Foaming process for production of foam materials
A production process can produce foam materials from polymer compositions. This process involves preheating in the foaming of polymers containing blowing agents and subsequent foaming by a thermal process assisted by microwaves.
1. A process for producing a foam, comprising:
preheating a polymer composition to be foamed, and
foaming the polymer composition containing a blowing agent in an apparatus having a thermal heating device for heating to an internal temperature of the apparatus Ts and irradiating simultaneously the polymer composition by at least one microwave source of the apparatus:
wherein the polymer composition, prior to the foaming, is preheated to a preheating temperature T v above a glass transition temperature T g of the polymer composition.
2. The process according to claim 1 , wherein the polymer composition is preheated in the apparatus at a temperature between a minimum of 80° C. below and a maximum of 10° C. above the internal temperature of the apparatus T S .
3. The process according to claim 1 , wherein a temperature differential between a coldest point and a hottest point within the polymer composition after the preheating is not greater than 15° C.
4. The process according to claim 1 , wherein the preheated polymer composition is supplied directly to the foaming process in the apparatus.
5. The process according to claim 1 , wherein the polymer composition is a material that forms a rigid foam after the foaming.
6. The process according to claim 1 , wherein a preheating temperature Tv is between 110 and 190° C., and a preheating time is at least 85 min.
7. The process according to claim 1 , wherein microwave radiation from the at least one microwave source has a frequency between 0.85 and 6.0 GHz.
8. The process according to claim 1 , wherein the polymer composition comprises PMI (polymethacrylimide), wherein a preheating temperature T V is between 120 and 190° C., and wherein an internal temperature of the apparatus T S is between 180 and 240° C.
9. The process according to claim 1 , wherein the polymer composition comprises PMMA or methacrylate-based copolymer, werein a preheating temperature T V is between 110 and 140° C., and wherein an internal temperature of the apparatus T S is between 120 and 190° C.
10. The process according to claim 5 , wherein the rigid foam is selected from the group selecting of P(M)I (poly(meth)acrylimide), PMMA, a methactylate-based copolymer, polyvinyl chloride (PVC), polypropylene (PP), polyurethane (PU), a polysulfone, and a poly(ether)imide.
11. The process according to claim 6 , wherein the preheating time is at least 110 min.
12. The process according to claim 1 , wherein a preheating time is at least 70 min.
13. The process according to claim 1 , wherein a preheating time is at least 80 min.