Exterior coating composition
A coating composition is provided for inhibiting growth of fungus and/or algae on a surface. The coating composition includes a dry film preservative and an antibacterial dry-film preservative comprising an immobilized isothiazolin-3-one derivative/zinc oxide complex. The amount of the antibacterial preservative comprising immobilized 1,2-isothiazolin-3-one derivative/zinc oxide complex and the dry film preservative contained in the coating composition is sufficient to inhibit or prevent the defacement of a surface exposed to the environment, when such defacement is due to growth of fungi or algae, or a combination of fungi and algae on a surface coated with said surface coating composition.
1. A dry-film preservative composition useful against fungus and/or algae, the composition comprising:
a) at least one bactericide comprising an immobilized isothiazolin-3-one derivative/zinc oxide complex;
b) at least one dry film preservative useful against fungus, or useful against algae, or useful against fungus and algae,
wherein the weight ratio of a):b) is from 1:25 to 25:1, limits inclusive.
2. The composition according to claim 1 , wherein the immobilized isothiazolin-3-one derivative/zinc oxide complex is selected from the group consisting of immobilized 1,2-benzisothiazolin-3(2H)-one (BIT)/zinc oxide complex; immobilized N-(n-butyl)-1,2-benzisothiazolin-3-one (BB1T)/zinc oxide complex; immobilized 2-methyl-4-isothiazolin-3-one (MIT)/zinc oxide complex; immobilized 5-chloro-2-methyl-4-isothiazolin-3-one (CMIT)/zinc oxide complex; immobilized 2-octyl-2H-isothiazol-3-one (OIT)/zinc oxide complex; immobilized 4,5-dichloro-2-octyl-4-isothiazolin-3-one (DCOIT)/zinc oxide complex; and mixtures thereof.
3. The composition according to claim 1 wherein the dry film preservative b) is selected from the group consisting of: 3-iodoprop-2-yn-1-yl butylcarbamate (IPBC); methylbenzimidazole-2-yl carbamate (BCM); 3-(3,4-dichlorphenyl)-1,1-dimethylurea (Diuron); 2-tert-butylamino-4-ethylamino-6-methylthio-1,3,5-triazin (Terbutryn); 3-(4-isopropylphenyl)-1,1-dimethylurea (Isoproturon); zinc pyrithione (ZPT); 2-(tert-butylamino)-4-(cyclopropylamino)-6-(methylthio)-s-triazine (Irgarol); N-tert-butyl-6-chloro-N′-ethyl-1,3,5-triazine-2,4-diamine (Terbuthylazine); and mixtures thereof.
4. The composition according to claim 2 wherein the dry film preservative b) is selected from the group consisting of 3-iodoprop-2-yn-1-yl butylcarbamate (IPBC); methylbenzimidazole-2-yl carbamate (BCM); 3-(3,4-dichlorphenyl)-1,1-dimethylurea (Diuron); 2-tert-butylamino-4-ethylamino-6-methylthio-1,3,5-triazin (Terbutryn); 3-(4-isopropylphenyl)-1,1-dimethylurea (Isoproturon); zinc pyrithione (ZPT); 2-octyl-2H-isothiazol-3-one (OIT); 4,5-dichloro-2-octyl-4-isothiazolin-3-one (DCOIT); 2-(tert-butylamino)-4-(cyclopropylamino)-6-(methylthio)-s-triazine (Irgarol); N-tert-butyl-6-chloro-N′-ethyl-1,3,5-triazine-2,4-diamine (Terbuthylazine); and mixtures thereof.
5. The composition according to claim 1 , wherein the immobilized isothiazolin-3-one derivative/zinc oxide complex is 1,2-benzisothiazolin-3(2H)-one (BIT)/zinc oxide complex.
6. The composition according to claim 2 , wherein the immobilized isothiazolin-3-one derivative/zinc oxide complex is immobilized 1,2-benzisothiazolin-3(2H)-one (BIT)/zinc oxide complex.
7. The composition according to claim 5 , wherein the immobilized isothiazolin-3-one derivative/zinc oxide complex is immobilized 1,2-benzisothiazolin-3-one (BIT)/zinc oxide complex.
8. The composition according to claim 7 , wherein the dry film preservative b) is selected from the group consisting of: 3-(3,4-dichlorphenyl)-1,1-dimethylurea (Diuron); 2-tert-Butylamino-4-ethylamino-6-methylthio-1,3,5-triazin (Terbutryn); 3-(4-isopropylphenyl)-1,1-dimethylurea (Isoproturon); 2-(tert-Butylamino)-4-(cyclopropylamino)-6-(methylthio)-s-triazine (Irgarol); N-tert-butyl-6-chloro-N′-ethyl-1,3,5-triazine-2,4-diamine (Terbuthylazine); and mixtures thereof.
9. The composition according to claim 8 , wherein b) is 3-(3,4-dichlorphenyl)-1,1-dimethylurea (Diuron).
10. The composition according to claim 1 , wherein the weight ratio of a):b) is from 1:4 to 4:1, limits inclusive.
11. A coating composition comprising the composition according to claim 1 and a carrier,
wherein the immobilized 1,2-benzisothiazolin-3(2H)-one/zinc oxide complex has a total mass of 0.001% to 10% weight percent of the coating composition.
12. A method of protecting a substrate from defacement when exposed to an environment, wherein the method comprises the steps of:
i) treating the substrate with the coating composition according to claim 11 ;
ii) allowing the coating composition to harden, forming a dry film.
13. The method according to claim 12 , wherein the environment comprises a microbial infestation.
14. The method according to claim 13 , wherein the microbial infestation is selected from the group consisting of fungal growth, algal growth, bacterial growth, and combinations thereof.
15. The method according to claim 12 wherein the coating composition is selected from the group consisting of paint, leather treatment, roof coating, mastic, adhesive, spackling compound, or stain.
16. The method according to claim 12 wherein the substrate is selected from the group consisting of wood, fresh sawn timber, stucco, concrete, wall board, leather, ceramic, stone, brick, plastic, leather, paper, metal, flexible PVC, pool liners, and fabric.
17. The method according to claim 12 wherein the substrate is an exterior surface.
18. The method according to claim 17 wherein the exterior surface is horizontal.
19. The coating composition according to claim 11 , wherein the immobilized 1,2-benzisothiazolin-3(2H)-one/zinc oxide complex has a total mass of 0.005% to 5% weight percent of the coating composition.