Use of closed-pore microspheres of expanded pearlite as a filler for the production of mouldings for the foundry industry
The present invention relates to the use of closed-pore microspheres of expanded perlite as a filler for producing moldings for the foundry industry, to a composition for producing moldings for the foundry industry, comprising closed-pore microspheres of expanded perlite as a filler, and a binder, the binder being selected from the group consisting of water glass, phenol-formaldehyde resins, two-component systems comprising as reactants a polyisocyanate and a polyol component containing free hydroxyl groups (OH groups), and starch, and also to moldings for the foundry industry and to a process for producing a molding for the foundry industry.
1. A molding for the foundry industry, produced using
closed-pore microspheres of expanded perlite, having a closed foam structure with pores separated from one another, and wherein the microspheres are closed on their surface;
wherein the microspheres have a particle size d50 of 200 to 250 μm;
expanded glass;
wherein a weight ratio of perlite to expanded glass ranges from 1:1 to 1:2;
and an organic or inorganic binder or a mixture of organic and inorganic binder, wherein the binder is selected from the group consisting of water glass, phenol-formaldehyde resins, two-component systems comprising as reactants a polyisocyanate and a polyol component containing free hydroxyl groups (OH groups), and starch
wherein the closed-pore microspheres of expanded perlite have a bulk density from 200 to 500 kg/m 3 .
2. The molding as claimed in claim 1 , wherein the microspheres are obtainable by a process in which a perlite sand is expanded in a trickle channel having multistage temperature zones.
3. The molding as claimed in claim 1 , wherein the microspheres have a ratio of pure density to apparent density of greater than 1.8, the apparent density and the pure density being determined with the helium pyknometer.
4. The molding as claimed in claim 1 , wherein the microspheres have a particle strength of above 1.3 N/mm 2 .
5. The molding as claimed in claim 1 , wherein the molding further comprises additional constituents selected from the group consisting of spheres of flyash, foamed glass, quartz sand, calcined kieselguhr, schamotte, cordierite, mullite, and mixtures thereof.
6. The molding as claimed in claim 1 , wherein the molding is selected from the group consisting of insulating or exothermic feeders, feeder surrounds, feeder sleeves, feeder caps, filling funnels, supply elements, and heating pads.
7. The molding as claimed in claim 1 , for producing insulating or exothermic feeders for nonferrous casting.
8. The molding as claimed in claim 1 , wherein the expanded glass comprises a first expanded glass and a second expanded glass, wherein a weight ratio between the first expanded glass and the second expanded glass ranges from 1:1 to 1:2.
9. The molding as claimed in claim 8 , wherein the first expanded glass has a particle size between 0.1 to 0.3 mm and the second expanded glass has a particle size between 0.25 to 0.5 mm.
10. The molding as claimed in claim 1 , wherein the closed-pore microspheres of expanded perlite have a bulk density of 200 to 350 kg/m 3 .