Method for preparing super absorbent polymer
The method for preparing a super absorbent polymer according to the present disclosure reduces the generating amount of a fine powder while realizing the same particle size distribution in the process of pulverizing the dried polymer, thereby reducing the load of the fine powder reassembly, drying, pulverizing and classifying steps.
1. A method for preparing a super absorbent polymer comprising:
performing crosslinking polymerization of a water-soluble ethylenically unsaturated monomer having an acidic group of which at least a part is neutralized, in the presence of an internal crosslinking agent and a polymerization initiator to form a hydrogel polymer containing a first crosslinked polymer;
drying the hydrogel polymer to form a dried polymer;
pulverizing the dried polymer to prepare pulverized particles so that particles having a diameter of 710 μm in or more are present in an amount of 75 wt % to 90 wt % and particles having a diameter of less than 180 μm are present in an amount of 8.0 wt % or less based on a total weight of the pulverized particles; and
subjecting the pulverized particles to secondary pulverization,
wherein during the secondary pulverization, a reference diameter is determined from a diameter range of 600 μm or more and 850 μm or less, and only particles having a diameter equal to or greater than the reference diameter among the pulverized particles are subjected to the secondary pulverization,
wherein the reference diameter is 710 μm.
2. The preparation method of claim 1 , wherein the crosslinking polymerization is performed in the presence of a foaming agent.
3. The preparation method of claim 1 , wherein particles subjected to the secondary pulverization are combined with particles not subjected to secondary pulverization among the pulverized particles.
4. The preparation method of claim 3 , further comprising classifying the pulverized particles into particles having a diameter of 850 μm or less and 150 μm or more and particles having a diameter of less than 150 μm.
5. The preparation method of claim 1 , wherein among the pulverized particles, particles having a diameter of less than 150 μm are assembled by adding water, and circulated to be included in the drying the hydrogel polymer.