Method for sulfonating and oxidizing sawdust to form a sorbent
A method for producing a modified sawdust sorbent. The method involves sulfonating sawdust with sulfuric acid and oxidizing the sulfonated sawdust with hydrogen peroxide. The method yields a modified sawdust sorbent containing sulfonated and oxidized cellulose. The modified sawdust sorbent has a higher surface area, higher organic dye adsorption capacity, and more rapid organic dye adsorption rate than unmodified sawdust. A method of using the modified sawdust sorbent for organic dye removal from water is included.
1. Method for sulfonating and oxidizing sawdust to form a modified sawdust sorbent comprising:
mixing the sawdust with sulfuric acid to form a sulfonating mixture,
heating the sulfonating mixture at 100 to 200° C. to form a sulfonated sawdust,
washing and drying the sulfonated sawdust at 50 to 150° C. to form a dried sawdust,
treating the dried sawdust with a 3-5 vol % hydrogen peroxide solution in an amount of 350 to 650 mL of hydrogen peroxide solution per 100 g of dried sawdust to form a peroxide-treated sawdust,
washing and drying the peroxide-treated sawdust at 50 to 150° C. to form a sulfonated and oxidized sawdust, and
milling and sieving the sulfonated and oxidized sawdust to form the modified sawdust sorbent,
wherein the modified sawdust sorbent has a dye adsorption capacity of 20 to 25 mg of dye per g of sorbent at 25 to 45° C.
2. The method of claim 1 , wherein the sawdust is yellow pine sawdust.
3. The method of claim 1 , wherein the sawdust is present in the sulfonating mixture in an amount of 45 to 65 wt % and the sulfuric acid is present in the sulfonating mixture in an amount of 35 to 55 wt %, each based on a total weight of the sulfonating mixture.
4. The method of claim 1 , wherein the sulfuric acid is dilute sulfuric acid having a concentration of 0.1 to 4.2 mol/L.
5. The method of claim 1 , wherein the treating is performed at ambient temperature for 1 to 3 hours.
6. The method of claim 1 , wherein the sieving is performed with a sieve with 400 to 800 μm openings.
7. The method of claim 1 , wherein the washing of the sulfonated sawdust and the washing of the peroxide-treated sawdust are performed with water.
8. The method of claim 1 , wherein the heating of the sulfonating mixture is performed in a vacuum oven at a pressure of 0.01 to 0.25 atm.
9. The method of claim 1 , where the drying of the sulfonated sawdust and the drying of the peroxide-treated sawdust are performed in a vacuum oven at a pressure of 0.01 to 0.25 atm.
10. The method of claim 1 , wherein the modified sawdust sorbent has a moisture content of 0.1 to 10 wt % based on a total weight of modified sawdust sorbent, a pH of 2 to 7, a density of 0.35 to 0.65 g/cm 3 , and a surface area of 1.75 to 2.85 m 2 /g.