Negative electrode active material for lithium secondary battery and method for preparing the same
A negative electrode active material including a core, an intermediate layer on a surface of the core, and a shell layer on a surface of the intermediate layer, wherein the core includes a silicon oxide of SiO x (0<x<2); the intermediate layer includes a lithium silicate, the shell layer includes lithium fluoride (LiF) and the intermediate layer is present in an amount of 5 wt %-15 wt % based on a total weight of the negative electrode active material. Also, a method for preparing the negative electrode active material, and a negative electrode and lithium secondary battery including the same. The negative electrode active material provides excellent initial efficiency and life characteristics.
1. A method for preparing a negative electrode active material, comprising the steps of:
(S1) dispersing particles of a silicon oxide of formula SiO x , wherein 0<x<2, in a dispersion medium to prepare a suspension;
(S2) adding a solution comprising lithium fluoride (LiF) to the suspension to obtain a mixture, and agitating and filtering the mixture to obtain SiO x particles having a shell layer comprising LiF formed on a surface thereof; and
(S3) heat treating the SiO x particles having the shell layer to form an intermediate layer comprising a lithium silicate at an interface between the SiO x particles and the shell layer,
wherein the heat treatment in step (S3) is carried out at a temperature lower than a melting point of LiF.
2. The method for preparing a negative electrode active material according to claim 1 , wherein the agitation in step (S2) is carried out at a temperature of 25° C.-100° C. for 0.5 hours-1 hour.
3. The method for preparing a negative electrode active material according to claim 1 , wherein the heat treatment in step (S3) is carried out at a temperature of 700° C.-780° C.
4. The method for preparing a negative electrode active material according to claim 1 , which further comprises a step of forming a carbon coating layer on a surface of the shell layer, after step (S3).
5. The method for preparing a negative electrode active material according to claim 1 , wherein the dispersion medium comprises ethanol.
6. The method for preparing a negative electrode active material according to claim 1 , wherein a weight ratio of the suspension of SiOx particles and the solution comprising lithium fluoride is 1:1-1:10.
7. The method for preparing a negative electrode active material according to claim 1 , wherein the shell layer is present in an amount of 0.1 wt %-3 wt % based on a total weight of the negative electrode active material.
8. The method for preparing a negative electrode active material according to claim 1 , wherein the heat treatment in step (S3) is carried out under vacuum or under inert atmosphere.