Method for manufacturing metal plate
A method for manufacturing a metal plate, the metal plate including a first surface and a second surface positioned on the opposite side of the first surface, may include a step of rolling a base metal having an iron alloy containing nickel to produce the metal plate. The metal plate may include particles containing as a main component an element other than iron and nickel. In a sample including the first surface and the second surface of the metal plate, the following conditions (1) and (2) regarding the particles may be satisfied: (1) The number of the particles having an equivalent circle diameter of 1 μm or more is 50 or more and 3000 or less per 1 mm 3 in the sample, and (2) The number of the particles having an equivalent circle diameter of 3 μm or more is 50 or less per 1 mm 3 in the sample.
1. A method for manufacturing a metal plate used for manufacturing a deposition mask, the metal plate including a first surface and a second surface positioned on the opposite side of the first surface, the method comprising:
a step of rolling a base metal having an iron alloy containing 34% by mass to 38% by mass nickel to produce the metal plate,
wherein the metal plate comprises particles containing as a main component an element other than iron and nickel;
wherein in a sample including the first surface and the second surface of the metal plate, the following conditions (1) and (2) regarding the particles are satisfied
(1) the number of the particles having an equivalent circle diameter of 1 μm or more is 50 or more and 3000 or less per 1 mm 3 in the sample; and
(2) the number of the particles having an equivalent circle diameter of 3 μm or more is 50 or less per 1 mm 3 in the sample;
wherein a first ratio of the metal plate is 70% or more;
wherein the first ratio is a ratio of a first quantity to a total quantity;
wherein the total quantity is the number of the particles per 1 mm 3 in the sample; the particles having an equivalent circle diameter of 1 μm or more; and
wherein the first quantity is the number of the particles per 1 mm 3 in the sample, the particles having an equivalent circle diameter of 1 μm or more and less than 3 μm.
2. The method for manufacturing a metal plate according to claim 1 , comprising a surface treatment step of removing a surface part of the base metal or the metal plate.
3. The method for manufacturing a metal plate according to claim 2 , wherein the surface treatment step includes a base-metal surface treatment step of removing the surface part of the base metal; and
wherein a thickness of the surface part is 10 mm or more.
4. The method for manufacturing a metal plate according to claim 2 , wherein the surface treatment step includes a metal-plate surface treatment step of removing the surface part of the metal plate; and
wherein a thickness of the surface part is 5 μm or more.
5. The method for manufacturing a metal plate according to claim 2 , wherein
the surface treatment step includes a step of removing the surface part by exposing a surface of the base metal or the metal plate to a surface treatment liquid.
6. The method for manufacturing a metal plate according to claim 1 , comprising a selection step of selecting the metal plate in which, in a sample including the first surface and the second surface of the selected metal plate, the following conditions (1) and (2) regarding the particles are satisfied:
(1) the number of the particles having an equivalent circle diameter of 1 μm or more is 50 or more and 3000 or less per 1 mm 3 in the sample; and
(2) the number of the particles having an equivalent circle diameter of 3 μm or more is 50 or less per 1 mm 3 in the sample.
7. The method for manufacturing a metal plate according to claim 1 , wherein
the following condition (3) regarding the particles is satisfied:
(3) the number of the particles having an equivalent circle diameter of 1 μm or more is 50 or more and 1000 or less per 1 mm 3 in the sample.
8. The method for manufacturing a metal plate according to claim 1 , wherein
the following condition (4) regarding the particles is satisfied:
(4) the number of the particles having an equivalent circle diameter of 3 μm or more is 20 or less per 1 mm 3 in the sample.
9. The method for manufacturing a metal plate according to claim 1 , wherein
the following condition (5) regarding the particles is satisfied:
(5) the number of the particles having an equivalent circle diameter of 5 μm or more is 20 or less per 1 mm 3 in the sample.
10. The method for manufacturing a metal plate according to claim 1 , wherein
the following condition (6) regarding the particles is satisfied:
(6) the number of the particles having an equivalent circle diameter of 5 μm or more is 2 or less per 1 mm 3 in the sample.
11. The method for manufacturing a metal plate according to claim 1 , wherein
a thickness of the metal plate is 50 μm or less.
12. The method for manufacturing a metal plate according to claim 1 , wherein
a thickness of the metal plate is 30 μm or less.