Water-, oil- and grease-resistant multilayer coating for paper-based substrate and uses thereof
The present invention relates to a water-, oil- and grease-resistant multilayer coating for a paper-based substrate comprising a water-based inner primer coating, an intermediate polymeric extrusion coating, and a water-based top barrier coating, wherein a surface of the paper-based substrate coated therewith has water, oil and grease barrier properties, and wherein the paper-based substrate coated therewith is repulpable and recyclable.
1. A water-, oil- and grease-resistant multilayer coating for a paper-based substrate comprising:
a water-based inner primer coating comprising 0.01 g/m 2 of polyethyleneimine (PEI);
an intermediate polymeric extrusion coating comprising 10 g/m 2 of co-extruded low-density polyethylene (LDPE) and high-density polyethylene (HDPE) by weight ratio about 40/60 respectively; and
5 g/m 2 of a water-based top barrier coating,
wherein a surface of the paper-based substrate coated therewith has water, oil and grease barrier properties, and wherein the paper-based substrate coated therewith is repulpable and recyclable.
2. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the water-based inner primer coating acts as an adhesion promoter for the intermediate polymeric extrusion coating.
3. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the intermediate polymeric extrusion coating provides flexibility, water, oil and grease barrier properties.
4. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the water-based top barrier coating provides additional water, oil and grease barrier properties onto the intermediate polymeric extrusion coating.
5. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the water-based top barrier coating acts as a protective layer for the intermediate polymeric extrusion coating for corrugated applications.
6. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the water-, oil- and grease-resistant multilayer coating preserves physical properties of the surface of the paper-based substrate coated therewith.
7. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein physical properties comprises mechanical strength, printability and gluability.
8. The water-, oil- and grease-resistant multilayer coating of claim 7 , wherein the mechanical strength comprises resistance to tear, burst, ring crush, short span compression strength (STFI), tensile, tensile energy absorption (TEA) stiffness, box compression strength (BCT), edge crush strength (ECT), flat crush strength (FCT), or a combination thereof.
9. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the water-based inner primer coating is formed from a water-based composition having at least one solvent-based adhesive.
10. The water-, oil- and grease-resistant multilayer coating of claim 9 , wherein the solvent-based adhesive comprises water as a solvent.
11. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the intermediate polymeric extrusion coating is obtained by extrusion of a polymer or co-extrusion of polymers.
12. The water-, oil- and grease-resistant multilayer coating of claim 11 , wherein the intermediate polymeric extrusion coating further comprises a low surface tension polymer.
13. The water-, oil- and grease-resistant multilayer coating of claim- 12 , wherein the low surface tension polymer consists of low density polyethylene (LDPE).
14. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the water-based top barrier coating is formed from a water-based composition having at least one polymer providing water, oil and grease barrier properties.
15. The water-, oil- and grease-resistant multilayer coating of claim 9 , wherein the solvent-based adhesive is selected from the group consisting of polyethyleneimine (PEI), styrene-butadiene copolymer, styrene-acrylic copolymer, styrene-acrylic-acrylonitrile copolymer, polyester-polyurethane elastomer, acrylates, starch, PVOH (polyvinyl alcohol), PVAc (polyvinyl acetate), PVDC (polyvinylidene chloride), LDPE emulsions, HDPE emulsions, Nylon emulsions, clay coating, PHA/PHB, dextrin and combinations thereof.
16. The water-, oil- and grease-resistant multilayer coating of claim- 11 , wherein the polymer to be extruded or co-extruded is selected from the group consisting of polyethylene (PE), polylactic acid (PLA), PBS, PBAT, PP, PET, Nylon, EVOH, EMA, and combinations thereof.
17. The water-, oil- and grease-resistant multilayer coating of claim- 16 further comprises an inorganic extrusion master batch as a filler.
18. The water-, oil- and grease-resistant multilayer coating of claim 17 , wherein the inorganic extrusion master batch is selected from the group consisting of calcium carbonate, clays, talc, titanium dioxide and combinations thereof.
19. The water-, oil- and grease-resistant multilayer coating of claim 16 , wherein the polyethylene is selected from the group consisting of low-density polyethylene (LDPE), high-density polyethylene (HDPE), metallocene linear low-density polyethylene (mLLDPE) and combinations thereof.
20. The water-, oil- and grease-resistant multilayer coating of claim 14 , wherein the at least one polymer is selected from the group consisting of styrene-acrylic copolymer, styrene-acrylic-acrylonitrile copolymer, styrene-butadiene copolymer, PVDC, PVOH, Starch, PLA emulsion, PHA/PHB emulsion, LDPE emulsions, HDPE emulsions, Nylon emulsions, polyurethane, silicones emulsions and combinations thereof.
21. The water-, oil- and grease-resistant multilayer coating of claim 1 , wherein the surface of the paper-based substrate coated therewith presents a Cobb test value below 2.0 gram of water/m 2 , a Water Vapor Transmission Rate (WVTR) test value below 60.0 grams of water/m 2 , a surface tension test value at least about 50.0 dynes/cm and an oil and grease resistance 3M kit test value of at least about 12.0.
22. A water-, oil- and grease-resistant multilayer coating for paper-based substrate, comprising:
an inner water-based primer coating comprising 0.01 g/m 2 of polyethyleneimine (PEI);
an intermediate polymeric extrusion coating comprising 10 g/m 2 of co-extruded low-density polyethylene (LDPE) and high-density polyethylene (HDPE) in a three-layers HDPE-LDPE-HDPE arrangement where HDPE represents 60% by weight of the total weight of the intermediate polymeric extrusion coating; and
5 g/m 2 of a top water-based barrier coating.