Substrate-free adhesive tape
A substrate-free adhesive tape that is excellent in adhesive physical properties and is suitable for a continuous process is provided. The substrate-free adhesive tape includes a release film, and an adhesive layer provided on one surface of the release film and the adhesive layer containing a cured product of an adhesive composition, wherein when the release film is fixed on the outer surface of a semicircular tip part of a jig, the semicircular tip part having a radius of 22.5 mm, a breaking distance of the adhesive layer is 110 mm or less when the adhesive layer is stretched at a rate of 20 m/min from a semicircular center of the semicircular tip part toward an outermost direction of the semicircular tip part.
1. A substrate-free adhesive tape comprising a release film, and an adhesive layer provided on one surface of the release film and the adhesive layer containing a cured product of an adhesive composition,
wherein when the release film is fixed on the outer surface of a semicircular tip part of a jig, the semicircular tip part having a radius of 22.5 mm, a breaking distance of the adhesive layer is 110 mm or less when the adhesive layer is stretched at a rate of 20 m/min from a semicircular center of the semicircular tip part toward an outermost direction of the semicircular tip part,
wherein the adhesive composition includes an acrylic copolymer obtained by copolymerization of a monomer mixture containing:
an alkyl group-containing (meth)acrylate monomer;
a cycloalkyl group-containing (meth)acrylate monomer;
a heterocycloalkyl group-containing (meth)acrylate monomer;
a polar group-containing (meth)acrylate monomer; and
2-(2-ethoxyethoxy)ethylacrylate,
wherein the one surface of the release film is a heavy peel surface, and the other surface of the release film is a light peel surface,
wherein the heavy peel surface of the release film is in contact with the adhesive layer,
wherein a release peel force of the heavy peel surface of the release film is 25 g/in or more and less than 54 g/in at the time of peeling off tesa 7475 tape which is a reference tape at a rate of 2.4 m/min, and
wherein the release peel force of the heavy peel surface of the release film is measured as follows:
the reference tape (tesa 7475) with a width of 25.4 mm x a length of 150 mm is attached to the heavy peel surface of the release film by reciprocating a roller with a load of 2 kg twice at a rate of 10 mm/s, aging is performed for 24 hours and then peel strengths at 180 degrees are measured at a rate of 2.4 m/min by using an AR-1000 tester.
2. The substrate-free adhesive tape according to claim 1 ,
wherein the adhesive layer has a travelling distance of 25 mm or less traveled by a ball measured according to ASTM D3121.
3. The substrate-free adhesive tape according to claim 1 ,
wherein the adhesive layer has a thickness of 10 μm or more and 80 μm or less.
4. The substrate-free adhesive tape according to claim 1 , wherein a content of the polar group-containing (meth)acrylate monomer is 3 parts by weight or more and 7 parts by weight or less based on 100 parts by weight of the monomer mixture.
5. The substrate-free adhesive tape according to claim 1 , wherein a content of the alkyl group-containing (meth)acrylate monomer is 50 parts by weight or more and 75 parts by weight or less based on 100 parts by weight of the monomer mixture.
6. The substrate-free adhesive tape according to claim 1 , wherein a content of the cycloalkyl group-containing (meth)acrylate monomer is 5 parts by weight or more and 15 parts by weight or less based on 100 parts by weight of the monomer mixture.
7. The substrate-free adhesive tape according to claim 1 , wherein a content of the heterocycloalkyl group-containing (meth)acrylate monomer is 2 parts by weight or more and 7 parts by weight or less based on 100 parts by weight of the monomer mixture.
8. The substrate-free adhesive tape according to claim 1 , wherein the acrylic copolymer has a weight average molecular weight of 800,000 g/mol or more and 1,200,000 g/mol or less.