Method of producing organic-inorganic hybrid infrared absorbing particles and organic-inorganic hybrid infrared absorbing particles
A method of producing organic-inorganic hybrid infrared absorbing particles includes a dispersion liquid preparing step of preparing a dispersion liquid containing infrared absorbing particles, a dispersant, and a dispersion medium; a dispersion medium removing step of removing the dispersion medium from the dispersion liquid by an evaporation; a raw material mixture liquid preparing step of preparing a raw material mixture liquid containing the infrared absorbing particles collected after the dispersion medium removing step, a coating resin material, an organic solvent, an emulsifying agent, water, and a polymerization initiator; a stirring step of stirring the raw material mixture liquid while cooling; and a polymerizing step of polymerizing the coating resin material after deoxygenation treatment which reduces an amount of oxygen in the raw material mixture liquid.
1. A method of producing organic-inorganic hybrid infrared absorbing particles comprising:
preparing a dispersion liquid containing infrared absorbing particles, a dispersant, and a dispersion medium;
removing the dispersion medium from the dispersion liquid by an evaporation;
preparing a raw material mixture liquid containing the infrared absorbing particles collected after the dispersion medium removing step, a coating resin material, an organic solvent, an emulsifying agent, water, and a polymerization initiator;
stirring the raw material mixture liquid while cooling; and
polymerizing the coating resin material after deoxygenation treatment which reduces an amount of oxygen in the raw material mixture liquid.
2. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 1 , wherein the dispersant is an amine compound.
3. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 2 , wherein the dispersant includes one or more polymeric materials selected from a long chain alkyl group and a benzene ring.
4. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 3 , wherein the emulsifying agent is a cationic surfactant.
5. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 2 , wherein the emulsifying agent is a cationic surfactant.
6. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 2 , wherein the amine compound is a tertiary amine.
7. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 6 , wherein the dispersant includes one or more polymeric materials selected from a long chain alkyl group and a benzene ring.
8. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 7 , wherein the emulsifying agent is a cationic surfactant.
9. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 6 , wherein the emulsifying agent is a cationic surfactant.
10. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 1 , wherein the dispersant includes one or more polymeric materials selected from a long chain alkyl group and a benzene ring.
11. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 10 , wherein the emulsifying agent is a cationic surfactant.
12. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 1 , wherein the emulsifying agent is a cationic surfactant.
13. The method of producing the organic-inorganic hybrid infrared absorbing particles according to claim 1 ,
wherein the infrared absorbing particles include one or more oxides selected from a tungsten oxide and a composite tungsten oxide,
wherein the tungsten oxide is represented by a general formula WyOz,
wherein W represents tungsten, O represents oxygen, and 2.2≤z/y≤2.999,
wherein the composite tungsten oxide is represented by a general formula MxWyOz, and
wherein an element M is one or more elements selected from H, He, alkali metal, alkaline earth metal, rare earth elements, Mg, Zr, Cr, Mn, Fe, Ru, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd, Al, Ga, In, Tl, Si, Ge, Sn, Sb, B, F, P, S, Se, Br, Te, Ti, Nb, V, Mo, Ta, Re, Be, Hf, Os, Bi, and I, where 0.001≤x/y≤1 and 2.0≤z/y≤3.0.