Method of preparing a micronized sulphur fertilizer product with urea
A process for the production of elemental sulphur-urea fertilizer products is described, comprising the preparation of molten urea; preparing a suspension of micronized sulphur particles with water; mixing the molten urea with suspension of micronized sulphur particles with water wherein the micronized sulphur particles substantially remain in micronized solid state; and spraying the mixture of molten urea and suspension of micronized sulphur particles with water into a granulator, wherein the water in the mixture is flashed off, resulting in the formation of sulphur-urea granules with an even distribution of urea and micronized sulphur particles. An elemental sulphur-urea fertilizer composition obtained by the process is also described.
1. A method of producing a sulphur-urea fertilizer granule, comprising the steps of:
a) preparing and maintaining molten urea at a suitable temperature for injection into a granulator;
b) preparing and maintaining a suspension of micronized sulphur particles with at least 20% water content, with a relatively uniform micronized particle size distribution, for injection into the granulator;
c) prior to injection into the granulator, combining the urea and micronized sulphur suspension, wherein the water content of the suspension cools the mixture of urea and micronized sulphur suspension, and the micronized sulphur particles substantially remain in solid state; and
d) spraying the mixture of urea and micronized sulphur suspension into a granulator using a nozzle where about 20% wt. of the water content in the mixture of urea and micronized sulphur suspension is flashed off, wherein the granulator forms micronized sulphur-urea granules with a relatively uniform distribution of urea and micronized sulphur particles.
2. The method of claim 1 , wherein the urea and micronized sulphur suspension are combined in a tee connection proximal to the entry into the granulator.
3. The method of claim 2 , wherein the water content of the micronized sulphur suspension cools the mixture of urea and micronized sulphur suspension without solidification of urea.
4. The method of claim 3 , wherein the urea is maintained at a temperature of at least 135° C. before its combination with the micronized sulphur suspension.
5. The method of claim 4 , wherein the preparation and maintaining of the urea is in a urea reactor in fluid communication with the tee connection.
6. The method of claim 5 , wherein the micronized sulphur particles have an average diameter of less than about 30 microns.
7. The method of claim 6 , wherein the micronized sulphur particles have an average diameter of less than about 7 microns.
8. The method of claim 7 , wherein the micronized sulphur particles have an average diameter of less than about 5 microns.
9. The method of claim 8 , wherein the sulphur-urea fertilizer granules are produced without a further drying step in a dedicated drying equipment.
10. A sulphur-urea fertilizer composition obtained by:
a) preparing and maintaining molten urea at a suitable temperature for injection into a granulator;
b) preparing and maintaining a suspension of micronized sulphur particles with at least 20% water wt. content, with a relatively uniform micronized particle size distribution, for injection into the granulator the suspension further comprising a surfactant;
c) prior to injection into the granulator, combining the urea and micronized sulphur suspension, wherein the water wt. content of the suspension cools the mixture of urea and micronized sulphur suspension, and the micronized sulphur particles substantially remain in solid state;
d) spraying the mixture of urea and micronized sulphur suspension into a granulator using a nozzle where about 20% wt. of the water content in the mixture of urea and micronized sulphur suspension is flashed off, wherein the granulator forms micronized sulphur-urea granules with a relatively uniform distribution of urea and micronized sulphur particles; and
e) forming the granules of sulphur-urea fertilizer composition without a further drying step in a dedicated drying equipment, wherein the granulator forms sulphur-urea granules with a relatively uniform distribution of urea and micronized sulphur particles.