Process for removing impurities in the recycling of lithium-ion batteries
A method of treating a leaching solution derived from a black mass from spent lithium-ion batteries comprising setting pH of the leaching solution to about pH 1.2 to 2.5, adding iron powder to induce copper cementation, adding lime after copper cementation, and after adding lime, transiting pH of the leaching solution to about pH 6 to extract calcium fluoride, titanium hydroxide, aluminium hydroxide, iron hydroxide, and iron phosphate. A black mass recycling system comprising an impurity removal reactor configured to receive a sodium hydroxide feed, an iron powder feed, and a lime feed.
1. A method of treating a leaching solution comprising:
setting pH of the leaching solution to about pH 1.2 to 2.15, wherein the leaching solution is derived from a black mass comprising iron, copper, fluorine, phosphorous, titanium, and aluminium;
adding iron powder to induce copper cementation;
after copper cementation, adding lime; and
after adding lime, transiting pH of the leaching solution to about pH 6 to extract calcium fluoride, titanium hydroxide, aluminium hydroxide, iron hydroxide, and iron phosphate.
2. The method according to claim 1 , wherein about 2.5 g of iron powder is added for each litre of the leaching solution.
3. The method according to claim 1 , wherein the iron powder is added over a period of about 15 minutes.
4. The method according to claim 1 , wherein the lime is calcium oxide and about 20-40 g of calcium oxide is added for each kg of black mass.
5. The method according to claim 1 , wherein the lime is calcium hydroxide and about 30-60 g of calcium hydroxide is added for each kg of black mass.
6. The method according to claim 1 , wherein the leaching solution is derived from the black mass by leaching the black mass with sulfuric acid and hydrogen peroxide.
7. The method according to claim 6 , wherein the sulfuric acid is 4M sulfuric acid and about 6 litres of sulfuric acid is added for each kg of the black mass.
8. The method according to claim 6 , wherein the sulfuric acid and hydrogen peroxide are added in consecutive order.
9. The method according to claim 6 , wherein the black mass, sulfuric acid and hydrogen peroxide are agitated for a period of 1 hour.
10. The method according to claim 9 , further comprising diluting the sulfuric acid to about 2M by adding deionised water after the period of 1 hour.
11. A black mass recycling system comprising:
an impurity removal reactor configured to receive a sodium hydroxide feed, an iron powder feed, and a lime feed;
a leaching reactor configured to receive a sulfuric acid feed, a hydrogen peroxide feed, a deionised water feed, and a black mass feed comprising iron, copper, fluorine, phosphorous, titanium, and aluminium; and
a first valved outlet associated with the leaching reactor providing fluid communication between the leaching reactor and the impurity removal reactor.
12. The black mass recycling system of claim 11 , further comprising
an impurity removal agitator provided within the impurity removal reactor; and
a leaching reactor agitator provided within the leaching reactor.