Glass articles with mixed polymer and metal oxide coatings
According to one or more embodiments, a pharmaceutical package may include a glass container and a coating. The glass container may include a first surface and a second surface opposite the first surface. The first surface may be an outer surface of the glass container. The coating may be positioned over at least a portion of the first surface of the glass container. The coating may include one or more polyimide compositions and one or more metal oxide compositions. The one or more polyimide compositions and the one or more metal oxide compositions may be mixed in the coating.
1. A pharmaceutical package comprising:
a glass container comprising a first surface and a second surface opposite the first surface, wherein the first surface is an outer surface of the glass container; and
a coating positioned on and in direct contact with at least a portion of the first surface of the glass container, the coating comprising
a fluorinated polyimide copolymer formed from a dianhydride monomer component and a diamine monomer component, wherein
the dianhydride monomer component is 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA), and
the diamine monomer component is selected from the group consisting of (i) 1,4-phenylenediamine (mPDA) and 1,3-phenylenediamine (pPDA); (ii) 4,4′-oxydianiline (ODA); (iii) 4,4′-(2,2,2-trifluoro(1-trifluoromethyl)ethylidene)bisbenzeneamine (4,4′-6F); (iv) 3,3′-(2,2,2-trifluoro(1-trifluoromethyl)ethylidene)bisbenzeneamine (3,3′-6F); (v) 2,3,5,6-tetramethylphenylene; and (vi) 2,2,-bis[4-(4-aminophenoxy)phenyl] hexafluoropropane (4BDAF); and
from 33.85 wt. % to 91.5 wt. % titania;
wherein the fluorinated polyimide copolymer and the titania are mixed in the coating;
the coating has a thickness of 100 nm or less;
the combination of the fluorinated polyimide copolymer and titania comprise at least 99.5 wt. % of the coating;
the portion of the first surface of the glass container with the coating has a coefficient of friction of less than or equal to about 0.5; and
the portion of the first surface of the glass container with the coating retains the coefficient of friction of less than or equal to about 0.5 following a heat treatment at a temperature of at least about 300° C. for about 30 minutes.
2. The pharmaceutical package of claim 1 , wherein a light transmission through the pharmaceutical package is greater than or equal to about 55% of a light transmission through an uncoated glass container for each wavelength from about 400 nm to about 700 nm.
3. The pharmaceutical package of claim 2 , wherein the pharmaceutical package retains the light transmission through the pharmaceutical package of greater than or equal to about 55% of the light transmission through the uncoated glass container for each wavelength from about 400 nm to about 700 nm following a heat treatment at a temperature of at least about 250° C. for 30 minutes.
4. The pharmaceutical package of claim 1 , wherein the coating consists of the fluorinated polyimide copolymer and the titania.
5. The pharmaceutical package of claim 1 , wherein the coating consists of the fluorinated polyimide copolymer and the titania, and the fluorinated polyimide copolymer is 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride-co-2,2-bis[4-(4-aminophenoxy)phenyl] hexafluoropropane (6FDA-co-4BDAF).