Method for manufacturing pillar-shaped honeycomb structure filter
A method for manufacturing a pillar-shaped honeycomb structure filter including preparing a pillar-shaped honeycomb structure having a plurality of first cells and a plurality of second cells that are alternately arranged adjacent to each other with a porous partition wall interposed therebetween; adhering ceramic particles containing 50% by mass or more in total of one or two selected from SiC and SiN to a surface of the first cells; and performing a heat-oxidation treatment on the pillar-shaped honeycomb structure in which the ceramic particles are adhered to the surface of the first cells to form a porous film comprised of the ceramic particles having an oxide film thereon so as to satisfy: (1) 0.05≤T≤0.5; (2) 0.05≤T/D50; and (3) 4≤{(W 1 −W 0 )/W 0 ×100}/D50.
1. A method for manufacturing a pillar-shaped honeycomb structure filter, comprising:
preparing a pillar-shaped honeycomb structure comprising a plurality of first cells extending from an inlet side end surface to an outlet side end surface, opening on the inlet side end surface and having a sealing portion on the outlet side end surface, and a plurality of second cells extending from the inlet side end surface to the outlet side end surface, having a sealing portion on the inlet side end surface and opening on the outlet side end surface, the first cells and the second cells being alternately arranged adjacent to each other with a porous partition wall interposed therebetween;
adhering ceramic particles to a surface of each of the plurality of first cells by injecting an aerosol containing the ceramic particles toward the inlet side end surface while applying a suction force to the outlet side end surface to suck the injected aerosol from the inlet side end surface, wherein the ceramic particles contain 50% by mass or more in total of one or two selected from SiC and SiN, and the ceramic particles have a median diameter (D50) in a volume-based cumulative particle size distribution measured by a laser diffraction/scattering method of 0.1 to 6.0 μm; and
performing a heat-oxidation treatment on the pillar-shaped honeycomb structure in which the ceramic particles are adhered to the surface of each of the plurality of first cells to form a porous film on the entire surface of each of the plurality of first cells, the porous film comprised of the ceramic particles having an oxide film thereon so as to satisfy following relational expressions (1) to (3)
0.05≤ T≤ 0.5 (1)
0.05≤ T/D 50 (2)
4≤{( W 1 −W 0 )/ W 0 ×100}/ D 50 (3)
wherein, T (unit: μm) represents an average thickness of the oxide film; D50 (unit: μm) represents the median diameter of the ceramic particles in the volume-based cumulative particle size distribution measured by a laser diffraction/scattering method;
W 0 (unit: g) represents a mass of the ceramic particles adhered to the pillar-shaped honeycomb structure before the heat-oxidation treatment; and
W 1 (unit: g) represents the mass of the ceramic particles adhered to the pillar-shaped honeycomb structure after the heat-oxidation treatment.
2. The method for manufacturing a pillar-shaped honeycomb structure filter according to claim 1 , wherein the porous film has an average film thickness of 2 to 50 μm.
3. The method for manufacturing a pillar-shaped honeycomb structure filter according to claim 1 , wherein the heat-oxidation treatment is performed so as to satisfy 4≤(W 1 −W 0 )/W 0 ×100≤50.
4. The method for manufacturing a pillar-shaped honeycomb structure filter according to claim 1 , wherein the heat-oxidation treatment is performed under a condition of keeping the pillar-shaped honeycomb structure at a maximum temperature of 1000° C. or higher for 1 hour or longer.
5. The method for manufacturing a pillar-shaped honeycomb structure filter according to claim 1 , wherein the porous partition wall contains 50% by mass or more of cordierite.