Austenitic stainless alloy
The present disclosure relates to an austenitic stainless alloy comprising in weight % (wt %): C less than 0.03; Si less than 1.0; Mn less than or equal to 1.2; Cr 26.0 to 30.0; Ni 29.0 to 37.0; Mo 6.1 to 7.1 or (Mo+W/2) 6.1 to 7.1; N 0.25 to 0.36; P less than or equal to 0.04; S less than or equal to 0.03; Cu less than or equal to 0.4; balance Fe and unavoidable impurities and to the use thereof and to products made thereof. Thus, the austenitic stainless alloy comprises a low content of manganese in combination with a high content of nitrogen. The present disclosure also relates to the use of said austenitic stainless alloy, especially in highly corrosive environments and to products made of thereof.
1. An austenitic stainless alloy consisting of in weight %:
C less than 0.03;
Si more than 0.1 to less than 1.0;
Mn 0.6 to 1.1;
Cr 26.0 to 30.0;
Ni 34 to 36;
Mo 6.1 to 7.1;
N 0.26 to 0.36;
P less than or equal to 0.04;
S less than or equal to 0.03;
Cu 0.001 to 0.4;
one or more elements of the group of Al, V, Nb, Ti, O, Zr, Hf, Ta, Mg, Pb, Co, Bi, Ca, La, Ce, Y and B in a total content of less than or equal to 1.0; and
a balance of Fe and unavoidable impurities,
wherein the austenitic stainless alloy has a critical pitting temperature of greater than 108° C., conducted per ASTM G150 with 3M MgCl 2 and ground sample.
2. The austenitic stainless alloy according to claim 1 , wherein the content of Si is less than 0.5 wt %.
3. The austenitic stainless alloy according to claim 1 , wherein the content of Si is from 0.1 to 0.3 wt %.
4. The austenitic stainless alloy according to claim 1 , wherein the content of Cr is from 26 to 29 wt %.
5. The austenitic stainless alloy according to claim 1 , wherein the content of Cr is from 26 to 28 wt %.
6. The austenitic stainless alloy according to claim 1 , wherein the content of Cr is more than 26 wt %.
7. The austenitic stainless alloy according to claim 1 , wherein the content of Mo is from 6.3 to 6.8 wt %.
8. The austenitic stainless alloy according to claim 1 , wherein the austenitic stainless alloy has a yield strength (Rp 0 2 ) of 351 MPa to 427 MPa.
9. The austenitic stainless alloy according to claim 1 , wherein the critical pitting temperature is 108° C. to 112.6° C.
10. The austenitic stainless alloy according to claim 8 , wherein the austenitic stainless alloy has a tensile strength (R m ) of 739 MPa to 827 MPa.
11. The austenitic stainless alloy according to claim 1 , wherein the austenitic stainless alloy has an elongation (A) of 56.3% to 66.8%.
12. An object comprising the austenitic stainless alloy according to claim 1 .
13. The object according to claim 12 , wherein said object is a tube, a pipe, a bar, a wire, a plate, a sheet and/or a strip.
14. An austenitic stainless alloy consisting of in weight %:
C less than 0.03;
Si 0.1 to 0.3;
Mn 0.6 to 1.1;
Cr 26.0 to 28.0;
Ni 34.0 to 36.0;
Mo 6.3 to 6.8;
N 0.26 to 0.36;
P less than or equal to 0.04;
S less than or equal to 0.03;
Cu 0.001 to 0.4;
one or more elements of the group of Al, V, Nb, Ti, O, Zr, Hf, Ta, Mg, Pb, Co, Bi, Ca, La, Ce, Y and B in a total content of less than or equal to 1.0; and
a balance of Fe and unavoidable impurities,
wherein the austenitic stainless alloy has a critical pitting temperature of greater than 108° C., conducted per ASTM G150 with 3M MgCl 2 and ground sample.
15. The austenitic stainless alloy according to claim 14 , wherein the austenitic stainless alloy has a yield strength (Rp 0 2 ) of 351 MPa to 427 MPa, and wherein the critical pitting temperature is 108° C. to 112.6° C.
16. An object comprising the austenitic stainless alloy according to claim 14 , wherein the object is a tube, a pipe, a bar, a wire, a plate, a sheet and/or a strip.
17. The austenitic stainless alloy according to claim 14 , wherein the critical pitting temperature is 108° C. to 112.6° C.
18. An object comprising the austenitic stainless alloy according to claim 17 , wherein the object is a tube, a pipe, a bar, a wire, a plate, a sheet and/or a strip.
19. The austenitic stainless alloy according to claim 14 , wherein the content of C is less than 0.020 wt %, wherein the content of N is 0.26 to 0.30 wt %, and wherein the content of Cu is 0.10 to 0.4 wt %.
20. The austenitic stainless alloy according to claim 19 , wherein the critical pitting temperature is 108° C. to 112.6° C.
21. An object comprising the austenitic stainless alloy according to claim 20 , wherein the object is a tube, a pipe, a bar, a wire, a plate, a sheet and/or a strip.