Solid electrolyte material and battery

1. A solid electrolyte material comprising:

Li, M, and X, wherein:

M contains Y and further contains at least one selected from the group consisting of Mg, Ca, Sr, Ba, Zn, Zr, Nb, Ta, and Sm;

X is at least one selected from the group consisting of Cl, Br, and I;

a first converted pattern includes a base peak within a range in which q is 2.109 Å −1 or more and 2.315 Å −1 or less, wherein the first converted pattern is obtained by converting an X-ray diffraction pattern of the solid electrolyte material to change a horizontal axis of the X-ray diffraction pattern from a diffraction angle 2θ to q, where q=4π sin θ/λ, where λ is a wavelength of X-rays

a second converted pattern includes a peak within each of a range in which q/q 0 is 1.28 or more and 1.30 or less and a range in which q/q 0 is 1.51 or more and 1.54 or less, wherein the second converted pattern is obtained by converting the X-ray diffraction pattern to change the horizontal axis of the X-ray diffraction pattern from the diffraction angle 2θ to q/q 0 , where q 0 is a value of q corresponding to the base peak in the first converted pattern; and

the solid electrolyte material satisfies at least one selected from the group consisting of the following: I 2 /I 4 ≤20% and I 3 /I 4 ≤30%,

where I 2 is an intensity of a second peak, which is a strongest peak within a second range of the second converted pattern, in the second range q/q 0 being 0.511 or more and 0.531 or less,

I 3 is an intensity of a third peak, which is a strongest peak within a third range of the second converted pattern, in the third range q/q 0 being 0.565 or more and 0.585 or less, and

I 4 is an intensity of a peak in the second converted pattern at a point at which q/q 0 is 1.

2. The solid electrolyte material according to claim 1 , wherein

the solid electrolyte material satisfies at least one selected from the group consisting of the following: Δθ 1 /θ p1 >0.5%, Δθ 2 /θ p2 >0.5%, and Δθ 3 /θ p3 >0.5%,

where 2θ p1 is a diffraction angle at which a first peak, which is a strongest peak within a first range of the second converted pattern, in the first range q/q 0 being 0.503 or more and 0.514 or less, has an apex,

Δ2θ 1 is a half-width of the first peak,

2θ p2 is a diffraction angle at which the second peak has an apex,

Δ2θ 2 is a half-width of the second peak,

2θ p3 is a diffraction angle at which the third peak has an apex, and

Δ2θ 3 is a half-width of the third peak.

3. The solid electrolyte material according to claim 1 , wherein

X contains Cl.

4. The solid electrolyte material according to claim 1 , wherein:

the solid electrolyte material has a crystal structure of a Li 3 YbCl 6 system, which belongs to a space group Pnma;

M occupies equivalent positions in the crystal structure; and

an M occupancy of each of the equivalent positions is 10% or more.

5. A battery comprising:

a positive electrode;

a negative electrode; and

an electrolyte layer between the positive electrode and the negative electrode, wherein

at least one selected from the group consisting of the positive electrode, the negative electrode, and the electrolyte layer contains a solid electrolyte material according to claim 1 .

6. A solid electrolyte material comprising:

Li, M, and X, wherein:

M contains Y and further contains at least one selected from the group consisting of Mg, Ca, Sr, Ba, Zn, Zr, Nb, Ta, and Sm;

X is at least one selected from the group consisting of Cl, Br, and I;

a first converted pattern includes a base peak within a range in which q is 2.109 Å −1 or more and 2.315 Å −1 or less, wherein the first converted pattern is obtained by converting an X-ray diffraction pattern of the solid electrolyte material to change a horizontal axis of the X-ray diffraction pattern from a diffraction angle 2θ to q, where q=4π sin θ/λ, where λ is a wavelength of X-rays;

a second converted pattern includes a peak within each of a range in which q/q 0 is 1.28 or more and 1.30 or less and a range in which q/q 0 is 1.51 or more and 1.54 or less, wherein the second converted pattern is obtained by converting the X-ray diffraction pattern to change the horizontal axis of the X-ray diffraction pattern from the diffraction angle 2θ to q/q 0 , where q 0 is a value of q corresponding to the base peak in the first converted pattern; and

the solid electrolyte material satisfies at least one selected from the group consisting of the following: I 2 /I 1 ≤100% and I 2 /I 4 ≤30%,

where I 1 is an intensity of a first peak, which is a strongest peak within a first range of the second converted pattern, in the first range q/q 0 being 0.503 or more and 0.514 or less,

I 2 is an intensity of a second peak, which is a strongest peak within a second range of the second converted pattern, in the second range q/q 0 being 0.550 or more and 0.565 or less, and

I 4 is an intensity of a peak in the second converted pattern at a point at which q/q 0 is 1.

7. The solid electrolyte material according to claim 6 , wherein

X contains Cl.

8. The solid electrolyte material according to claim 6 , wherein:

the solid electrolyte material has a crystal structure of a Li 3 ErCl 6 system, which belongs to a space group P-3m1;

M occupies three or more equivalent positions in the crystal structure; and

an M occupancy of each of the three or more equivalent positions is 10% or more.

9. A battery comprising:

a positive electrode;

a negative electrode; and

an electrolyte layer between the positive electrode and the negative electrode, wherein

at least one selected from the group consisting of the positive electrode, the negative electrode, and the electrolyte layer contains a solid electrolyte material according to claim 6 .

10. A solid electrolyte material comprising:

Li, M, and X, wherein:

M contains Y and further contains at least one selected from the group consisting of Mg, Ca, Sr, Ba, Zn, Zr, Nb, Ta, and Sm;

X is at least one selected from the group consisting of Cl, Br, and I;

a first converted pattern includes a base peak within a range in which q is 1.76 Å −1 or more and 2.18 Å −1 or less, wherein the first converted pattern is obtained by converting an X-ray diffraction pattern of the solid electrolyte material to change a horizontal axis of the X-ray diffraction pattern from a diffraction angle 2θ to q, where q=4π sin θ/λ, where λ is a wavelength of X-rays, and, of the two peaks, the peak at a smaller q is a base peak;

a second converted pattern includes a peak within each of a range in which q/q 0 ′ is 1.14 or more and 1.17 or less and a range in which q/q 0 ′ is 1.625 or more and 1.645 or less, wherein the second converted pattern is obtained by converting the X-ray diffraction pattern to change the horizontal axis of the X-ray diffraction pattern from the diffraction angle 2θ to q/q 0 ′, where q 0 ′ is a q corresponding to the base peak in the first converted pattern; and

the solid electrolyte material satisfies at least one selected from the group consisting of the following: I 1 /I 6 ≤15%, I 2 /I 6 ≤5%, I 3 /I 6 ≤10%, and I 4 /I 6 ≤5%,

where I 1 is an intensity of a first peak, which is a strongest peak within a first range of the second converted pattern, in the first range q/q 0 ′ being 0.494 or more and 0.511 or less,

I 2 is an intensity of a second peak, which is a strongest peak within a second range of the second converted pattern, in the second range q/q 0 ′ being 0.538 or more and 0.550 or less,

I 3 is an intensity of a third peak, which is a strongest peak within a third range of the second converted pattern, in the third range q/q 0 ′ being 0.559 or more and 0.575 or less,

I 4 is an intensity of a fourth peak, which is a strongest peak within a fourth range of the second converted pattern, in thr fourth range q/q 0 ′ being 0.632 or more and 0.644 or less, and

I 6 is an intensity of a sixth peak, which is a strongest peak within a sixth range of the second converted pattern, in the sixth range q/q 0 ′ being 1.140 or more and 1.170 or less.

11. The solid electrolyte material according to claim 10 , wherein

the solid electrolyte material satisfies at least one selected from the group consisting of the following: I 1 /I 5 ≤20%, I 2 /I 5 ≤10%, I 3 /I 5 ≤20%, and I 4 /I 5 ≤10%,

where I 5 is an intensity of a peak in the second converted pattern at a point at which q/q 0 ′ is 1.

12. The solid electrolyte material claim 10 , wherein

the solid electrolyte material satisfies at least one selected from the group consisting of the following: Δθ 1 /θ p1 >1%, Δθ 2 /θ p2 >1%, Δθ 3 /θ p3 >1%,and Δθ 4 /θ p4 >1%,

where 2θ p1 is a diffraction angle at which a first peak has an apex,

Δ2θ 1 is a half-width of the first peak,

2θ p2 is a diffraction angle at which the second peak has an apex,

Δ2θ 2 is a half-width of the second peak,

2θ p3 is a diffraction angle at which the third peak has an apex,

Δ2θ 3 is a half-width of the third peak

2θ p4 is a diffraction angle at which the fourth peak has an apex, and

Δ2θ 4 is a half-width of the fourth peak.

13. The solid electrolyte material according to claim 10 , wherein

X contains Br.

14. The solid electrolyte material according to claim 10 , wherein:

the solid electrolyte material has a crystal structure of a Li 3 ErBr 6 system, which belongs to a space group C2/m;

M occupies equivalent positions in the crystal structure; and

an M occupancy of each of the equivalent positions is 10% or more.

15. A battery comprising:

a positive electrode;

a negative electrode; and

an electrolyte layer between the positive electrode and the negative electrode, wherein

at least one selected from the group consisting of the positive electrode, the negative electrode, and the electrolyte layer contains a solid electrolyte material according to claim 10 .