Waterproof membrane with cross-laminated film

1. A waterproof extrusion laminated membrane, comprising:

a first non-woven layer having first and second surfaces;

a water impermeable cross laminated film layer formed from two plies of high density polyethylene, the two plies being mechanically oriented forming an oriented cross laminated film, the cross laminated film layer having a thickness of about 3.0 mils;

a second non-woven layer having first and second surfaces; and

a tie layer between the first non-woven first surface and the oriented cross-laminated film and the second non-woven first surface and the oriented cross-laminated film,

wherein the membrane is flexible and exhibits a tensile break in a machine direction and a transverse direction measured in accordance with standard ASTM D 882 of about 32 lbs/in and 29 lbs/in, respectively, a tear propagation resistance in the machine direction and the transverse direction measured in accordance with standard ASTM D 1938 of about 7.2 lbs/in and 6.6 lbs/in, respectively, a Toyo impact measured in accordance with a modified standard ASTM D 781 of about 145 kilogram centimeters, and a water vapor transmission rate measured in accordance with standard ASTM E96—procedure E of less than about 0.075 US Perms measured at about 37.8 C at about 90% relative humidity,

wherein the tie layer is a polyolefin or polyolefin copolymer or a blend thereof.

2. A waterproof extrusion laminated membrane, comprising:

a first non-woven layer having first and second surfaces;

a water impermeable cross laminated film layer formed from two plies of high density polyethylene, the two plies being mechanically oriented forming an oriented cross laminated film, the cross laminated film layer having a thickness of about 3.0 mils;

a second non-woven layer having first and second surfaces; and

a tie layer between the first non-woven first surface and the oriented cross-laminated film and the second non-woven first surface and the oriented cross-laminated film,

wherein the membrane is flexible and exhibits a tensile break in a machine direction and a transverse direction measured in accordance with standard ASTM D 882 of about 32 lbs/in and 29 lbs/in, respectively, a tear propagation resistance in the machine direction and the transverse direction measured in accordance with standard ASTM D 1938 of about 7.2 lbs/in and 6.6 lbs/in, respectively, a Toyo impact measured in accordance with a modified standard ASTM D 781 of about 145 kilogram centimeters, and a water vapor transmission rate measured in accordance with standard ASTM E96—procedure E of less than about 0.075 US Perms measured at about 37.8 C at about 90% relative humidity,

wherein the tie layer is a propylene based elastomer blend.

3. The membrane of claim 2 wherein the propylene based elastomer blend includes low density polyethylene (LDPE).

4. The membrane of claim 3 wherein the propylene based elastomer is present at about 10 percent to about 60 percent by weight of the blend and wherein the LDPE is present at about 40 percent to about 90 percent by weight of the blend.

5. The membrane of claim 3 wherein the propylene based elastomer is present at about 25 percent by weight of the blend and wherein the LDPE is present at about 75 percent by weight of the blend.

6. A waterproof extrusion laminated membrane, comprising:

a first non-woven layer having first and second surfaces;

a water impermeable cross laminated film layer formed from two plies of high density polyethylene, the two plies being mechanically oriented forming an oriented cross laminated film, the cross laminated film layer having a thickness of about 3.0 mils;

a second non-woven layer having first and second surfaces; and

a tie layer between the first non-woven first surface and the oriented cross-laminated film and the second non-woven first surface and the oriented cross-laminated film,

wherein the membrane is flexible and exhibits a tensile break in a machine direction and a transverse direction measured in accordance with standard ASTM D 882 of about 32 lbs/in and 29 lbs/in, respectively, a tear propagation resistance in the machine direction and the transverse direction measured in accordance with standard ASTM D 1938 of about 7.2 lbs/in and 6.6 lbs/in, respectively, a Toyo impact measured in accordance with a modified standard ASTM D 781 of about 145 kilogram centimeters, and a water vapor transmission rate measured in accordance with standard ASTM E96—procedure E of less than about 0.075 US Perms measured at about 37.8 C at about 90% relative humidity,

wherein the tie layer is present at about 5 to about 20 lbs per ream of membrane.

7. The membrane of claim 6 wherein the tie layer is present at about 7 to about 10 lbs per ream of membrane.

8. The membrane of claim 1 wherein the non-woven layer is a polypropylene non-woven fabric.

9. The membrane of claim 1 wherein the polypropylene non-woven fabric has a basis weight of about 0.5 osy to about 4.0 osy.

10. The membrane of claim 9 wherein the polypropylene non-woven fabric has a basis weight of about 0.9 osy.

11. The membrane of claim 1 wherein the HDPE oriented cross laminated film has a thickness of about 3.0 mils.

12. An extrusion laminated waterproof membrane, comprising:

first and second polypropylene non-woven layers having first and second surfaces;

a water impermeable HDPE oriented cross laminated film layer, the oriented cross laminated film layer having a thickness of about 3.0 mils; and

a tie layer between the first non-woven first surface and the oriented cross laminated film layer and the second non-woven first surface and the oriented cross laminated film layer, the tie layer being a propylene based elastomer or propylene based elastomer blend,

wherein the first and second polypropylene non-woven layers each have a basis weight of about 0.9 osy, the HDPE oriented cross laminated film layer has a thickness of about 3.0 mils, and each tie layer is present at about 7 to about 10 lbs per ream of membrane,

wherein the tie layer is a propylene based elastomer blend with LDPE and wherein the propylene based elastomer is present at about 25 percent by weight of the blend and wherein the LDPE is present at about 75 percent by weight of the blend, and

wherein the membrane is flexible.

13. A waterproof extrusion laminated flexible membrane for waterproofing a curvilinear finished surface, comprising:

first and second polypropylene non-woven layers having first and second surfaces;

a water impermeable HDPE oriented cross laminated film layer, the cross laminated film layer having a thickness of about 3.0 mils; and

a tie layer between the first non-woven first surface and the cross laminated film layer and the second non-woven first surface and the cross laminated film layer, the tie layer being a propylene based elastomer or propylene based elastomer blend,

wherein the flexible membrane may be seamlessly applied to a substrate on a curvilinear surface for waterproofing,

wherein the first and second polypropylene non-woven layers each have a basis weight of about 0.9 osy, the oriented cross laminated film layer has a thickness of about 3.0 mils, and each tie layer is present at about 7 to about 10 lbs per ream of membrane, and

wherein the tie layer is a propylene based elastomer blend with LDPE and wherein the propylene based elastomer is present at about 25 percent by weight of the blend and wherein the LDPE is present at about 75 percent by weight of the blend.

14. The membrane of claim 2 wherein the non-woven layer is a polypropylene non-woven fabric.

15. The membrane of claim 2 wherein the polypropylene non-woven fabric has a basis weight of about 0.5 osy to about 4.0 osy.

16. The membrane of claim 15 wherein the polypropylene non-woven fabric has a basis weight of about 0.9 osy.

17. The membrane of claim 2 wherein the HDPE oriented cross laminated film has a thickness of about 3.0 mils.