-mode fiber includes a core and claddings covering the core. The core layer has a radius in a range of 3-5 μm and a relative refractive index difference in a range of 0.15% to 0.45%. The claddings comprise a first depressed cladding, a raised cladding, a second depressed cladding, and an outer cladding arranged sequentially from inside to outside. The first depressed cladding has a unilateral width in a range of 2-7 μm and a relative refractive index difference in a range of −0.4% to 0.03%. The raised cladding has a unilateral width in a range of 2-7 μm and a relative refractive index difference in a range of 0.05% to 0.20%. The second depressed cladding has a unilateral width in a range of 0-8 μm and a relative refractive index difference in a range of 0% to −0.2%. The outer cladding is formed of pure silicon dioxide glass.
1. A low-dispersion single-mode fiber, comprising:
core layer and claddings, wherein
the core layer has a radius R1 in a range from 3 μm to 3.98 μm and a relative refractive index difference Δ1 in a range from 0.15% to 0.45%, and
the claddings comprise a first depressed cladding, a raised cladding, a second depressed cladding, and an outer cladding from inside to outside, wherein
the first depressed cladding has a unilateral width (R2−R1) in a range from 2 μm to 7 μm and a relative refractive index difference Δ2 in a range from −0.4% to 0.03%;
the raised cladding has a unilateral width (R3−R2) in a range from 2 μm to 7 μm and a relative refractive index difference Δ3 in a range from 0.05% to 0.20%;
the second depressed cladding has a unilateral width (R4−R3) in a range from 0 μm to 8 μm and a relative refractive index difference Δ4 in a range from 0% to −0.2%; and
the outer cladding is a layer made of pure silicon dioxide glass,
wherein the core layer is a silicon dioxide glass layer co-doped with germanium Ge and fluorine F, and has a contribution amount of doped F, wherein ΔF1 is in a range from −0.2% to −0.02%.
2. The low-dispersion single-mode fiber according to claim 1 , wherein the radius of the core layer is in a range from 3.5 μm to 3.98 μm.
3. The low-dispersion single-mode fiber according to claim 1 , wherein the relative refractive index difference Δ1 of the core layer is in a range from 0.20% to 0.40%.
4. The low-dispersion single-mode fiber according to claim 1 , wherein the unilateral width of the first depressed cladding (R2−R1) is in a range from 2.5 μm to 5.5 μm.
5. The low-dispersion single-mode fiber according to claim 1 , wherein a difference value between the relative refractive index difference of the core layer and the relative refractive index difference of the first depressed cladding, wherein Δ1-Δ2 is in a range from 0.3% to 0.5%.
6. The low-dispersion single-mode fiber according to claim 1 , wherein a value of annular area integral for the relative refractive index difference of the first depressed cladding, wherein Δ2×(R2 2 −R1 2 ) is in a range from −15%·μm 2 to −2%·μm 2 .
7. The low-dispersion single-mode fiber according to claim 6 , wherein the first depressed cladding is a silicon dioxide glass layer co-doped with Ge and F, and has a contribution amount of doped F, wherein ΔF2 is in a range from −0.45% to −0.04%.
8. The low-dispersion single-mode fiber according to claim 1 , wherein a value of annular area integral for the relative refractive index difference of the raised cladding, wherein Δ3×(R3 2 −R2 2 ) is in a range from 4%·μm 2 to 21%·μm 2 .
9. The low-dispersion single-mode fiber according to claim 8 , wherein the raised cladding is a silicon dioxide glass layer doped with Ge or co-doped with Ge and F, and has a contribution amount of doped F, wherein ΔF3 is in a range from −0.20% to 0%.
10. The low-dispersion single-mode fiber according to claim 1 , wherein the fiber has an MFD at a wavelength of 1310 nm in a range from 8.5 μm to 9.5 μm.
11. The low-dispersion single-mode fiber according to claim 1 , wherein the fiber has a cable cutoff wavelength λ cc smaller than or equal to 1260 nm.
12. The low-dispersion single-mode fiber according to claim 1 , wherein the fiber has attenuation smaller than or equal to 0.45 dB at a waveband ranging from 1270 nm to 1380 nm.
13. The low-dispersion single-mode fiber according to claim 1 , wherein the fiber has dispersion in a range from −12 ps/nm/km to 5 ps/nm/km at a waveband ranging from 1270 nm to 1380 nm.
14. The low-dispersion single-mode fiber according to claim 1 , wherein the fiber has dispersion in a range from −3.5 ps/nm/km to 3.5 ps/nm/km at a waveband ranging from 1340 nm to 1380 nm.
15. The low-dispersion single-mode fiber according to claim 1 , wherein the fiber has a dispersion slope smaller than or equal to 0.08 ps/nm 2 ·km at a waveband ranging from 1270 nm to 1380 nm.
16. The low-dispersion single-mode fiber according to claim 1 , wherein the fiber has a zero dispersion wavelength in a range from 1300 nm to 1400 nm.
17. Use of the fiber according to claim 1 as a low-dispersion single-mode fiber in a communication system, wherein the fiber is used for a WDM transmission system at a waveband ranging from 1270 nm to 1380 nm.
18. A low-dispersion single-mode fiber, comprising:
core layer and claddings, wherein
the core layer has a radius R1 in a range from 3 μm to 5 μm and a relative refractive index difference Δ1 in a range from 0.15% to 0.45%, and
the claddings comprise a first depressed cladding, a raised cladding, a second depressed cladding, and an outer cladding from inside to outside, wherein
the first depressed cladding has a unilateral width (R2−R1) in a range from 2 μm to 7 μm and a relative refractive index difference Δ2 in a range from −0.4% to 0.03%;
the raised cladding has a unilateral width (R3−R2) in a range from 2 μm to 7 μm and a relative refractive index difference Δ3 in a range from 0.05% to 0.20%;
the second depressed cladding has a unilateral width (R4−R3) in a range from 0 μm to 8 μm and a relative refractive index difference Δ4 in a range from 0% to −0.2%; and
the outer cladding is a layer made of pure silicon dioxide glass,
wherein the core layer is a silicon dioxide glass layer co-doped with germanium Ge and fluorine F, and has a contribution amount of doped F, wherein ΔF1 is in a range from −0.2% to −0.02%.