Blown films comprising bimodal ethylene-based polymers having high molecular weight high density fractions
A blown film having a bimodal ethylene-based polymer including a high density fraction (HDF) from 3.0% to 25.0%, an I 10 /I 2 ratio from 5.5 to 7.5, a short chain branching distribution (SCBD) less than or equal to 10 C, a zero shear viscosity ratio from 1.0 to 2.5, a density from 0.902 g/cc to 0.925 g/cc, and a melt index (I 2 ) from 0.5 g/10 mins to 2.0 g/10 mins.
1. A blown film comprising a bimodal ethylene-based polymer comprising:
a high density fraction (HDF) from 3.0% to 25.0%, wherein the high density fraction is measured by crystallization elution fractionation (CEF) integration at temperatures from 93° C. to 119° C.;
an I 10 /I 2 ratio from 5.5 to 7.5, wherein I 2 is a melt index when measured according to ASTM D 1238 at a load of 2.16 kg and temperature of 190° C. and I 10 is a melt index when measured according to ASTM D 1238 at a load of 10 kg and temperature of 190° C.;
a short chain branching distribution (SCBD) less than or equal to 10° C., wherein the short chain branching distribution is measured by CEF full width at half height;
a density from 0.902 g/cc to 0.925 g/cc, wherein the density is measured in accordance with ASTM D792, Method B, and a melt index (I 2 ) from 0.5 g/10 mins to 2.0 g/10 mins, wherein the melt index (I 2 ) is measured in accordance to ASTM D1238 at 190° C. at 2.16 kg.
2. The blown film of claim 1 , wherein the bimodal ethylene-based polymer has a density from 0.910 g/cc to 0.920 g/cc.
3. The blown film of claim 1 , wherein bimodal ethylene-based polymer has a melt index (I 2 ) from 0.7 g/10 mins to 1.8 g/10 mins.
4. The blown film of claim 1 , wherein the bimodal ethylene-based polymer has a zero shear velocity ratio from 1.1 to 3.0.
5. The blown film of claim 1 , wherein the blown film has average clarity from 97.0% to 99.5%, wherein the average clarity is measured using BYK Gardner Haze-gard as specified in ASTM D 1746.
6. The blown film of claim 1 , wherein the blown film has average gloss from 50 to 75, wherein the average gloss is measured in accordance with ASTM D2457 using a BYK Gardner Glossmeter Microgloss at 45°.
7. The blown film of claim 1 , wherein the blown film has average bulk haze from 6.25% to 13.75%, wherein the average bulk haze is measured in accordance with ASTM D1003 using BYK Gardner Haze-gard.
8. The blown film of claim 7 , wherein the blown film has average dart impact strength from 450 g/mil to 700 g/mil, wherein the average dart impact strength is measured according to ASTM-D 1709-04, Method A.
9. The blown film of claim 1 , wherein the blown film has average puncture from 125.0 ft·lb/in 3 to 175.0 ft·lb/in 3 , wherein the average puncture is measured in accordance with ASTM D5748-95.
10. The blown film of claim 1 , wherein the blown film has average tear in a cross-machine direction from 325 g/mil to 550 g/mil wherein the average tear is Elmendorf Tear Resistance measured in accordance with ASTM D1922.
11. The blown film of claim 1 , wherein the blown film has average tear in a machine direction from 250 g/mil to 350 g/mil, wherein the average tear is Elmendorf Tear Resistance measured in accordance with ASTM D1922.
12. The blown film of claim 1 , wherein the blown film has average secant modulus in a cross-machine direction from 10,000 psi to 39,000 psi, wherein the average secant modulus is measured in accordance with ASTM D882.
13. The blown film of claim 1 , wherein the blown film has average secant modulus in a machine direction from 10,000 psi to 33,500 psi, wherein the average secant modulus is measured in accordance with ASTM D882.
14. The blown film of claim 1 , wherein the blown film has average tensile strength in a cross-machine direction from 7500.0 psi to 8000.0 psi, wherein the average tensile strength is measured in accordance with ASTM D882.
15. The blown film of claim 1 , wherein the blown film has average tensile strength in a cross-machine direction from 8000.0 psi to 8700.0 psi, wherein the average tensile strength is measured in accordance with ASTM D882.
16. The blown film of claim 1 , wherein the blown film comprises a mixture of the bimodal ethylene-based polymer and at least one polymer selected from the group consisting of low density polyethylene, ultra-low density polyethylene, linear low density polyethylene, high density polyethylene, a propylene-based polymer, and mixtures thereof.
17. The blown film of claim 1 , wherein the bimodal ethylene-based polymer has a HDF from 3.0% to 7.5%.
18. The blown film of claim 1 , wherein the bimodal ethylene-based polymer has an I 10 /I 2 ratio from 5.5 to 6.0.
19. The blown film of claim 1 , wherein the bimodal ethylene-based polymer has an SCBD less than or equal to 8° C.
20. The blown film of claim 1 , wherein the bimodal ethylene-based polymer has a ratio of Mw to Mn less than 2.800.