Charged isoporous materials for electrostatic separations
Multiblock polymer materials, methods of preparing, and using to separate proteins, nucleic acids, other biological or other biomolecules, compounds, or solutes, with high fluxes through electrostatic interactions where the self-assembled block polymer materials contain at least one of macro, meso, or micro pores, and at least some of the pores are isoporous, and at least one polymer block contains stationary electrostatic charge, or reactive functional groups to provide large surface areas that are charged in isoporous structure.
1. A charged, self-assembled poly(isoprene-b-styrene-b-4-vinyl pyridine) triblock copolymer material for solute separations, the material comprising:
a surface layer comprising a plurality of mesopores having a size of from 5 nm to 100 nm, wherein the mesopores are isoporous and have a pore size distribution from 1 to 3, wherein the pore size distribution is defined as the ratio of the maximum pore diameter to the minimum pore diameter;
wherein at least a portion of the 4-vinyl pyridine block is quaternized to provide the material with a positive stationary charge wherein the degree of charge on the at least a portion of the 4-vinyl pyridine block is ≤90% of all available units; and
wherein the material exhibits a hydraulic permeability of 50 to 200 L·m −2 ·hr −1 ·bar −1 at a pH of 7.0.
2. The material of claim 1 , wherein the material has an asymmetric structure or a symmetric structure.
3. The material of claim 2 , wherein the material contains macroporous domains and mesoporous wall structures in a single, integral structure.
4. The material of claim 3 , wherein the macroporous domains are continuous.
5. The material of claim 1 , wherein the 4-vinyl pyridine block is quaternized by a functionalization reaction, and the functionalization reaction provides the positive stationary charge.
6. The material of claim 1 , wherein the 4-vinyl pyridine block is quaternized by reacting the 4-vinyl pyridine block with a quaternizing agent defined by the formula R—X, where R comprises a C 1 -C 24 substituted or unsubstituted, straight-chain, cyclic or branched alkyl or alkenyl group and X is a leaving group.
7. The material of claim 1 , wherein the 4-vinyl pyridine block is quaternized by reacting the 4-vinyl pyridine block with a quaternizing agent having the formula R—W—(R)—CH 2 —X, where R is a C 1 -C 24 substituted or unsubstituted alkyl, alkenyl or aryl group, W is a heteroatom and X is a leaving group.
8. The material of claim 1 , wherein the 4-vinyl pyridine block is quaternized by reacting the 4-vinyl pyridine block with a quaternizing agent of the formula X—R—X, where R is an alkyl, alkenyl, alkenyl or aryl group, and X is a leaving group.
9. The material of claim 6 , wherein R—X is selected from a group consisting of 2-bromoethanol, bromobutane, bromo-PEG, bromopropionic acid, bromovaleric acid, chloroacetamide, chlorobutane, chlorobutyric acid, dodecyl iodide, iodobutane, iodoacetamide, iodoacetic acid and iodopropionic acid.
10. The material of claim 1 , wherein the 4-vinyl pyridine block is quaternized by reacting the 4-vinyl pyridine block with crotonic acid.
11. A self-assembled, charged, A-B-C triblock copolymer material having a surface layer comprising a plurality of mesopores having a size of from 5 nm to 200 nm, wherein the mesopores are isoporous and have a pore size distribution from 1 to 3, wherein the pore size distribution is defined as the ratio of the maximum pore diameter to the minimum pore diameter are isoporous, wherein
one polymer block of the triblock copolymer has a T g of ≤25° C.; and
one polymer block of the triblock copolymer comprises an aromatic heterocycle that is quaternized to provide the material with a positive stationary charge, the aromatic heterocycle selected from the group consisting of pyridines, pyrazines, pyrimidines, pyridazines, quinolones, isoquinolines, quinoxalines, quinazolines, penazines, isoazoles, isothiazoles, imidazoles, benzimidazoles, triazoles, and tetrazoles; wherein the degree of charge on the one polymer block of the triblock copolymer that is quaternized is ≤90% of all available units.
12. The material of claim 11 , wherein the aromatic heterocycle is quaternized by reacting the aromatic heterocycle with a quaternizing agent defined by the formula R-X, where R comprises a C 1 -C 24 substituted or unsubstituted, straight chain, cyclic or branched alkyl or alkenyl group or a polyethylene glycol (PEG) and X is a leaving group.
13. The material of claim 11 , wherein the aromatic heterocycle is quaternized by reacting the aromatic heterocycle with a quaternizing agent having the formula R—W—(R)—CH 2 —X, where R is a C 1 -C 24 substituted or unsubstituted alkyl, alkenyl or aryl group, W is a heteroatom and X is a leaving group.
14. The material of claim 11 , wherein the aromatic heterocycle is quaternized by reacting the aromatic heterocycle with a quaternizing agent of the formula R—(W)—COCH 2 —X where R is a C 1 -C 24 alkyl or alkenyl, or C 6 -C 10 aryl group, W is a heteroatom and X is a leaving group.
15. The material of claim 11 , wherein the aromatic heterocycle is quaternized by reacting the aromatic heterocycle with a quaternizing agent of the formula X—R—X, where R is an alkyl, alkenyl, alkenyl or aryl group, and X is a leaving group.
16. The material of claim 12 , wherein R—X is selected from a group consisting of 2-bromoethanol, bromobutane, bromo-PEG, bromopropionic acid, bromovaleric acid, chloroacetamide, chlorobutane, chlorobutyric acid, dodecyl iodide, iodobutane, iodoacetamide, iodoacetic acid and iodopropionic acid.
17. The material of claim 11 , wherein the aromatic heterocycle is quaternized by reacting the aromatic heterocycle with crotonic acid.
18. The material of claim 11 wherein the polymer block having a Tg of ≤25° C. is a polyisoprene block; and the block comprising the aromatic heterocycle is a poly( 2 -vinyl pyridine) block or a poly(4-vinyl pyridine) block.
19. The material of claim 11 , wherein the A-B-C triblock copolymer material is a poly(isoprene-b-styrene-4-vinyl pyridine) block and the material exhibits a hydraulic permeability of 50 to 200 L·m -2 ·hr -1 ·bar -1 at a pH of 7.0.
20. A method of forming a charged, isoporous multiblock polymer material according to claim 11 , comprising providing at least a portion of the polymer block comprising the aromatic heterocycle with a charged moiety.
21. A method of forming a charged, isoporous multiblock polymer material according to claim 11 , comprising contacting the A-B-C triblock copolymer material with a chemical agent that reacts with the aromatic heterocycle to introduce a stationary charge.
22. A process of separating a target biomolecule from a mixture of other biomolecules or other solutes containing the target biomolecule comprising contacting the mixture with a material according to claim 11 , and then separating and/or removing the target biomolecule.