Superabsorbent polymer and preparation method thereof
Provided is a method of preparing a superabsorbent polymer. More particularly, provided is a method of preparing a superabsorbent polymer, the method capable of preparing the superabsorbent polymer maintaining excellent basic absorption performances such as centrifugal retention capacity, absorbency under load, etc. while also exhibiting an improved absorption rate.
1. A method of preparing a superabsorbent polymer, the method comprising:
a) mixing a water-soluble ethylenically unsaturated monomer, an internal crosslinking agent, and a polymerization initiator to prepare a monomer composition;
b) polymerizing the monomer composition to prepare a water-containing gel polymer;
c) chopping the water-containing gel polymer;
d) adding one or more fibers of a fluff pulp and a synthetic polymeric fiber to the chopped water-containing gel polymer and mixing them with each other to prepare a mixture;
e) chopping the mixture;
f) drying the mixture; and
g) pulverizing the mixture,
wherein the fiber has a length of 1 mm to 20 mm.
2. The method of preparing a superabsorbent polymer of claim 1 , wherein the fiber is included in an amount of 1 part by weight to 18 parts by weight with respect to 100 parts by weight of the water-containing gel polymer.
3. The method of preparing a superabsorbent polymer of claim 1 , wherein the fiber has a width of 1 μm to 100 μm.
4. The method of preparing a superabsorbent polymer of claim 1 , wherein water is further added in one or more of c) to e).
5. The method of preparing a superabsorbent polymer of claim 4 , wherein the water is added in an amount of 1 part by weight to 20 parts by weight with respect to 100 parts by weight of the water-containing gel polymer.
6. The method of preparing a superabsorbent polymer of claim 1 , wherein the monomer composition further includes a foaming agent.
7. The method of preparing a superabsorbent polymer of claim 6 , wherein the monomer composition further includes one or more foam stabilizers selected from the group consisting of alkyl sulfate salts, alkyl sulfonate salts, alkyl phosphate salts, alkyl carbonate salts, polyethylene glycol alkyl ester, polypropylene glycol alkyl ester, glucoside alkyl ester, glycerol alkyl ester, and block-copolymers of polyethylene glycol and polypropylene glycol.
8. The method of preparing a superabsorbent polymer of claim 1 , further comprising, after g),
h) adding a surface crosslinking agent to the mixture obtained in g); and
i) performing a surface crosslinking reaction.
9. The method of preparing a superabsorbent polymer of claim 8 , wherein the surface crosslinking agent is one or more selected from the group consisting of a polyhydric alcohol compound; an epoxy compound; a polyamine compound; a haloepoxy compound; a condensation product of a haloepoxy compound; an oxazoline compound; a mono-, di-, or polyoxazolidinone compound; a cyclic urea compound; a polyvalent metal salt; and an alkylene carbonate compound.
10. The method of preparing a superabsorbent polymer of claim 8 , wherein the surface crosslinking agent is added in an amount of 0.001 part by weight to 5 parts by weight with respect to 100 parts by weight of the mixture.