Negative electrode active material for non-aqueous electrolyte secondary cell, and non-aqueous electrolyte secondary cell
Negative electrode active material particles comprise base particles having: a silicate phase containing Li 2 O, SiO 2 , at least one oxide selected from M 1 2 O 3 , M 2 O 2 , M 3 2 O 5 , and M 4 O 3 (where M 1 , M 2 , M 3 , and M 4 are elements other than alkali metals, alkali earth metals, and Si), and a discretionary component MO (where M is an alkali earth metal); and silicon particles dispersed in the silicate phase. The element contents for the elements contained in the silicate phase are: 3-33 mol % of Li; 40-78 mol % of S; and 1-40 mol % of M 1 , M 2 , M 3 , and M 4 . If MO is contained, the M content in the silicate phase is 1-10 mol %.
1. A negative electrode active material for a non-aqueous electrolyte secondary battery, comprising base particles,
each of the base particles comprising: a silicate phase including Li, Si, M X , wherein M X is one or more elements other than an alkali metal, an alkaline earth metal, and Si and is selected from the group consisting of B, Bi, Sb, Ge, Zr, P, V, W and La,
wherein, in the silicate phase, a Li content is 3 to 45 mol %, a Si content is 40 to 78 mol %, and an M X content is 1 to 40 mol %, each based on the total amount of elements in the silicate phase other than oxygen.
2. The negative electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein
the silicate phase includes an alkaline earth metal M, and
in the silicate phase, an M content is 1 to 5 mol % based on the total amount of elements other than oxygen.
3. The negative electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein, in the silicate phase, the Li content is 5 to 23 mol %, the Si content is 45 to 78 mol %, and the M X content is 2 to 35 mol %, each based on the total amount of elements other than oxygen.
4. The negative electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein M X includes at least one of B, Zr, P, La, and W.
5. The negative electrode active material for a non-aqueous electrolyte secondary battery according to claim 4 , wherein M X includes at least one of B and Zr.
6. The negative electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein a conductive layer is formed on a surface of the base particle.
7. A non-aqueous electrolyte secondary battery comprising: a negative electrode including the negative electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 , a positive electrode, and a non-aqueous electrolyte.
8. The negative electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein M x further includes at least one of Al and Ti.