Synthetic pozzolans
Synthetic pozzolans are produced using local materials to provide a cementitious material that is uniform in chemistry and properties independent of the location where the materials are obtained. Two methods of production are described. One is a high temperature process in which materials are processed in a semi-molten or molten state. The second process is a low temperature aqueous process.
1. A method of forming a cured cementitious material, the method comprising:
forming a synthetic calcium silicate cement from precursor materials, the synthetic calcium silicate cement comprising at least 10% by mass of an amorphous phase,
wherein forming the synthetic calcium silicate cement from precursor materials comprises:
selecting one or more precursor raw materials;
blending said one or more precursor raw materials to obtain a blended precursor composition; and
(i) heating said blended precursor composition to a temperature between about 800° C. to about 1400° C. for a time sufficient to react said blended precursor composition, or (ii) performing an aqueous reaction on the blended precursor composition;
adding the synthetic calcium silicate cement to a hydraulic cement to form a mixture, the mixture comprising 10% by mass or more of total solids of the synthetic calcium silicate cement; and
curing the mixture, the curing comprising reacting the synthetic calcium silicate cement and the hydraulic cement.
2. The method of claim 1 , wherein the amorphous phase comprises one or more of siliceous, aluminosiliceous, aluminous material, calcium-aluminum-iron-magnesium-silicate, calcium-silicate.
3. The method of claim 1 , wherein the synthetic calcium silicate cement further comprising crystalline phases such as wollastonite, pseudowollastonite, rankinite, belite, and melilite.
4. The method of claim 1 , wherein the synthetic calcium silicate cement comprises at least 30% by mass of the amorphous phase.
5. The method of claim 1 , wherein the synthetic calcium silicate cement comprises at least 70% by mass of the amorphous phase.
6. The method of claim 1 , wherein the precursor materials comprise calcium silicate.
7. The method of claim 1 , further comprising reacting the synthetic calcium silicate cement with CO 2 to form amorphous SiO 2 and CaCO 3 .
8. The method of claim 1 , wherein the reaction comprises reacting the amorphous phase of the synthetic calcium silicate cement with the hydraulic cement in the presence of water.
9. The method of claim 1 , wherein the reacting of the synthetic calcium silicate cement and the hydraulic cement in the presence of water produces a calcium silicate hydrate compound as a reaction product.
10. The method of claim 7 , wherein Si ions from the amorphous SiO 2 participate in a pozzolanic reaction between the synthetic calcium silicate cement and the hydraulic cement.
11. The method of claim 1 , wherein the mixture comprising 30% or more by mass of total solids of the synthetic calcium silicate cement.
12. The method of claim 11 , wherein the mixture comprising 40% or more by mass of total solids of the synthetic calcium silicate cement.
13. The method of claim 1 , further comprising adding aggregates to the mixture.
14. The method of claim 1 , further comprising adding water to the mixture.
15. The method of claim 1 , further comprising adding at least one admixture to the mixture.
16. The method of claim 1 , wherein the hydraulic cement comprises Ordinary Portland Cement.
17. A method forming a cured cementitious material, the method comprising:
forming a synthetic calcium silicate cement from precursor materials, the synthetic calcium silicate cement comprising at least 10% by mass of an amorphous phase,
wherein forming the synthetic calcium silicate cement from precursor materials further comprises analyzing the chemical compositions of said one or more precursor raw materials;
adding the synthetic calcium silicate cement to a hydraulic cement to form a mixture, the mixture comprising 10% by mass or more of total solids of the synthetic calcium silicate cement; and
curing the mixture, the curing comprising reacting the synthetic calcium silicate cement and the hydraulic cement.
18. A method of forming a cured cementitious material, the method comprising:
forming a synthetic calcium silicate cement from a blend of precursor materials, the synthetic calcium silicate cement comprising at least 10% by mass of an amorphous phase,
wherein a ratio of Ca to the sum of Al, Fe, Mg, and Si of the blend of precursor materials is 0.5-1.0,
adding the synthetic calcium silicate cement to a hydraulic cement to form a mixture, the mixture comprising 10% by mass or more of total solids of the synthetic calcium silicate cement; and
curing the mixture, the curing comprising reacting the synthetic calcium silicate cement and the hydraulic cement.