Alumina hydrate particles, flame retardant, resin composition and electric wire/cable
The present invention provides alumina hydrate particles, a flame retardant and a resin composition that are each for an electric wire/cable covering material improvable in flame retardancy and mechanical properties while the covering material keeps acid resistance; such an electric wire/cable; and producing methods thereof. The alumina hydrate particles of the present invention for electric wire/cable covering material have an average particle size of 0.5 to 2.5 μm, and having a primary particle variation R of 24% or less, the variation R being represented by the following expression: primary particle variation R (%)=“standard deviationσ(μm) of major axis diameters of the primary particles”/“average value(μm) of the major axis diameters of the primary particles”×100.
1. Alumina hydrate particles for electric wire/cable covering material, having an average particle size of 0.5 to 2.5 μm, having a BET specific surface area of 2.5 to 10 m 2 /g, and having a primary particle variation R of 24% or less, the variation R being represented by the following expression: primary particle variation R (%)=“standard deviation σ(μm) of major axis diameters of the primary particles”/“average value (μm) of the major axis diameters of the primary particles”×100.
2. The alumina hydrate particles according to claim 1 , comprising boehmite, which is an alumina monohydrate.
3. The alumina hydrate particles according to claim 1 which are treated with at least one surface treating agent selected from the group consisting of higher aliphatic acids, higher aliphatic acid alkaline earth metal salts, coupling agents, esters each made from an aliphatic acid and a polyhydric alcohol, and phosphates each made from phosphoric acid and a higher alcohol.
4. A flame retardant for electric wire/cable covering material that comprises alumina hydrate particles surface-treated with a surface treating agent,
wherein the surface-treated alumina hydrate particles have an average particle size of 0.5 to 2.5 μm, have a BET specific surface area of 2.5 to 10 m 2 /g, and have a primary particle variation R of 24% or less, the variation R being represented by the following expression:
primary particle variation R (%)=“standard deviation σ(μm) of major axis diameters of the primary particles”/“average value (μm) of the major axis diameters of the primary particles”×100.
5. The flame retardant according to claim 4 , wherein the alumina hydrate comprises boehmite, which is an alumina monohydrate.
6. A resin composition for electric wire/cable covering material, comprising a polyolefin resin, and the flame retardant recited in claim 4 in an amount of 5 to 500 parts by mass for 100 parts by mass of the polyolefin resin.
7. An electric wire/cable, comprising a covering material formed using the resin composition recited in claim 6 .