Process for the preparation of polyacrylamides using an eco-friendly lubricant composition
Process for preparing water-soluble polymers in powder form by polymerization of water-soluble monoethylenically unsaturated monomers comprising the successive steps: a) Spraying on the inner wall of a polymerization vessel, the lubricant composition LC1: alkyl oleate/polyoxyethylene oleyl ether phosphate/sorbitan monolaurate, b) Polymerizing in aqueous solution in the presence of polymerization initiators at least one water-soluble monounsaturated ethylenic monomer, c) Discharging the polymer gel, d) Granulating the polymer gel thus obtained in a granulator, in presence of a lubricant composition LC2: alkyl oleate/polyxoyethylene oleyl ether phosphate/sorbitan monolaurate, e) Drying the polymer gel to obtain a polymer in powder form, f) Grinding and sifting the powder.
1. A process for preparing water-soluble polymers in powder form by polymerization of water-soluble monoethylenically unsaturated monomers comprising the successive steps:
a) spraying on the inner wall of the polymerization vessel the lubricant composition LC1 comprising: 25-40 weight % alkyl oleate/50-65 weight % polyoxyethylene oleyl ether phosphate/and 5-15 weight % sorbitan monolaurate,
b) polymerizing in aqueous solution, in the polymerization vessel, in the presence of polymerization initiators at an initiation temperature between −20° C. and 50° C., at least one water-soluble monounsaturated ethylenic monomer, the total mass concentration of monomer relative to the polymerization charge being between 10 and 60%,
c) discharging the polymer gel from the polymerization vessel,
d) granulating the polymer gel thus obtained in a granulator, in presence of a lubricant composition LC2 comprising: 15-35 weight % alkyl oleate/15-45 weight % polyoxyethylene oleyl ether phosphate/35-55 weight % sorbitan monolaurate,
e) drying the polymer gel to obtain a polymer in powder form, and
f) grinding and sifting the powder.
2. The process for preparing water-soluble polymers in powder form according to claim 1 wherein water-soluble monoethylenically unsaturated monomers are nonionic and/or anionic and/or cationic:
non-ionic monomers are selected from the group consisting of acrylamide; methacrylamide; N-mono derivatives of acrylamide; N-mono derivatives of methacrylamide; N,N derivatives of acrylamide; N,N derivatives of methacrylamide; acrylic esters; and methacrylic esters,
anionic monomers are selected from the group consisting of monomers having a carboxylic function and salts thereof including acrylic acid, methacrylic acid, itaconic acid; maleic acid, monomers having a sulfonic acid function and salts thereof; including acrylamide tertio butyl sulfonic acid (ATBS), monomers having a phosphonic acid function and salts thereof,
cationic monomers are selected from the group consisting of dimethylaminoethyl acrylate (DMAEA) quaternized or salified; dimethylaminoethyl methacrylate (DMAEMA) quaternized or salified; diallyldimethyl ammonium chloride (DADMAC); acrylamidopropyltrimethylammonium chloride (APTAC); methacrylamidopropyltrimethylammonium chloride (MAPTAC).
3. The process for preparing water-soluble polymers in powder form according to claim 1 wherein the alkyl oleate of lubricant compositions LC1 and/or LC2, is selected from the group: methyl oleate, ethyl oleate, propyl oleate; isopropyl oleate, butyl oleate, isobutyl oleate, amyl oleate, and ethylhexyl oleate.
4. The process for preparing water-soluble polymers in powder form according to claim 1 wherein the polyoxyethylene group of the polyxoyethylene oleyl ether phosphate of lubricant compositions LC1 and/or LC2, contains between 2 and 50 oxyethylene moieties.
5. The process for preparing water-soluble polymers in powder form according to claim 1 wherein in step a) of the process 0.01 to 0.8 weight % of the lubricant composition LC1 is sprayed based on the weight of the polymerization charge.
6. The process for preparing water-soluble polymers in powder form according to claim 1 wherein in step d) of the process 0.01 to 1.2 weight % of the lubricant composition LC2 based on the weight of the polymerization charge is sprayed on the polymer in the cutting chamber of the granulator.
7. The process for preparing water-soluble polymers in powder form according to claim 2 wherein the water-soluble monoethylenically unsaturated monomers comprise anionic monomers selected from acrylic acid, acrylamide tertio butyl sulfonic acid (ATBS), and alkaline or alkaline earth or ammonium salts thereof.
8. The process for preparing water-soluble polymers in powder form according to claim 2 wherein the alkyl oleate of lubricant compositions LC1 and/or LC2, is selected form the group: methyl oleate, ethyl oleate, propyl oleate; isopropyl oleate, butyl oleate, isobutyl oleate, amyl oleate, ethylhexyl oleate.
9. The process for preparing water-soluble polymers in powder form according to claim 2 wherein the polyoxyethylene group of the polyxoyethylene oleyl ether phosphate of lubricant compositions LC1 and/or LC2, contains between 2 and 50 oxyethylene moieties.
10. The process for preparing water-soluble polymers in powder form according to claim 3 wherein the polyoxyethylene group of the polyxoyethylene oleyl ether phosphate of lubricant compositions LC1 and/or LC2, contains between 2 and 50 oxyethylene moieties.
11. The process for preparing water-soluble polymers in powder form according to claim 7 wherein the polyoxyethylene group of the polyxoyethylene oleyl ether phosphate of lubricant compositions LC1 and/or LC2, contains between 2 and 50 oxyethylene moieties.
12. The process for preparing water-soluble polymers in powder form according to claim 8 wherein the polyoxyethylene group of the polyxoyethylene oleyl ether phosphate of lubricant compositions LC1 and/or LC2, contains between 2 and 50 oxyethylene moieties.
13. The process for preparing water-soluble polymers in powder form according to claim 2 wherein in step a) of the process 0.01 to 0.8 weight % of the lubricant composition LC1 is sprayed based on the weight of the polymerization charge.
14. The process for preparing water-soluble polymers in powder form according to claim 3 wherein in step a) of the process 0.01 to 0.8 weight % of the lubricant composition LC1 is sprayed based on the weight of the polymerization charge.
15. The process for preparing water-soluble polymers in powder form according to claim 4 wherein in step a) of the process 0.01 to 0.8 weight % of the lubricant composition LC1 is sprayed based on the weight of the polymerization charge.
16. The process for preparing water-soluble polymers in powder form according to claim 7 wherein in step a) of the process 0.01 to 0.8 weight % of the lubricant composition LC1 is sprayed based on the weight of the polymerization charge.
17. The process for preparing water-soluble polymers in powder form according to claim 2 wherein in step d) of the process 0.01 to 1.2 weight % of the lubricant composition LC2 based on the weight of the polymerization charge is sprayed on the polymer in the cutting chamber of the granulator.
18. The process for preparing water-soluble polymers in powder form according to claim 3 wherein in step d) of the process 0.01 to 1.2 weight % of the lubricant composition LC2 based on the weight of the polymerization charge is sprayed on the polymer in the cutting chamber of the granulator.
19. The process for preparing water-soluble polymers in powder form according to claim 4 wherein in step d) of the process 0.01 to 1.2 weight % of the lubricant composition LC2 based on the weight of the polymerization charge is sprayed on the polymer in the cutting chamber of the granulator.
20. The process for preparing water-soluble polymers in powder form according to claim 5 wherein in step d) of the process 0.01 to 1.2 weight % of the lubricant composition LC2 based on the weight of the polymerization charge is sprayed on the polymer in the cutting chamber of the granulator.