Method for manufacturing a cellulose product, cellulose product forming apparatus and cellulose product

1. A method for manufacturing a cellulose product, comprising the steps:

dry forming a cellulose blank consisting essentially of cellulose fibres in a dry forming unit, wherein the cellulose blank is free of plastic,

arranging the cellulose blank in a forming mould,

heating the cellulose blank to a forming temperature of at least 100° C.; and

pressing the cellulose blank in the forming mould with a forming pressure of at least 1 MPa, characterized in that, when dry forming the cellulose blank in the dry forming unit cellulose fibres are carried and formed to the cellulose blank by air as carrying medium

wherein the cellulose blank is formed into a cellulose product having a three-dimensional shape.

2. A method according to claim 1 , wherein the cellulose blank is heated at a range of from 100° C. to 200° C.

3. A method according to claim 1 , wherein the forming pressure is in the range of 1 MPa to 100 MPa.

4. A method according to claim 1 , wherein the heating of the cellulose blank at least partly takes place before pressing the cellulose blank.

5. A method according to claim 1 , wherein the forming mould is heated before pressing the cellulose blank.

6. A method according to claim 1 , wherein the dry forming unit comprises a separating unit, a forming wire and a compacting unit, the method further comprising the steps:

separating cellulose into detached cellulose fibres in the separating unit; arranging the cellulose fibres onto the forming wire; and

compacting the cellulose fibres in the compacting unit to form the cellulose blank.

7. A method according to claim 6 , further comprising the step:

applying a sizing agent to the cellulose fibres to increase the hydrophobic properties and/or mechanical strength of the cellulose blank.

8. A method according to claim 1 , wherein the cellulose blank is formed as a continuous cellulose web in the dry forming unit.

9. A method according to claim 8 , wherein the continuous cellulose web is intermittently fed to the forming mould by a feeding unit.

10. A cellulose product forming apparatus for manufacturing a cellulose product having a three-dimensional shape from a cellulose, the cellulose product forming apparatus comprising:

a heating unit configured for heating a cellulose blank which is free of plastic to a forming temperature of at least 100° C.;

a forming mould configured to form the cellulose product by pressing the cellulose blank in the forming mould with a forming pressure of at least 1 MPa;

characterized in that the cellulose product forming apparatus further comprises a dry forming unit for forming the cellulose blank consisting essentially of cellulose fibres, where the cellulose fibres are carried and formed to the cellulose blank by air as carrying medium wherein the forming mould is adapted to form the cellulose blank into a cellulose product having a three-dimensional shape.

11. A cellulose product forming apparatus according to claim 10 ,

wherein the heating unit is configured for heating the cellulose blank at a range of from 100° C. to 200° C.

12. A cellulose product forming apparatus according to claim 10 , characterized in that the dry forming unit comprises:

a separating unit for separating cellulose into detached cellulose fibres;

a forming wire for the cellulose fibres; and

a compacting unit for compacting the cellulose fibres to form the cellulose blank.

13. A cellulose product forming apparatus according to claim 10 , characterized in that the forming mould comprises the heating unit.

14. A cellulose product forming apparatus according to claim 10 ,

characterized in that the cellulose product forming apparatus comprises an application unit adapted to apply sizing agents or other substances to the cellulose fibres.

15. A cellulose product forming apparatus according to claim 10 ,

characterized in that the dry forming unit is adapted to form the cellulose blank as a continuous cellulose web.

16. A cellulose product forming apparatus according to claim 15 ,

characterized in that the cellulose product forming apparatus comprises a feeding unit adapted to intermittently feed the continuous cellulose web to the forming mould.

17. A cellulose product manufactured by the method according to claim 1 .

18. A cellulose product according to claim 17 ,

characterized in that the cellulose product comprises at least 90 weight percent cellulose fibres.

19. A cellulose product according to claim 17 which is recyclable.