(Per)fluoropolyether polymers

Inventors: Cristiano Monzani (Trezzo sull'Adda, IT); Marco Galimberti (Bollate, IT); Vito Tortelli (Milan, IT)

Assignee: SOLVAY SPECIALITY POLYMERS ITALY S.P.A.

C10M107/38 C08G65/007 C08G65/3317 C10M2213/0606 C10N2040/18

View Patent ↗

Loading inventors, assignments & file history…

Monitor This Case

Get email alerts when status or documents change.

Order Certified Copies

Most orders are placed with the USPTO same day — all within 24 business hours.

Order via The Patent Place →

Pre-filled with this patent's details

Quick Facts

Patent No.: US 11,591,536
App. No.: 17/251,524
Granted: Feb 28, 2023
Kind: B2

External Links

USPTO Patent Center↗ Full Patent PDF↗

Abstract

The present invention relates to a novel process for the synthesis of (per)fluoropolyether polymers, to certain novel (per)fluoropolyether polymers. The present invention also relates to the use of the (per)fluoropolyether polymers thus obtained as intermediate compounds for the manufacture of further polymers suitable for use as lubricants, notably for magnetic recording media (MRM).

Claims (136)

1. A method (method (M FH )) for the synthesis of a mixture of polymers comprising a partially fluorinated polyether backbone possessing a plurality of recurring units including at least one cyclic group and having two chain ends, wherein said chain ends comprise at least one group selected from hydroxy group, allyl group and vinyl group, said method comprising the step of:

Step (1): a step of reacting:

(1a) at least one fluorinated compound (compound (F)) comprising at least two unsaturated groups selected from vinyl groups and allyl groups, and

(1b) at least one fully or partially hydrogenated compound (compound (H)) comprising at least two hydroxy groups,

to provide a mixture (FH),

wherein:

(i) at least one compound (F) is a compound (F c ) of formula:

CF 2 ═CF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CF═CF 2

wherein:

R cf is a divalent fluorocarbon cyclic group, which may be a cycloaliphatic or a cycloaromatic group, which may comprise one or more than one cyclic moiety, and which may comprise one or more than one heteroatom included in the cycle, said heteroatom being selected from N, O and S;

each of E f , equal to or different from each other, is a bond, or a divalent fluorocarbon group, possibly comprising one or more than one heteroatoms selected from Cl, N, O and S;

each or R f 1 and R f 2 , equal to or different from each other, is F or a C 1 -C 6 perfluorocarbon group;

a and b being independently zero or 1; and

(ii) at least one compound (H) is a compound (H C ) of formula:

HO—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -(CR H 1 R H 2 ) h2 -OH

wherein:

each of E HC is selected from a bond, a —O— group and a divalent linear or branched (oxy)alkylene group, wherein said (oxy)alkylene group comprises from 1 to 8 carbon atoms and is optionally interrupted by one or more than one ethereal oxygen atom;

R HC is divalent hydrocarbon cyclic group, which may be a cycloaliphatic or a cycloaromatic group, which may comprise one or more than one cyclic moiety, and which may comprise one or more than one heteroatom included in the cycle, said heteroatom being selected from N, O and S;

h1 and h2 being independently zero or 1;

each of R H 1 and R H 2 , equal to or different from each other at each occurrence, is independently H or a C 1 -C 6 hydrocarbon group.

2. The method of claim 1 , wherein mixture (FH) is a mixture of polymers comprising a partially fluorinated polyether backbone possessing a plurality of recurring units including at least one cyclic group and having two chain ends, wherein each of said chain ends comprises a group selected from hydroxy group, allyl group or vinyl group; and

said backbone comprises recurring units selected from the group consisting of units (R FcH ) and units (R FHc ):

unit (R FcH ): —O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E cf -R cf -E cf -O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -J H -(CR H 1 R H 2 ) h2 -O—;

unit (R FHc ):

—O—CF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -(CR H 1 R H 2 ) h2 -O—;

wherein:

R f is either a divalent, linear or branched, fluoro(hydro)carbon chain, wherein said fluoro(hydro)carbon chain comprises from 1 to 10 carbon atoms and is optionally interrupted by one or more oxygen atoms; or is a group of formula: -E f -R cf -E f -, with E f , and R cf having the meaning defined in claim 1 for compound (F C );

R f 1 , R f 2 , a and b have the same meanings defined in claim 1 for compound (F C )

J H is either selected from a bond, a —O— group and a divalent linear or branched (oxy)alkylene group, wherein said (oxy)alkylene group comprises from 1 to 8 carbon atoms and is optionally interrupted by one or more than one ethereal oxygen atom; or is a group -E HC -R HC -E HC -; and

h1, h2, E HC , R HC , R H 1 and R H 2 have the same meanings defined in claim 1 for compound (H C ).

3. The method of claim 2 , wherein at least one compound (H) is a compound (H C ), and is reacted with compounds (F) different from compound (F C ).

4. The method of claim 3 , wherein polymers of mixture (FH) have a backbone which comprises units (R FHc ).

5. The method according to claim 1 , wherein said method (M FH ) comprises a Step (3) of contacting mixture (FH) with a source of molecular fluorine to effect fluorination of polymers of mixture (FH).

6. The method according to claim 5 , said method (M FH ) further including an additional Step (2), after Step (1) and before Step (3), in which end groups of hydroxyl-type are protected, and wherein Step (2) is a step of converting hydroxyl groups of formula: HO—(CR H 1 R H 2 ) h1 - and/or —(CR H 1 R H 2 ) h2 -OH into corresponding fluoroformate groups of formula F—C(O)—O—(CR H 1 R H 2 ) h1 - and/or formula —(CR H 1 R H 2 ) h2 -O—C(O)—F.

7. The method of claim 6 , said method (M FH ) further comprising a Step (4), after Step (3), wherein said Step (4) comprises reacting polymers having one or more than one fluoroformate group to provide corresponding polymers having one or more than one carboxylic acid groups of formula —COOH and/or ester group of formula —C(═O)O—R alk wherein R alk is a linear or branched alkyl chain comprising from 1 to 10 carbon atoms.

8. The method of claim 7 , wherein in Step (4) mixture (FF −OC(O)F ) including polymers having one or more than one fluoroformate group is submitted to hydrolysis conditions in the presence of water, wherein polymers possessing fluoroformate end groups are advantageously decomposed through decarboxylation and dehydrofluorination, and are transformed into corresponding carboxylic acid-derivatives.

9. A mixture (mixture (FH)) of polymers comprising a partially fluorinated polyether backbone possessing a plurality of recurring units including at least one cyclic group and having two chain ends, wherein each of said chain ends comprises a group selected from hydroxy group, allyl group or vinyl group; and

said backbone comprises recurring units selected from the group consisting of units (R FcH ) and units (R FHc ):

unit (R FcH ): —O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E cf -R cf -E cf -O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -J H -(CR H 1 R H 2 ) h2 -O—;

unit (R FHc ):

—O—CF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 )—CFHCF 2 —O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -(CR H 1 R H 2 ) h2 -O—;

wherein:

each of E f , equal to or different from each other, is a bond, or a divalent fluorocarbon group, possibly comprising one or more than one heteroatoms selected from Cl, N, O and S;

each or R f 1 and R f 2 , equal to or different from each other, is F or a C 1 -C 6 perfluorocarbon group;

a and b being independently zero or 1;

h1 and h2 being independently zero or 1;

each of R H 1 and R H 2 , equal to or different from each other at each occurrence, is independently H or a C 1 -C 6 hydrocarbon group.

10. The mixture (FH) of claim 9 , wherein polymers of mixture (FH) have a backbone which comprises units (R FHc ).

11. The mixture (FH) of claim 9 , which is a mixture of polymers of any of formulae below:

polymer(R FcH bis-OH ): HO—(CR H 1 R H 2 ) h1 -J H -{(CR H 1 R H 2 ) h2 —O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -J H -} nFH -(CR H 1 R H 2 ) h2 -OH

polymer(R FHc bis-OH ): HO—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -} nFH —(CR H 1 R H 2 ) h2 -OH

polymer(R FcH OH-vinyl ): HO—(CR H 1 R H 2 ) h1 -J H -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -J H -} nFH —(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CF═CF 2

polymer(R FHc OH-vinyl ): HO—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -} nFH —(CR H 1 R H 2 ) h2 -OCF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CF═CF 2

polymer(R FcH bis-vinyl ): CF 2 ═CF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR H 1 R H 2 ) h1 -J H -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -J H -} nFH —(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CF═CF 2

polymer(R FHc bis-vinyl ): CF 2 ═CF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR H 1 R H 2 ) h1 -E H -R H -E HC -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -} nFH —(CR H 1 R H 2 ) h2 -OCF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CF═CF 2

wherein in formulae above nFH is an integer of 1 or more.

12. A mixture (mixture (FF)) of polymers comprising a fully fluorinated polyether backbone possessing a plurality of recurring units including at least one cyclic group; and

said backbone comprises recurring units selected from the group consisting of units (R FcF ) and units (R FFc ):

unit (RFcF): —O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E cfF -R cfF -E cfF -O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -J F -(CR F 1 R F 2 ) h2 -O—;

unit (R FHc ):

—O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O—R fF —O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -E FC - R FC -E FC -(CR F 1 R F 2 ) h2 -O—;

wherein:

each or R f 1 and R f 2 , equal to or different from each other, is F or a C 1 -C 6 perfluorocarbon group;

a and b being independently zero or 1;

R fF is either a divalent, linear or branched, perfluorocarbon chain, wherein said perfluorocarbon chain comprises from 1 to 10 carbon atoms and is optionally interrupted by one or more oxygen atoms; or is a group of formula: -E fF -R cf -E fF -;

R cfF is a divalent perfluorocarbon cyclic group, which may be a perfluorocycloaliphatic, which may comprise one or more than one cyclic moiety, and which may comprise one or more than one oxygen atom included in the cycle;

each of E fF , equal to or different from each other, is a bond, or a divalent perfluorocarbon group, possibly comprising one or more than one heteroatoms selected from Cl, and O;

J F is either selected from a bond, a —O— group and a divalent linear or branched perfluoro(oxy)alkylene group, wherein said perfluoro(oxy)alkylene group comprises from 1 to 8 carbon atoms and is optionally interrupted by one or more than one ethereal oxygen atom; or is a group -E FC -R FC -E FC -;

each of E FC is selected from a bond, a —O— group and a divalent linear or branched perfluoro(oxy)alkylene group, wherein said perfluoro(oxy)alkylene group comprises from 1 to 8 carbon atoms and is optionally interrupted by one or more than one ethereal oxygen atom;

R FC is divalent perfluorocarbon cyclic group, which may be a perfluorocycloaliphatic, which may comprise one or more than one cyclic moiety, and which may comprise one or more than one oxygen atom included in the cycle;

h1 and h2 being independently zero or 1;

each of R F 1 and R F 2 , equal to or different from each other at each occurrence, is independently F or a C 1 -C 6 perfluorocarbon group.

13. A mixture (FHOC(O)F) of polymers of any of formulae below:

polymer(R FcH bis-OC(O)F ): F—C(O)—O—(CR H 1 R H 2 ) h1 -JH-{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -J H -}nFH—(CR H 1 R H 2 ) h2 -O—C(O)—F

polymer(R FHc bis-OC(O)F ): F—C(O)—O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -}nFH—(CR H 1 R H 2 ) h2 -O—C(O)—F

polymer(R FcH OC(O)F-vinyl ): F—C(O)—O—(CR H 1 R H 2 ) h1 -J H -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -J H -}nFH—(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CF═CF 2

polymer(R FHc OC(O)—F-vinyl ): F—C(O)—O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -}nFH—(CR H 1 R H 2 ) h2 -OCF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CF═CF 2

polymer(R FcH bis-vinyl ): CF 2 ═CF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR H 1 R H 2 ) h1 -J H -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -J H -}nFH—(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O- E f -R cf -E f -O—(CR f 1 R f 2 ) b —CF═CF 2

polymer(R FHc bis-vinyl ): CF 2 ═CF—(CR f 1 R f 2 ) a —O-E f -R cf -E f -O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -{(CR H 1 R H 2 ) h2 -O—CF 2 CHF—(CR f 1 R f 2 ) a —O—Rf-O—(CR f 1 R f 2 ) b —CFHCF 2 —O—(CR H 1 R H 2 ) h1 -E HC -R HC -E HC -} nFH —(CR H 1 R H 2 ) h2 -OCF 2 CHF—(CR f 1 R f 2 ) a —O—R f —O—(CR f 1 R f 2 ) b —CF═CF 2

wherein in formulae above nFH is an integer of 1 or more;

and wherein:

wherein:

each of E f , equal to or different from each other, is a bond, or a divalent fluorocarbon group, optionally comprising one or more than one heteroatoms selected from Cl, N, O and S;

each or R f 1 and R f 2 , equal to or different from each other, is F or a C 1 -C 6 perfluorocarbon group;

a and b being independently zero or 1;

h1 and h2 being independently zero or 1;

each of R H 1 and R H 2 , equal to or different from each other at each occurrence, is independently H or a C 1 -C 6 hydrocarbon group.

14. A mixture (FF—OC(O)F) of polymers of any of formulae below:

polymer(R FcF bis-OC(O)F ): F—C(O)—O—(CR F 1 R F 2 ) h1 -J F -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cf -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -J F -}nFF—(CR F 1 R F 2 ) h2 -O—C(O)—F

polymer(R FFc bis-OC(O)F ): F—C(O)—O—(CR F 1 R F 2 ) h1 -E FC -R FC -E FC -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O—R fF —O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -E FC -R FC -E FC -} nFF —(CR F 1 R F 2 ) h2 -O—C(O)—F

polymer(R FcF OC(O)F-C2F5 ): F—C(O)—O—(CR F 1 R F 2 ) h1 -J F -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -J F -} nFF —(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 3

polymer(R FFc OC(O)—F-C2F5 ): F—C(O)—O—(CR F 1 R F 2 ) h1 -E FC -R FC -E FC -{(CR F 1 R F 2 ) h2 —O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O—R fF —O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -E FC -R FC -E FC -} nFF —(CR F 1 R F 2 ) h2 -OCF 2 CF 2 —(CR f 1 R f 2 ) a —O—R fF —O—(CR f 1 R f 2 ) b —CF 2 CF 3

polymer(R FcF bis-C2F5 ): CF 3 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR F 1 R F 2 ) h1 -J F -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -J F -} nFF —(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 3

polymer(R FFc bis-C2F5 ): CF 3 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR F 1 R F 2 ) h1 -E FC -R FC -E FC -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O—R fF —O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -E FC -R FC -E FC -} nFH —(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 3

wherein in formulae above nFF is an integer of 1 or more;

wherein:

each of E fF , equal to or different from each other, is a bond, or a divalent perfluorocarbon group, possibly comprising one or more than one heteroatoms selected from Cl, and O;

each or R f 1 and R f 2 , equal to or different from each other, is F or a C 1 -C 6 perfluorocarbon group;

a and b being independently zero or 1;

R FC is divalent perfluorocarbon cyclic group, which may be a perfluorocycloaliphatic or a perfluorocycloaromatic group, which may comprise one or more than one cyclic moiety, and which may comprise one or more than one heteroatom included in the cycle, said heteroatom being selected from N, O and S;

h1 and h2 being independently zero or 1;

each of R F 1 and R F 2 , equal to or different from each other at each occurrence, is independently F or a C 1 -C 6 perfluorocarbon group.

15. A mixture (FF-COOH) of polymers of any of formulae below:

polymer(R FcF bis-COOH ): HOOC-J F -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -J F -} nFF -COOH

polymer(R FFc bis-COOH ): HOOC-E FC -R FC -E FC -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O—R fF —O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -E FC -R FC -E FC -} nFF -COOH

polymer(R FcF COOH-C2F5 ): HOOC-J F -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cf -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -J F -} nFF —(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 3

polymer(R FFc COOH-C2F5 ): HOOC-E FC -R FC -E FC -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O—R fF —O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -E FC -R FC -E FC -} nFF —(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O—R fF —O—(CR f 1 R f 2 ) b —CF 2 CF 3

polymer(R FcF bis-C2F5 ): CF 3 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR F 1 R F 2 ) h1 -J F -{(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 2 —O—(CR F 1 R F 2 ) h1 -J F -}nFF—(CR F 1 R F 2 ) h2 -O—CF 2 CF 2 —(CR f 1 R f 2 ) a —O-E fF -R cfF -E fF -O—(CR f 1 R f 2 ) b —CF 2 CF 3

wherein in formulae above nFF is an integer of 1 or more;

and wherein:

each of E fF , equal to or different from each other, is a bond, or a divalent perfluorocarbon group, possibly comprising one or more than one heteroatoms selected from Cl, and O;

each or R f 1 and R f 2 equal to or different from each other, is F or a C 1 -C 6 perfluorocarbon group;

a and b being independently zero or 1;

h1 and h2 being independently zero or 1;

each of R F 1 and R F 2 , equal to or different from each other at each occurrence, is independently F or a C 1 -C 6 perfluorocarbon group.

16. A method for lubricating a magnetic recording medium, comprising using the mixture of claim 9 , or any derivative thereof.

Priority Claims (1)

EP 18178895 · Jun 20, 2018 · regional

Continuity (1)

Related Publication 20210246394A1 · Aug 12, 2021

Cited By (2)

US 12,415,964 US 12,584,075